1.
Int Dent J ; 73(6): 834-839, 2023 Dec.
Artigo em Inglês | MEDLINE | ID: mdl-37230841

RESUMO

AIM: This in vitro study aimed to evaluate the effect of matrix metalloproteinase (MMP) inhibitors on the bond strength of resin-cemented fibre posts to radicular dentin under an aged-loaded condition. MATERIALS AND METHODS: Radicular dentin was prepared and irrigated by MMP inhibitor solution after root canal obturation in 60 extracted single-rooted teeth based on 6 groups: (1) 2% chlorhexidine (CHX) + loaded; (2) CHX + unloaded; (3) 0.5% benzalkonium chloride (BAC) + loaded; (4) BAC + unloaded; (5) 17% ethylenediaminetetraacetic acid (EDTA) + loaded; and (6) EDTA + unloaded. After final rinsing, all specimens were sliced cross-sectionally and kept in a water bath for 12 months of ageing. Groups 1, 3, and 5 were subjected to cyclic loading. Push-out tests were conducted using a universal testing machine, and failure mode was examined. The data were analysed using 3-way analysis of variance and post hoc tests at α = 0.05. RESULTS: BAC + unloaded demonstrated the highest mean bond strength (3.12 ± 0.18 MPa; P < .001), while the BAC + loaded and CHX + loaded groups showed a significantly lower push-out bond strength than their unloaded counterparts. Mixed adhesive-cohesive failure was the most common failure mode observed. CONCLUSIONS: Without cycling loading, BAC was superior to CHX and EDTA in preserving the bond strength of resin-cemented fibre posts after 12 months of ageing. Loading significantly weakened the effectiveness of BAC and CHX in preserving the bond strength.


Assuntos
Colagem Dentária , Humanos , Idoso , Inibidores de Metaloproteinases de Matriz/farmacologia , Ácido Edético/farmacologia , Clorexidina/química , Clorexidina/farmacologia , Cimentos de Resina/química , Cimentos de Resina/farmacologia , Dentina , Teste de Materiais
SELEÇÃO DE REFERÊNCIAS
DETALHE DA PESQUISA