Magnetically Recoverable TiO2/SiO2/γ-Fe2O3/rGO Composite with Significantly Enhanced UV-Visible Light Photocatalytic Activity.

In this paper, we report the preparation of a new composite (TiO2/SiO2/γ-Fe2O3/rGO) with a high photocatalytic efficiency. The properties of the composite were examined by different analyses, including X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), photoluminescence (PL), UV-Visible light diffuse reflectance spectroscopy, Fourier transform infrared spectroscopy (FTIR), Raman, vibrating-sample magnetometer (VSM), and nitrogen gas physisorption (BET) studies. The photocatalytic efficiency of the proposed composite was evaluated by the degradation of methylene blue under UV and visible light, and the results were compared with titanium dioxide (TiO2), where degradation increased from 30% to 84% and 4% to 66% under UV and visible light, respectively. The significant increase in photocatalytic activity may be explained by the higher adsorption of dye on the surface of the composite and the higher separation and transfer of charge carriers, which in turn promote active sites and photocatalytic efficiency.

Heterostructured TiO2/SiO2/γ-Fe2O3/rGO Coating with Highly Efficient Visible-Light-Induced Self-Cleaning Properties for Metallic Artifacts.

A novel nanohybrid composite of TiO2, SiO2, γ-Fe2O3, and reduced graphene oxide (TiO2@Si:Fe:rGO) is fabricated by the sol-gel method. The properties of the coated film were examined by structural and self-cleaning analyses using simulated discoloration/soiling and roofing tests. The fabricated transparent TiO2@Si:Fe:rGO composite showed excellent photoactivity and wettability, behaving well in self-cleaning applications. The addition of SiO2 improved the crystalline structure and surface hydroxylation of TiO2 nanoparticles. γ-Fe2O3 decreased the recombination rate of e-/h+ pairs, and significantly improved photocatalytic activity under visible light. Moreover, rGO sheets as excellent electron acceptors and transporters also reduced recombination, as well as affected wettability, achieving superhydrophilicity under irradiation. The coated substrate showed excellent resistance to simulated acid rain and significantly preserved the substrate from soiling in roofing tests.