Photocatalytic activity of TiO2 nanoparticles: effect of thermal annealing under various gaseous atmospheres.

The structure, composition and photocatalytic activity of TiO(2) nanoparticles annealed in various gas atmospheres (N(2), NH(3) and H(2)) were studied in this work. The effect of treatment on crystal structure, particle size, chemical composition and optical absorbance were assessed by means of x-ray diffraction, transmission electron microscopy, x-ray photoelectron spectroscopy and diffuse optical reflectance/transmittance measurements, respectively. Photocatalytic properties of the materials were evaluated by three different methods: degradation of methyl orange in water, killing of Staphylococcus aureus bacteria and photogeneration of radicals in the presence of 3-carboxy-2,2,5,5-tetramethyl pyrrolidine-1-oxyl (PCA) marker molecules. The results indicate that the correlation between pretreatment and the photocatalytic performance depends on the photocatalytic processes and cannot be generalized.

Synthesis and photocatalytic performance of titanium dioxide nanofibers and the fabrication of flexible composite films from nanofibers.

Titanium dioxide nanofibers were synthesized and applied in flexible composite films that are easy to handle and recycle after use. The nanofibers were obtained in a multi-step procedure. First, sodium titanate nanofibers were prepared from TiO2 nanoparticles through the alkali hydrothermal method. In the next step, sodium hydrogen titanate nanofibers were made by washing the sodium titanate nanofibers in HCl solution. Finally, the sodium hydrogen titanate nanofibers were transformed to TiO2 anatase nanofibers by calcination in air. The photocatalytic activity of TiO2 anatase nanofibers were evaluated and compared to a TiO2 nanoparticle catalyst by decomposing methyl orange dye in aqueous solutions. The achieved reaction rate constant of TiO2 anatase nanofibers was comparable to that of Degussa P25. Paper-like flexible composite films were prepared by co-filtrating aqueous dispersions of TiO2 catalyst materials and cellulose. The composite films made from the nanofibers exhibit better mechanical integrity than those of the nanoparticle-cellulose composites.

Three-dimensional carbon nanotube scaffolds as particulate filters and catalyst support membranes.

Three-dimensional carbon nanotube scaffolds created using micromachined Si/SiO2 templates are used as nanoparticulate filters and support membranes for gas-phase heterogeneous catalysis. The filtering efficiency of better than 99% is shown for the scaffolds in filtering submicrometer particles from air. In the hydrogenation of propene to propane reaction low activation energy of E(a) approximately 27.8 +/- 0.6 kJ x mol(-1), a considerably high turnover rate of approximately 1.1 molecules x Pd site(-1) x s(-1) and durable activity for the reaction are observed with Pd decorated membranes. It is demonstrated that appropriate engineering of macroscopic-ordered nanotube architectures can lead to multifunctional applications.

Electrical transport through single-wall carbon nanotube-anodic aluminum oxide-aluminum heterostructures.

Aluminum foils were anodized in sulfuric acid solution to form thick porous anodic aluminum oxide (AAO) films of thickness approximately 6 microm. Electrodes of carboxyl-functionalized single-wall carbon nanotube (SWCNT) thin films were inkjet printed on the anodic oxide layer and the electrical characteristics of the as-obtained SWCNT-AAO-Al structures were studied. Nonlinear current-voltage transport and strong temperature dependence of conduction through the structure was measured. The microstructure and chemical composition of the anodic oxide layer was analyzed using transmission and scanning electron microscopy as well as x-ray photoelectron spectroscopy. Schottky emission at the SWCNT-AAO and AAO-Al interfaces allowed by impurity states in the anodic aluminum oxide film together with ionic surface conduction on the pore walls of AAO gives a reasonable explanation for the measured electrical conduction. Calcined AAO is proposed as a dielectric material for SWCNT-field effect transistors.