Do preheated composite resin or adhesive resin layer strengthen the feldspar ceramic?

STATEMENT OF PROBLEM: Preheated composite resin and adhesive coating have been recommended as luting agents for ceramic veneers; however, information about the mechanical behavior of feldspathic porcelain veneers after using these methods is still limited. PURPOSE: The purpose of this in vitro study was to evaluate the influence of the use of preheated composite resin or an adhesive resin layer on the strengthening of a feldspathic porcelain. MATERIAL AND METHODS: Feldspathic porcelain disks were fabricated (N=210), etched (10% hydrofluoric acid for 90 seconds), and bonded according to resin-based luting agents (30 per group) for the biaxial flexural strength tests: photopolymerized resin cement, flowable composite resin, preheated composite resin, with or without previous adhesive coating. Characteristic strength and Weibull modulus were calculated. The viscosity of the luting agents was measured by using isothermal analyses. Finite element analysis simulated the flexural test. Fractographic and bonded interfaces were observed. RESULTS: The use of preheated composite resin led to the lowest stress levels in the feldspathic porcelain veneers. However, it did not increase the ceramic strengthening compared with other luting agents, as higher values were observed with flowable composite resin (P<.05). The use of an adhesive resin layer had no significant effect on ceramic strengthening when associated with preheated composite resin or resin cement (P>.05). Preheated composite resin presented the highest viscosity and led to incomplete filling of the porcelain surface irregularities. Failures originated on the ceramic surface subjected to tensile stress and were typically associated with pores at the ceramic-luting agent interface. CONCLUSIONS: The use of preheated composite resin or an adhesive resin layer did not have a positive effect on strengthening feldspathic porcelain.

Patients' perception about the outcomes of prosthetic treatment in Southern Brazil - a cross sectional study

Aim: this study assessed the patients' perception of the outcomes of prosthetic treatment in a University of Southern Brazil. Methods: patients seeking for prosthetic treatment were invited to answer a questionnaire with 41 items about the potential risks, benefits, and consequences of no treatment. Answers were obtained according to a five-item Likert-scale varying from 1 (completely disagree) to 5 (completely agree). Sociodemographic data was included in the comparison. Mann-Whitney or Kruskal-Wallis (95%) compared data depending on the variable. Results: two-hundred twenty-five patients answered the questionnaire. Median age of participants was 45-54 years. The potential benefits were similar among participants irrespective of the variable adopted. The perception of risks was significant influenced by variables gender, age, education level, type of edentulous space, prior treatment with prosthodontics, type of prosthodontics, and prosthodontics usage in years. Consequences of no treatment were affected by age, prior treatment with prosthodontics, and prosthodontics usage in years. Conclusions: the study showed the fundamental importance of correct elucidation about the potential risks (negative perception) in the initial appointment for the studied population. Elucidation about the consequences of no treatment are relevant because some differences were seen into the variables. Prosthodontics patients from the city of Passo Fundo seem well informed about the benefits of the prosthetic treatment, besides the significant influence of some sociodemographic and prosthetic conditions

The Influence of Post System Design and Material on the Biomechanical Behavior of Teeth with Little Remaining Coronal Structure.

PURPOSE: To evaluate the influence of different post systems on the biomechanical behavior of teeth with a severe loss of remaining coronal structure. MATERIALS AND METHODS: Fifty standardized bovine teeth (n = 10 per group) were restored with: cast post-and-core (CPC), prefabricated metallic post (PFM), parallel glass-fiber post (P-FP), conical glass-fiber post (C-FP), or composite core (no post, CC). The survival rate during thermomechanical challenging (TC), the fracture strength (FS), and failure patterns (FP) were evaluated. Finite element models evaluated the stress distribution after the application of 100 N. RESULTS: All specimens survived TC. Similar FS was observed among post-containing groups. Groups P-FP and CC presented 100% repairable fractures. The von Mises analysis showed the maximum stresses into the root canal in groups restored with metallic posts. Glass-fiber posts and CC presented the maximum stresses at the load contact point. Glass-fiber groups showed lower stresses in the analysis of maximal contact pressure; CPC led to the highest values of contact pressure. The modified von Mises (mvM) stress in dentin did not show differences among groups. Moreover, mvM values did not reach the dentin fracture limit for any group. CONCLUSIONS: The type of intracanal post had a relevant influence on the biomechanical behavior of teeth with little remaining coronal structure.

Lithium disilicate glass-ceramic vs translucent zirconia polycrystals bonded to distinct substrates: Fatigue failure load, number of cycles for failure, survival rates, and stress distribution.

The present study evaluated the fatigue behavior of monolithic translucent zirconia polycrystals (TZ) and lithium disilicate glass-ceramic (LD) bonded to different substrates. Disc-shaped specimens of ceramic materials TZ and LD were bonded to three substrates with different elastic modulus (E) (fiber-reinforced composite (FRC) - softest material, E = 14.9 GPa; titanium alloy (Ti) - intermediary properties, E = 115 GPa; and zirconia (Yz) - stiffest material, E = 210 GPa). The surfaces were treated and bonded with resin cement (disc-disc set-up). Fatigue testing followed a step-stress approach (initial maximum load = 200 N for 5000 cycles, incremental step load = 200 N for 10,000 cycles/step). The fatigue failure load and number of cycles until failure were recorded and statistically analyzed. Fractographic and finite element (FEA) analyzes were conducted as well. TZ ceramic depicted higher fatigue failure load, number of cycles until failure, and survival probabilities than LD, irrespective of the substrate. Moreover, TZ and LD presented better fatigue behaviors when bonded to substrates Ti and Yz in comparison to FRC. FEA revealed lower tensile stresses at restorative material when bonded to stiffer substrates. Fractography showed that the fracture origin started at bottom surface of restorative material (except for TZ bonded to Yz, in which crack initiated at load contact point). Translucent zirconia polycrystals present superior mechanical behavior than lithium disilicate glass-ceramic. The substrate type influences the mechanical performance of monolithic dental ceramics (stiffer substrates lead to better fatigue behavior).

Biomechanical behavior of teeth without remaining coronal structure restored with different post designs and materials.

The aim of this study was to access the biomechanical behavior of teeth without remaining coronal structure when restored with posts of different materials and configurations. Fifty bovine teeth (n=10 per group) with standard dimensions were restored as follows: cast post and core (CPC), prefabricated metallic post (PFM), parallel glass-fiber post (P-FP), conical glass-fiber post (C-FP) or composite core (no post, CC). The survival rate during thermomechanical challenging (TC), the fracture strength (FS), and failure pattern (FP) were evaluated. Finite element models were realized to evaluate the stress distribution with a 100N load. All post-containing teeth survived TC, while CC had 30% of failures. CPC and C-FP had the higher fracture strength, but a high number of irreparable fractures (60%), such as PFM (70%). Von Mises analysis has shown the maximum stresses into the canal in groups restored with metallic posts, while glass-fiber posts and CC presented the maximum stresses at load contact point in the crown. CPC led to higher modified von Mises (mvM) stress in the cervical third of dentin. However, mvM values did not reach the dentin fracture limit for any group. Analysis of maximal contact pressure has shown better stress distribution along with the dentin interface in post-containing groups, especially for CPC.