Join counting, a standard technique in spatial autocorrelation analysis, has been used to quantify the clustering of carbon, fluorine and sodium in cross-sectioned anode and cathode samples. The sample preparation and EDS mapping steps are sufficiently fast for every coating from two Design of Experiment (DoE) test matrices to be characterised. The results show two types of heterogeneity in material distribution; gradients across the coating from the current collector to the surface, and clustering. In the cathode samples, the carbon is more clustered than the fluorine, implying that the conductive carbon component is less well distributed than the binder. The results are correlated with input parameters systematically varied in the DoE e.g. coating blade gap, coating speed, and other output parameters e.g. coat weight, and electrochemical resistance.
RESUMO
Silicon-Few Layer Graphene (Si-FLG) composite electrodes are investigated using a scalable electrode manufacturing method. A comprehensive study on the electrochemical performance and the impedance response is measured using electrochemical impedance spectroscopy. The study demonstrates that the incorporation of few-layer graphene (FLG) results in significant improvement in terms of cyclability, electrode resistance and diffusion properties. Additionally, the diffusion impedance responses that occur during the phase changes in silicon is elucidated through Staircase Potentio Electrochemical Impedance Spectroscopy (SPEIS): a more comprehensive and straightforward approach than previous state-of-charge based diffusion studies.
RESUMO
Hybrid anode materials consisting of micro-sized silicon (Si) particles interconnected with few-layer graphene (FLG) nanoplatelets and sodium-neutralized poly(acrylic acid) as a binder were evaluated for Li-ion batteries. The hybrid film has demonstrated a reversible discharge capacity of â¼1800 mA h g-1 with a capacity retention of 97% after 200 cycles. The superior electrochemical properties of the hybrid anodes are attributed to a durable, hierarchical conductive network formed between Si particles and the multi-scale carbon additives, with enhanced cohesion by the functional polymer binder. Furthermore, improved solid electrolyte interphase (SEI) stability is achieved from the electrolyte additives, due to the formation of a kinetically stable film on the surface of the Si.