Effect of benzotriazole on the existing pits of copper tube in fire sprinkler system.

In this paper, two leaking tubes were investigated among copper tubes injected with 200 and 400 ppm benzotriazole after 8 years of usage. The electrochemical tests were conducted in simulated pit-out and pit-in environments (i.e., regions outside and inside of the pit) to determine the effect of benzotriazole on the propagation of an existing pit. The electrochemical analysis results showed that 200 and 400 ppm benzotriazole exhibit relatively lower inhibition efficiency in an acidic simulated pit-in environment because of the difficulty of forming a protective film and the benzotriazole cationization.

Comparison of Hydrogen Embrittlement Susceptibility of Different Types of Advanced High-Strength Steels.

This study investigated the hydrogen embrittlement (HE) characteristics of advanced high-strength steels (AHSSs). Two different types of AHSSs with a tensile strength of 1.2 GPa were investigated. Slow strain rate tests (SSRTs) were performed under various applied potentials (Eapp) to identify the mechanism with the greatest effect on the embrittlement of the specimens. The SSRT results revealed that, as the Eapp increased, the elongation tended to increase, even when a potential exceeding the corrosion potential was applied. Both types of AHSSs exhibited embrittled fracture behavior that was dominated by HE. The fractured SSRT specimens were subjected to a thermal desorption spectroscopy analysis, revealing that diffusible hydrogen was trapped mainly at the grain boundaries and dislocations (i.e., reversible hydrogen-trapping sites). The micro-analysis results revealed that the poor HE resistance of the specimens was attributed to the more reversible hydrogen-trapping sites.

Localized Corrosion Occurrence in Low-Carbon Steel Pipe Caused by Microstructural Inhomogeneity.

In this study, the cause of failure of a low-carbon steel pipe meeting standard KS D 3562 (ASTM A135), in a district heating system was investigated. After 6 years of operation, the pipe failed prematurely due to pitting corrosion, which occurred both inside and outside of the pipe. Pitting corrosion occurred more prominently outside the pipe than inside, where water quality is controlled. The analysis indicated that the pipe failure occurred due to aluminum inclusions and the presence of a pearlite inhomogeneous phase fraction. Crevice corrosion occurred in the vicinity around the aluminum inclusions, causing localized corrosion. In the large pearlite fraction region, cementite in the pearlite acted as a cathode to promote dissolution of surrounding ferrite. Therefore, in the groundwater environment outside of the pipe, localized corrosion occurred due to crevice corrosion by aluminum inclusions, and localized corrosion was accelerated by the large fraction of pearlite around the aluminum inclusions, leading to pipe failure.

Effect of Imidazole as Corrosion Inhibitor on Carbon Steel Weldment in District Heating Water.

Many research studies have been conducted on the corrosion inhibition performance of imidazole in acidic environments such as in the piping of a petrochemical plant. However, there has been no study on the effect of imidazole in alkaline conditions such as a local district water heating environment. Therefore, in this study, the effect of imidazole as a corrosion inhibitor on carbon steel weldment was investigated in alkaline district heating water. Inhibition efficiency and electrochemical properties were investigated by potentiodynamic polarization test and electrochemical impedance spectroscopy. As the concentration of imidazole increased up to 500 ppm, inhibition efficiency increased up to 91.7%. At 1000 ppm, inhibition efficiency decreased. Atomic force microscopy showed that surface coverage of imidazole at 1000 ppm is lower than that of imidazole at 500 ppm. X-ray photoelectron spectroscopy showed that with 500 ppm of imidazole, the amount of pyrrole type interaction is 4.8 times larger than pyridine type interaction. At 1000 ppm of imidazole, the amount of pyridine type interaction is 3.49 times larger than pyrrole type interaction. Depending on the concentration of imidazole, the ratio of interaction between carbon steel and imidazole affected inhibition efficiency.

Effect of Benzotriazole on the Localized Corrosion of Copper Covered with Carbonaceous Residue.

Carbonaceous residues on copper pipes during the manufacturing process are known to be one of the main causes of pitting corrosion on copper pipes. This study examined the corrosion-inhibiting effect of benzotriazole (BTA) on C12200 copper pipes with carbonaceous film in synthetic tap water. In the absence of BTA, localized corrosion mechanisms due to galvanic corrosion, crevice corrosion, and oxygen-concentration cell were proposed in the boundary part of the carbonaceous film on the copper through X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) with energy dispersive spectrometer (EDS) analyses. Electrochemical tests showed that BTA inhibits corrosion by forming Cu-BTA complexes on all over the copper surface where carbonaceous film is present. BTA mitigates galvanic corrosion and crevice corrosion at the boundary of the carbonaceous film and suppresses the formation of oxygen-concentration cells through the formation of a Cu-BTA complex.

