Can Heated Distilled Water Effectively Prevent Precipitate Formation between NaOCl and CHX?

Introduction: The present study aimed to investigate the capacity of different irrigation protocols using heated distilled water at 65°C (HDW), in preventing the formation of the brown-orange precipitate observed after the interaction between sodium hypochlorite (NaOCl) and chlorhexidine (CHX). Methods: Forty human canines were selected, prepared, and cleaved in two halves. Images of delimited areas in each root canal thirds were obtained through a stereomicroscope (16x and 40x). After reassembly, the teeth were distributed into four groups (n = 10) according to the final irrigation protocol: G1 (no HDW): EDTA + NaOCl + CHX with conventional irrigation (CI); G2 (HDW + CI): EDTA with passive ultrasonic irrigation (PUI) + NaOCl (PUI) + HDW (CI) + CHX (PUI); G3 (HDW + PUI): EDTA + NaOCl + HDW + CHX with PUI; G4 (HDW + CUI): EDTA (PUI) + NaOCl (PUI) + HDW with continuous ultrasonic irrigation (CUI) + CHX (PUI). After irrigation, the teeth were re-separated and images of the same delimited areas were obtained again. Scores were assigned according to the amount of precipitate observed, comparing the initial and final images. The data were submitted to Kruskal-Wallis, Dunn and Friedman statistical tests (α = 5%). Results: G1(no HDW) showed the highest scores in the analysis between groups (p < 0.001), with a greater amount of precipitate in the cervical and medium thirds (p < 0.001). The thirds of the other experimental groups did not differ from each other (p > 0.05). Conclusion: The intermediate irrigation with heated distilled water at 65°C prevented the formation of brown-orange precipitate, regardless of the use of ultrasonic activation (PUI or CUI).

Impact of Heating Exposure on the Micro-Push-Out Bond Strength of Bioceramic Sealers.

Introduction: The aim of this study was to evaluate the effect of heating of bioceramic and epoxy resin-based sealers on their micro-push-out bond strength (BS) to root canal dentin. Methods: After criterial selection, 30 human teeth were decoronated and 1-mm thick slices (n = 60) were obtained perpendicularly along tooth axis, from cervical and middle root thirds, with a diamond disc attached to a cutting machine. In each slice, three 1.0-mm diameter orifices were made. After rinsing with 17% EDTA and 2.5% NaOCl, each orifice was filled with Bio-C Sealer or BioRoot RCS or AH Plus, according to the manufacturers' instructions. After filling, half of the slices (n = 30) were heated at 100°C for 1 min, and the other half were kept at room temperature. After 7 days-controlled storage, micro-push-out test was performed in a Universal Testing Machine. Failures were analyzed using a stereomicroscope. Statistical analysis was performed with One-Way ANOVA and post hoc Tukey (α = 5%) tests. Results: AH Plus demonstrated higher BS values after heating (p=0.001) when compared to nonheated. The other sealers did not show a statistically significant difference (p > 0.05). When heated, the average BS values for AH Plus were higher than for BioRoot RCS and Bio-C Sealer (p < 0.001). Cohesive failure mode was the most frequent, followed by adhesive and mixed ones. Conclusion: Heating provided a higher push-out BS to root dentin for AH Plus and did not influence BioRoot RCS or Bio-C sealer.