Synthesis of TiO2-(B) Nanobelts for Acetone Sensing.

Titanium dioxide nanobelts were prepared via the alkali-hydrothermal method for application in chemical gas sensing. The formation process of TiO2-(B) nanobelts and their sensing properties were investigated in detail. FE-SEM was used to study the surface of the obtained structures. The TEM and XRD analyses show that the prepared TiO2 nanobelts are in the monoclinic phase. Furthermore, TEM shows the formation of porous-like morphology due to crystal defects in the TiO2-(B) nanobelts. The gas-sensing performance of the structure toward various concentrations of hydrogen, ethanol, acetone, nitrogen dioxide, and methane gases was studied at a temperature range between 100 and 500 °C. The fabricated sensor shows a high response toward acetone at a relatively low working temperature (150 °C), which is important for the development of low-power-consumption functional devices. Moreover, the obtained results indicate that monoclinic TiO2-B is a promising material for applications in chemo-resistive gas detectors.

Wake-up Free Ferroelectric Rhombohedral Phase in Epitaxially Strained ZrO2 Thin Films.

Zirconia- and hafnia-based thin films have attracted tremendous attention in the past decade because of their unexpected ferroelectric behavior at the nanoscale, which enables the downscaling of ferroelectric devices. The present work reports an unprecedented ferroelectric rhombohedral phase of ZrO2 that can be achieved in thin films grown directly on (111)-Nb:SrTiO3 substrates by ion-beam sputtering. Structural and ferroelectric characterizations reveal (111)-oriented ZrO2 films under epitaxial compressive strain exhibiting switchable ferroelectric polarization of about 20.2 µC/cm2 with a coercive field of 1.5 MV/cm. Moreover, the time-dependent polarization reversal characteristics of Nb:SrTiO3/ZrO2/Au film capacitors exhibit typical bell-shaped curve features associated with the ferroelectric domain reversal and agree well with the nucleation limited switching (NLS) model. The polarization-electric field hysteresis loops point to an activation field comparable to the coercive field. Interestingly, the studied films show ferroelectric behavior per se, without the need to apply the wake-up cycle found in the orthorhombic phase of ZrO2. Overall, the rhombohedral ferroelectric ZrO2 films present technological advantages over the previously studied zirconia- and hafnia-based thin films and may be attractive for nanoscale ferroelectric devices.

Palladium/palladium oxide coated electrospun fibers for wearable sweat pH-sensors.

The work describes the development of a flexible, hydrogel embedded pH-sensor that can be integrated in inexpensive wearable and non-invasive devices at epidermal level for electrochemical quantification of H+ ions in sweat. Such a device can be useful for swift, real time diagnosis and for monitoring specific conditions. The sensors' working electrodes are flexible poly(methyl methacrylate) electrospun fibers coated with a thin gold layer and electrochemically functionalized with nanostructured palladium/palladium oxide. The response to H+ ions is investigated by cyclic voltammetry and electrochemical impedance spectroscopy while open circuit potential measurements show a sensitivity of aprox. -59 mV per pH unit. The modification of the sensing interface upon basic and acid treatment is characterized by scanning and transmission electron microscopy and the chemical composition by X-ray photoelectron spectroscopy. In order to demonstrate the functionality of the pH-sensor at epidermal level, as a wearable device, the palladium/palladium oxide working electrode and silver/silver chloride reference electrode are embedded within a pad of polyacrylamide hydrogel and measurements in artificial sweat over a broad pH range were performed. Sensitivity up to -28 mV/pH unit, response time below 30 s, temperature dependence of approx. 1 mV/°C as well as the minimum volume to which the sensor responses of 250 nanoliters were obtained for this device. The proposed configuration represents a viable alternative making use of low-cost and fast fabrication processes and materials.

Ambiguous Role of Growth-Induced Defects on the Semiconductor-to-Metal Characteristics in Epitaxial VO2/TiO2 Thin Films.

Controlling the semiconductor-to-metal transition temperature in epitaxial VO2 thin films remains an unresolved question both at the fundamental as well as the application level. Within the scope of this work, the effects of growth temperature on the structure, chemical composition, interface coherency and electrical characteristics of rutile VO2 epitaxial thin films grown on TiO2 substrates are investigated. It is hereby deduced that the transition temperature is lower than the bulk value of 340 K. However, it is found to approach this value as a function of increased growth temperature even though it is accompanied by a contraction along the V4+-V4+ bond direction, the crystallographic c-axis lattice parameter. Additionally, it is demonstrated that films grown at low substrate temperatures exhibit a relaxed state and a strongly reduced transition temperature. It is suggested that, besides thermal and epitaxial strain, growth-induced defects may strongly affect the electronic phase transition. The results of this work reveal the difficulty in extracting the intrinsic material response to strain, when the exact contribution of all strain sources cannot be effectively determined. The findings also bear implications on the limitations in obtaining the recently predicted novel semi-Dirac point phase in VO2/TiO2 multilayer structures.

