Integration of Porous Nanomaterial-Infused Membrane in UF/FO Membrane Hybrid for Simulated Osmosis Membrane Bioreactor (OsMBR) Process.

This study explored the use of a combination of hydrothermal and sol-gel methods to produce porous titanium dioxide (PTi) powder with a high specific surface area of 112.84 m2/g. The PTi powder was utilized as a filler in the fabrication of ultrafiltration nanocomposite membranes using polysulfone (PSf) as the polymer. The synthesized nanoparticles and membranes were analyzed using various techniques, including BET, TEM, XRD, AFM, FESEM, FTIR, and contact angle measurements. The membrane's performance and antifouling properties were also assessed using bovine serum albumin (BSA) as a simulated wastewater feed solution. Furthermore, the ultrafiltration membranes were tested in the forward osmosis (FO) system using a 0.6-weight-percent solution of poly (sodium 4-styrene sulfonate) as the osmosis solution to evaluate the osmosis membrane bioreactor (OsMBR) process. The results revealed that the incorporation of PTi nanoparticles into the polymer matrix enhanced the hydrophilicity and surface energy of the membrane, resulting in better performance. The optimized membrane containing 1% PTi displayed a water flux of 31.5 L/m2h, compared to the neat membrane water value of 13.7 L/m2h. The membrane also demonstrated excellent antifouling properties, with a flux recovery of 96%. These results highlight the potential of the PTi-infused membrane as a simulated osmosis membrane bioreactor (OsMBR) for wastewater treatment applications.

Fabrication and characterization of dual-layer hollow fibre membranes incorporating poly(citric acid)-grafted GO with enhanced antifouling properties for water treatment.

Membrane fouling during the filtration process is a perennial issue and could lead to reduced separation efficiency. In this work, poly(citric acid)-grafted graphene oxide (PGO) was incorporated into a matrix of single-layer hollow fibre (SLHF) and dual-layer hollow fibrr (DLHF) membranes, respectively, aiming to improve membrane antifouling properties during water treatment. Different loadings of PGO ranging from 0 to 1 wt% were first introduced into the SLHF to identify the best PGO loading for the DLHF preparation with its outer layer modified by nanomaterials. The findings showed that at the optimized PGO loading of 0.7 wt%, the resultant SLHF membrane could achieve higher water permeability and bovine serum albumin rejection compared to the neat SLHF membrane. This is due to the improved surface hydrophilicity and increased structural porosity upon incorporation of optimized PGO loading. When 0.7 wt% PGO was introduced only to the outer layer of DLHF, the cross-sectional matrix of the membrane was altered, forming microvoids and spongy-like structures (more porous). Nevertheless, the BSA rejection of the membrane was improved to 97.7% owing to an inner selectivity layer produced from a different dope solution (without the PGO). The DLHF membrane also demonstrated significantly higher antifouling properties than the neat SLHF membrane. Its flux recovery rate is 85%, i.e. 37% better than that of a neat membrane. By incorporating hydrophilic PGO into the membrane, the interaction of the hydrophobic foulants with the membrane surface is greatly reduced.