Effect of Cr on Aqueous and Atmospheric Corrosion of Automotive Carbon Steel.

This study investigated the effect of Cr alloying element on the corrosion properties of automotive carbon steel (0.1C, 0.5Si, 2.5Mn, Fe Bal., composition given in wt.%) in aqueous and atmospheric conditions using electrochemical measurement and cyclic corrosion tests. Three steels with 0, 0.3, and 0.5 wt.% Cr were studied by electrochemical impedance spectroscopy. Polarization resistance (Rp) of 0.3 Cr and 0.5 Cr steels was higher than that of 0 Cr steel, and the Rp also increased as the Cr content increased. Therefore, Cr increases the corrosion resistance of automotive carbon steel immersed in a chloride ion (Cl-)-containing aqueous solution. In the cyclic corrosion test results, Cl- was concentrated at the metal/rust interface in all of the steels regardless of Cr content. The Cl- was uniformly concentrated and distributed on the 0 Cr steel, but locally and non-uniformly concentrated on the Cr-added steels. The inner rust layer consisted of ß-FeOOH containing Cl- and Cr-goethite, while the outer rust layer was composed of amorphous iron oxyhydroxide mixed with various types of rust. FeCl2 and CrCl3 are formed from the Cl- nest developed in the early stage, and the pitting at CrCl3-formed regions are locally accelerated because Cr is strongly hydrolyzed to a very low pH.

Optimization of Pickling Solution for Improving the Phosphatability of Advanced High-Strength Steels.

This study investigated the optimum pickling conditions for improving the phosphatability of advanced high-strength steel (AHSS) using surface analysis and electrochemical measurements. To remove the SiO2 that forms on the surface of AHSS, 30 wt.% NH4HF2 was added to the pickling solution, resulting in a significant reduction in the amount of SiO2 remaining on the surface of the AHSS. The phosphatability was improved remarkably using HNO3 concentrations higher than 13% in the pickling solution. Furthermore, phosphate crystals became finer after pickling with a HNO3-based solution rather than a HCl-based solution. Electrochemical impedance spectroscopy (EIS) data indicated that the corrosion resistance of AHSS subjected to HNO3-based pickling was higher than that of AHSS subjected to HCl-based pickling. Fluorine compounds, which were involved in the phosphate treatment process, were only formed on the surface of steel in HNO3-based solutions. The F compounds reacted with the phosphate solution to increase the pH of the bulk solution, which greatly improved the phosphatability. The phosphatability was better under HNO3-based conditions than a HCl-based condition due to the fineness of the phosphate structure and the increased surface roughness.

Effects of Corrosion on Mechanical Properties of Welded Carbon Steel Pipe in District Heating Water.

This study examined the effect of corrosion on mechanical properties of welded carbon steel pipe in district heating water. To evaluate the corrosion properties, potentiodynamic tests were conducted and a galvanostatic test was used to accelerate corrosion. Tensile tests and microstructure observations were performed to figure out the degradation of the corroded region, and stress intensity factors were calculated. As a result of the potentiodynamic tests, welded carbon steel pipe showed uniform corrosion and the total charge was calculated. Using the galvanostatic test, the current density at the equivalent aging time was applied to the specimens. The tensile tests showed that according to corrosion damages, mechanical properties were degraded due to corrosion. Through the microstructure observations and calculations of stress intensity factors, the corrosion of the welded carbon steel pipe induced the degradation of mechanical properties. The mode of fracture was changed from ductile to brittle fracture with increasing aging time.

Expression of vesicular glutamate transporters in transient receptor potential ankyrin 1 (TRPA1)-positive neurons in the rat trigeminal ganglion.