Facile, high yield ultrasound mediated protocol for ZnO hierarchical structures synthesis: Formation mechanism, optical and photocatalytic properties.

Hierarchical flowers-like zinc oxide structures have been successfully obtained by a simple and fast ultrasound-assisted method performed in a ordinary ultrasonic bath using an ammonia solution and zinc acetate, in the absence of any surfactant or template. The composition, structure, crystallinity, morphology and optical properties of the materials obtained at different ultrasound irradiation times were characterized by infrared, UV-Vis and photoluminescence spectroscopy, X-ray diffraction, scanning and transmission electron microscopy investigations. It was proved that the ultrasound irradiation time manipulates both the defect content (implicit the photoluminescent properties) and morphology of the ZnO materials: shorter irradiation times leads to the synthesis of high-defected ZnO structures of flower morphology with triangular-shaped petals, while higher irradiation times favours the formation of low-defected ZnO structures with tipped rod-like petals. A plausible growth mechanism of the architectures that implies aggregation via oriented attachment followed by an Ostwald ripening is advanced based on these results. The ZnO flower-like structures present high photocatalytic activities, a total phenol mineralization being registered in the case of visible light experiments. Electron-spin resonance measurements demonstrate the generation of reactive oxygen species, namely hydroxyl radicals but also C centred radicals adducts derived most probable from the residual acetate adsorbed on ZnO surface.

High Permittivity (1 - x)Ba(Zr(0.2)Ti(0.8))O3 - x(Ba(0.7)Ca(0.3))TiO3 (x = 0.45) Epitaxial Thin Films with Nanoscale Phase Fluctuations.

Epitaxial (1 - x)Ba(Ti0.8Zr0.2)TiO3 - x(Ba0.7Ca0.3)TiO3, x = 0.45 (BCZT 45), thin films have been deposited on (001) SrTiO3 (STO) and (001/100) SrLaAlO4 (SLAO) substrates by pulsed laser deposition. X-ray diffraction and high-resolution transmission electron microscopy (HRTEM) confirmed the epitaxial growth of the films. A high structural quality has been evidenced for the BCZT/STO films. Geometric phase analysis (GPA) associated with the HRTEM enabled us to obtain microstrain analysis and the in-plane and out-of-plane lattice parameter variation on different areas. Tetragonality ratio fluctuations at nanoscale level which are relevant for the existence of nanodomains have been evidenced on the BCZT/STO films. The in-plane dielectric constant has been measured on interdigital electrodes deposited by lift-off technique on the top of the films. High values of dielectric permittivity (>3000) combined with low dielectric loss (<0.01) are obtained for BCZT 45 film deposited on STO substrate, showing nearly constant values between 1 kHz and 10 MHz. The high dielectric permittivity of BCZT thin films was attributed to their high structural quality and to the loss of rotation stability of the polarization associated with the presence of nanodomains. This results into a divergence of fluctuations of polarization direction and a peak of dielectric susceptibility. The enhanced switching of such nanodomain configuration was probed by piezoforce microscopy, by writing and reading domains during topography scanning.

Synthesis and exceptional thermal stability of Mg-based bimetallic nanoparticles during hydrogenation.

Here we report the extraordinary thermal stability of Mg rich bimetallic nanoparticles (NPs), which is important for hydrogen storage technology. The enhanced NP stability is accomplished because of two critical improvements: (i) no void development within NPs (nanoscale Kirkendall effect) during their formation and (ii) suppressed Mg evaporation and NP hollowing during Mg hydrogenation at elevated temperature. The mechanism leading to the improved thermal stability of Mg-based bimetallic NPs is shown to be due to MgH2 hydride formation before evaporation can take place. These findings were tested for various compositions of Mg with Ni, Cu, and Ti, which are interesting combinations of materials for hydrogen storage systems. To achieve this we first demonstrate the synthesis mechanism of Mg-Ni and Mg-Cu NPs, which is well controlled at the single particle level, in order to accomplish multi-shell, alloy and intermetallic structures of interest for hydrogen storage tests. Aberration corrected transmission electron microscopy was carried out to unravel the detailed atomic structure and composition of the bimetallic NPs after production, processing, and hydrogenation. Finally, a simple and effective methodology is proposed for tuning the composition of the Mg-based bimetallic NPs based on the temperature-dependent nucleation behavior of NPs in the gas-phase.