RESUMO
This study assessed the mechanical properties and surface characteristics of dental prosthetic acrylic resin fabricated by 3D printing, comparing it with subtractive, pressing, and molding techniques. Bar-shaped specimens (N= 90; 65 × 10 × 3.3 mm; ISO:207951) were prepared and assigned into six groups: PRINT (3D printing vis stereolithography with PriZma 3D Bio Denture, Makertech Labs); SUB (subtractive manufacturing with Vipiblock Trilux, Vipi); PRESS Base (pressing using muffle with Thermo Vipi Wave, Vipi for base); PRESS Tooth (pressing with Onda-cryl, Clássico for tooth); MOLD Base (molding using addition silicone with Vipi Flash, Vipi for base); and MOLD Tooth (molding with Dencor, Clássico for tooth). Monotonic flexural strength (FS) and elastic modulus (E) were measured using a three-point bending approach (n= 5) on a universal testing machine at a crosshead speed of 5 mm/min. Fatigue testing (n= 10) followed similar geometry and settings, with a frequency of 2 Hz, initial stress level at 20 MPa, and stress increments of 5 MPa every 2,500 cycles. Surface roughness (n= 10) was assessed through profilometry, and fractographic and topographic analyses were conducted. Statistical analyses included One-Way ANOVA for monotonic FS, roughness, and E, along with Kaplan-Meier with Mantel-Cox post-hoc and Weibull analysis for fatigue strength. PRINT showed lower monotonic FS than the SUB and PRESS Tooth but comparable fatigue strength to these groups and superior to PRESS Base and MOLD (Base and Tooth) groups. All groups had similar Weibull moduli. Surface roughness of the PRINT group was comparable to most techniques but higher than the PRESS Tooth group. Fractographic analysis revealed fractures originating from surface defects under tensile stress, with SEM showing scratch patterns in all groups except PRINT, which had a more uniform surface. Despite its lower monotonic strength, 3D printed resin demonstrated comparable fatigue strength to subtractive and pressing methods and similar surface roughness to most methods, indicating its potential as a viable option for dental prosthesis.
Assuntos
Resinas Acrílicas , Teste de Materiais , Impressão Tridimensional , Propriedades de Superfície , Resinas Acrílicas/química , Estresse Mecânico , Testes Mecânicos , Módulo de Elasticidade , Fenômenos MecânicosRESUMO
Toxoplasma gondii is a protozoan that has great genetic diversity and is prevalent worldwide. In 2018, an outbreak of toxoplasmosis occurred in Santa Maria, Brazil, which was considered the largest outbreak ever described in the world. This paper describes the isolation and molecular characterization of Toxoplasma gondii from the placenta of two pregnant women with acute toxoplasmosis who had live births and were receiving treatment for toxoplasmosis during the outbreak. For this, placental tissue samples from two patients underwent isolation by mice bioassay, conventional PCR and genotyping using PCR-RFLP with twelve markers. Both samples were positive in isolation in mice. The isolate was lethal to mice, suggesting high virulence. In addition, the samples were positive in conventional PCR and isolates submitted to PCR-RFLP genotyping presented an atypical genotype, which had never been described before. This research contributes to the elucidation of this great outbreak in Brazil.