Transient receptor potential ankyrin 1 (TRPA1), a cold receptor in sensory neurons activated by a variety of stimuli, is implicated in nociception and mechanotransduction. To help understand the vesicular glutamate transporter (VGLUT)-mediated glutamate signaling in TRPA1-immunopositive (+) neurons, we examined the expression of VGLUT1 and VGLUT2 in the TRPA1+ neurons in the male rat trigeminal ganglion (n = 19) under normal conditions and following experimental inflammation in the vibrissal pad by light microscopic immunohistochemistry (n = 11), western blot (n = 8), and quantitative analysis. One half (50.8%, 250/492) of the TRPA1+ neurons expressed VGLUT2, and a small fraction (8.3%, 57/683) also expressed VGLUT1. The majority of the VGLUT2-expressing TRPA1+ (VGLUT2+/TRPA1+) neurons coexpressed the markers of peptidergic and non-peptidergic neurons, CGRP, IB4, and TRPV1 but not the markers of neurons with myelinated fibers, NF200 and parvalbumin. In contrast, most VGLUT1+/TRPA1+ neurons coexpressed NF200 and parvalbumin but rarely expressed CGRP, IB4, or TRPV1. Following experimental inflammation, the fraction of VGLUT2+ (experimental vs. control: 34.7% vs. 22.3%), TRPA1+ (39.3% vs. 25.3%), and VGLUT2+/TRPA1+ (60.7% vs. 49.7%) neurons and the protein levels for TRPA1 and VGLUT2 increased significantly, compared to control, whereas the fraction of VGLUT1+ and VGLUT1+/TRPA1+ neurons and the protein level for VGLUT1 remained unchanged. These findings suggest that both VGLUT1 and VGLUT2 are involved in the glutamate signaling in TRPA1+ neurons under normal conditions in the male rats, and raise a possibility that VGLUT2 may play a role in the TRPA1-induced hypersensitivity following inflammation.

Extrasynaptic homomeric glycine receptors in neurons of the rat trigeminal mesencephalic nucleus.

The neurons in the trigeminal mesencephalic nucleus (Vmes) innervate jaw-closing muscle spindles and periodontal ligaments, and play a crucial role in the regulation of jaw movements. Recently, it was shown that many boutons that form synapses on them are immunopositive for glycine (Gly+), suggesting that these neurons receive glycinergic input. Information about the glycine receptors that mediate this input is needed to help understand the role of glycine in controlling Vmes neuron excitability. For this, we investigated the expression of glycine receptor subunit alpha 3 (GlyRα3) and gephyrin in neurons in Vmes and the trigeminal motor nucleus (Vmo), and the Gly+ boutons that contact them by light- and electron-microscopic immunocytochemistry and quantitative ultrastructural analysis. The somata of the Vmes neurons were immunostained for GlyRα3, but not gephyrin, indicating expression of homomeric GlyR. The immunostaining for GlyRα3 was localized away from the synapses in the Vmes neuron somata, in contrast to the Vmo neurons, where the staining for GlyRα3 and gephyrin were localized at the subsynaptic zones in somata and dendrites. Additionally, the ultrastructural determinants of synaptic strength, bouton volume, mitochondrial volume, and active zone area, were significantly smaller in Gly+ boutons on the Vmes neurons than in those on the Vmo neurons. These findings support the notion that the Vmes neurons receive glycinergic input via putative extrasynaptic homomeric glycine receptors, likely mediating a slow, tonic modulation of the Vmes neuron excitability.

Vesicular glutamate transporter 1 (VGLUT1)- and VGLUT2-immunopositive axon terminals on the rat jaw-closing and jaw-opening motoneurons.

To provide information on the glutamatergic synapses on the trigeminal motoneurons, which may be important for understanding the mechanism of control of jaw movements, we investigated the distribution of vesicular glutamate transporter (VGLUT)1-immunopositive (+) and VGLUT2 + axon terminals (boutons) on the rat jaw-closing (JC) and jaw-opening (JO) motoneurons, and their morphological determinants of synaptic strength by retrograde tracing, electron microscopic immunohistochemistry, and quantitative ultrastructural analysis. We found that (1) the large majority of VGLUT + boutons on JC and JO motoneurons were VGLUT2+, (2) the density of VGLUT1 + boutons terminating on JC motoneurons was significantly higher than that on JO motoneurons, (3) the density of VGLUT1 + boutons terminating on non-primary dendrites of JC motoneurons was significantly higher than that on somata or primary dendrites, whereas the density of VGLUT2 + boutons was not significantly different between JC and JO motoneurons and among various compartments of the postsynaptic neurons, and (4) the bouton volume, mitochondrial volume, and active zone area of the VGLUT1 + boutons forming synapses on JC motoneurons were significantly bigger than those of VGLUT2 + boutons. These findings suggest that JC and JO motoneurons receive glutamatergic input primarily from VGLUT2-expressing intrinsic neurons (premotoneurons), and may be controlled differently by neurons in the trigeminal mesencephalic nucleus and by glutamatergic premotoneurons.