RESUMO
The welding of cemented carbide to tool steel is a challenging task, of scientific and industrial relevance, as it combines the high level of hardness of cemented carbide with the high level of fracture toughness of steel, while reducing the shaping cost and extending the application versatility, as its tribological, toughness, thermal and chemical properties can be optimally harmonised. The already existing joining technologies often impart either insufficient toughness or poor high-temperature strength to a joint to withstand the ever-increasing severe service condition demands. In this paper, a novel capacitor discharge welding (CDW) process is investigated for the case of a butt-joint between a tungsten carbide-cobalt (WC-Co) composite rod and an AISI M35 high-speed steel (HSS) rod. The latter was shaped with a conical-ended projection to promote a high current concentration and heat at the welding zone. CDW functions by combining a direct current (DC) electric current pulse and external uniaxial pressure after a preloading step, in which only uniaxial pressure is applied. The relatively high heating and cooling rates promote a thin layer of a characteristic ultrafine microstructure that combines high strength and toughness. Morphological analysis showed that the CDW process: (a) forms a sound and net shaped joint, (b) preserves the sub-micrometric grain structure of the original WC-Co composite base materials, via a transitional layer, (c) refines the microstructure of the original martensite of the HSS base material, and (d) results in an improved corrosion resistance across a 1-mm thick layer near the weld interface on the steel side. A nano-indentation test survey determined: (e) no hardness deterioration on the HSS side of the weld zone, although (f) a slight decrease in hardness was observed across the transitional layer on the composite side. Furthermore, (g) an indication of toughness of the joint was perceived as the size of the crack induced by processing the residual stress after sample preparation was unaltered.
RESUMO
Tungsten carbide-cobalt (WC-Co) composites are a class of advanced materials that have unique properties, such as wear resistance, hardness, strength, fracture-toughness and both high temperature and chemical stability. It is well known that the local indentation properties (i.e., nano- and micro-hardness) of the single crystal WC particles dispersed in such composite materials are highly anisotropic. In this paper, the nanoindentation response of the WC grains of a compact, full-density, sintered WC-10Co composite material has been investigated as a function of the crystal orientation. Our nanoindentation survey has shown that the nanohardness was distributed according to a bimodal function. This function was post-processed using the unique features of the finite mixture modelling theory. The combination of electron backscattered diffraction (EBSD) and statistical analysis has made it possible to identify the orientation of the WC crystal and the distinct association of the inherent nanoindentation properties, even for a small set (67) of nanoindentations. The proposed approach has proved to be faster than the already existing ones and just as reliable, and it has confirmed the previous findings concerning the relationship between crystal orientation and indentation properties, but with a significant reduction of the experimental data.
