Detecting ferroelectricity at micro- and nanoscales is crucial for advanced nanomaterials and materials with complicated topography. Switching spectroscopy piezoresponse force microscopy (SSPFM), which involves measuring piezoelectric hysteresis loops via a scanning probe microscopy tip, is a widely accepted approach to characterize polarization reversal at the local scale and confirm ferroelectricity. However, the local hysteresis loops acquired through this method often exhibit unpredictable shapes, a phenomenon often attributed to the influence of parasitic factors such as electrostatic forces and current flow. Our research has uncovered that the deviation in hysteresis loop shapes can be caused by spontaneous backswitching occurring after polarization reversal. Moreover, we've determined that the extent of this effect can be exacerbated when employing inappropriate SSPFM waveform parameters, including duration, frequency, and AC voltage amplitude. Notably, the conventional 'pulse-mode' SSPFM method has been found to intensify spontaneous backswitching. In response to these challenges, we have redesigned SSPFM approach by introducing the positive up-negative down (PUND) method within the 'step-mode' SSPFM. This modification allows for effective probing of local piezoelectric hysteresis loops in ferroelectrics with reversible piezoresponse while removing undesirable electrostatic contribution. This advancement extends the applicability of the technique to a diverse range of ferroelectrics, including semiconductor ferroelectrics and relaxors, promising a more reliable and accurate characterization of their properties.
RESUMO
Nanocomposite films of BiFeO3-Bi2Fe4O9 were fabricated on a sapphire substrate Al2O3 using the method of gas discharge high-frequency cathodic sputtering of a ceramic target with a stoichiometric composition in an oxygen atmosphere. The results of the film analysis using X-ray structural analysis, Raman scattering, XPS, and atomic force microscopy are presented. The lattice parameters, surface topography, chemical composition of the films, concentration, and average sizes of the crystallites for each phase were determined. It was shown that the ratio of the BiFeO3 to Bi2Fe4O9 phases in the obtained film is approximately 1:2. The sizes of the crystallites range from 15 to 17 nm. The optical and magnetic properties of the nanocomposite layers were studied, and the band gap width and magnetization hysteresis characteristic of ferromagnetic behavior were observed. The band gap width was found to be 1.9 eV for the indirect and 2.6 eV for the direct interband transitions. The magnetic properties are characterized by a hysteresis loop resembling a "wasp-waist" shape, indicating the presence of magnetic anisotropy.