Helical Milling of CFRP/Ti6Al4V Stacks Using Nano Fluid Based Minimum Quantity Lubrication (NF-MQL): Investigations on Process Performance and Hole Integrity.

The structural components in the aeronautical industry require CFRP/Ti6Al4V stacks to be processed together, which results in poor hole integrity due to the thermal properties of the materials and challenges related to processability. These challenges include quality variation of the machined holes because of the limitations in process properties. Therefore, a novel solution through helical milling is investigated in the study using nano fluid based minimum quantity lubrication (NF-MQL). The analysis of variance shows, for Ti6Al4V, eccentricity (PCR = 28.56%), spindle speed (Ti) (PCR = 42.84%), and tangential feed (PCR = 8.61%), and for CFRP, tangential feed (PCR = 40.16%), spindle speed (PCR = 28.75%), and eccentricity (PCR = 8.41%) are the most significant parameters for diametric error. Further on, the rise in the circularity error is observed because of prolonged tool engagement at a higher value of tangential feed. Moreover, the surface roughness of Ti was reduced with an increasing percentage of MoS2 in the lubricant. The spindle speed (37.37%) and lubricant (45.76%) have a potential influence on the processing temperature, as evident in the analysis of variance. Similarly, spindle speed Ti (61.16%), tangential feed (23.37%), and lubrication (11.32%) controlled flank wear, which is critical to tool life. Moreover, the concentration of MoS2 decreased edge wear from ~105 µm (0.5% concentration) to ~70 µm (1% concentration). Thorough analyses on process performance in terms of hole accuracy, surface roughness, processing temperature, and tool wear are carried out based on the physical science of the process for cleaner production. The NF-MQL has significantly improved process performance and hole integrity.

Surface modification for osseointegration of Ti6Al4V ELI using powder mixed sinking EDM.

Biomedical implant rejection due to micromotion and inflammation around an implant leads to osteolysis and eventually has an implant failure because of poor osseointegration. To enhance osseointegration, the implant surface modification both at the nano and micro-scale levels is preferred to result in an enhanced interface between the body tissue and implant. The present study focuses on the modification of the surface of Titanium (α+ß) ELI medical grade alloy using powder-mixed electric discharge machining (PMEDM). Pulse current, on/off time, and various silicon carbide (SiC) powder concentrations are used as input parameters to comprehend desired surface modifications. Powder concentration is considered as the most important factor to control surface roughness and recast layer depth. A significant decrease in surface fracture density and roughness is observed using a 20 g/l concentration of SiC particles. Elemental mapping analysis has confirmed the migration of Si and the generation of promising surface texture and chemistry. Oxides and carbides enriched surface improved the microhardness of the re-solidified layer from 320 HV to 727 HV. Surface topology reveals nano-porosity (50-200 nm) which enhances osseointegration due to the absorption of proteins especially collagen to the surface.