Supercurrent and multiple Andreev reflections in an InSb nanowire Josephson junction.

Epitaxially grown, high quality semiconductor InSb nanowires are emerging material systems for the development of high performance nanoelectronics and quantum information processing and communication devices and for the studies of new physical phenomena in solid state systems. Here, we report on measurements of a superconductor-normal conductor-superconductor junction device fabricated from an InSb nanowire with aluminum-based superconducting contacts. The measurements show a proximity-induced supercurrent flowing through the InSb nanowire segment with a critical current tunable by a gate in the current bias configuration and multiple Andreev reflection characteristics in the voltage bias configuration. The temperature dependence and the magnetic field dependence of the critical current and the multiple Andreev reflection characteristics of the junction are also studied. Furthermore, we extract the excess current from the measurements and study its temperature and magnetic field dependences. The successful observation of the superconductivity in the InSb nanowire-based Josephson junction device indicates that InSb nanowires provide an excellent material system for creating and observing novel physical phenomena such as Majorana fermions in solid-state systems.

Correlation-induced conductance suppression at level degeneracy in a quantum dot.

The large, level-dependent g factors in an InSb nanowire quantum dot allow for the occurrence of a variety of level crossings in the dot. While we observe the standard conductance enhancement in the Coulomb blockade region for aligned levels with different spins due to the Kondo effect, a vanishing of the conductance is found at the alignment of levels with equal spins. This conductance suppression appears as a canyon cutting through the web of direct tunneling lines and an enclosed Coulomb blockade region. In the center of the Coulomb blockade region, we observe the predicted correlation-induced resonance. Our findings are supported by numerical and analytical calculations.

The electrical and structural properties of n-type InAs nanowires grown from metal-organic precursors.

The electrical and structural properties of 111B-oriented InAs nanowires grown using metal-organic precursors have been studied. On the basis of electrical measurements it was found that the trends in carbon incorporation are similar to those observed in the layer growth, where an increased As/In precursor ratio and growth temperature result in a decrease in carbon-related impurities. Our results also show that the effect of non-intentional carbon doping is weaker in InAs nanowires compared to bulk, which may be explained by lower carbon incorporation in the nanowire core. We determine that differences in crystal quality, here quantified as the stacking fault density, are not the primary cause for variations in resistivity of the material studied. The effects of some n-dopant precursors (S, Se, Si, Sn) on InAs nanowire morphology, crystal structure and resistivity were also investigated. All precursors result in n-doped nanowires, but high precursor flows of Si and Sn also lead to enhanced radial overgrowth. Use of the Se precursor increases the stacking fault density in wurtzite nanowires, ultimately at high flows leading to a zinc blende crystal structure with strong overgrowth and very low resistivity.

Precursor evaluation for in situ InP nanowire doping.

The use of tetraethyltin (TESn) and dimethylzinc (DMZn) as in situ n- and p-dopant precursors during particle-assisted growth of InP nanowires is reported. Gate voltage dependent transport measurements demonstrate that the nanowires can be predictably synthesized as either n- or p-type. These doped nanowires can be characterized based on their electric field response and we find that n-type doping scales over a range from 10(17) to 10(19) cm(-3) with increasing input TESn dopant molar fraction. On the other hand, the p-type doping using DMZn saturates at low levels, probably related to a strong increase in nanowire growth rate with increasing DMZn molar fractions. By optimizing growth conditions with respect to tapering, axial pn-junctions exhibiting rectifying behavior were fabricated. The pn-junctions can be operated as light emitting diodes.