RESUMO
OBJECTIVE: Iridium oxide films are commonly used as a high charge-injection electrode material in neural devices. Yet, few studies have performed in-depth assessments of material performance versus film thickness, especially for films grown on three-dimensional (instead of planar) metal surfaces in neutral pH electrolyte solutions. Further, few studies have investigated the driving voltage requirements for constant-current stimulation using activated iridium oxide (AIROF) electrodes, which will be a key constraint for future use in wirelessly powered neural devices. APPROACH: In this study, iridium microwire probes were activated by repeated potential pulsing in room temperature phosphate buffered saline (pH 7.1-7.3). Electrochemical measurements were recorded in three different electrolyte conditions for probes with different geometric surface areas (GSAs) as the AIROF thickness was increased. MAIN RESULTS: Maintaining an anodic potential bias during the inter-pulse interval was required for AIROF electrodes to deliver charge levels considered necessary for neural stimulation. Potential pulsing for 100-200 cycles was sufficient to achieve charge injection levels of 2.5 mC cm-2 (50 nC/phase in a biphasic pulse) in PBS with 2000 µm2 iridium probes. Increasing the electrode surface area to 3000 µm2 and 4000 µm2 significantly increased charge-injection capacity, reduced the driving voltage required to deliver a fixed amount of charge, and reduced polarization of the electrodes during constant-current pulsing. SIGNIFICANCE: This study establishes methods for choosing an activation protocol and a desired GSA for three-dimensional iridium electrodes suitable for neural tissue insertion and stimulation, and provides guidelines for evaluating electrochemical performance of AIROF using model saline solutions.