High intergrain critical current density in fine-grain (Ba0.6K0.4)Fe2As2 wires and bulks.

The K- and Co-doped BaFe(2)As(2) (Ba-122) superconducting compounds are potentially useful for applications because they have upper critical fields (H(c2)) of well over 50 T, H(c2) anisotropy γ < 2and thin-film critical current densities J(c) exceeding 1 MA cm(-2) (refs 1-4) at 4.2 K. However, thin-film bicrystals of Co-doped Ba-122 clearly exhibit weak link behaviour for [001] tilt misorientations of more than about 5°, suggesting that textured substrates would be needed for applications, as in the cuprates. Here we present a contrary and very much more positive result in which untextured polycrystalline (Ba(0.6)K(0.4))Fe(2)As(2) bulks and round wires with high grain boundary density have transport critical current densities well over 0.1 MA cm(-2) (self-field, 4.2 K), more than 10 times higher than that of any other round untextured ferropnictide wire and 4-5 times higher than the best textured flat wire. The enhanced grain connectivity is ascribed to their much improved phase purity and to the enhanced vortex stiffness of this low-anisotropy compound (γ~1-2) when compared with YBa(2)Cu(3)O(7-x) (γ~5).

Strongly linked current flow in polycrystalline forms of the superconductor MgB2.

The discovery of superconductivity at 39 K in magnesium diboride, MgB2, raises many issues, a critical one being whether this material resembles a high-temperature copper oxide superconductor or a low-temperature metallic superconductor in terms of its behaviour in strong magnetic fields. Although the copper oxides exhibit very high transition temperatures, their in-field performance is compromized by their large anisotropy, the result of which is to restrict high bulk current densities to a region much less than the full magnetic-field-temperature (H-T) space over which superconductivity is found. Moreover, the weak coupling across grain boundaries makes transport current densities in untextured polycrystalline samples low and strongly sensitive to magnetic field. Here we report that, despite the multiphase, untextured, microscale, subdivided nature of our MgB2 samples, supercurrents flow throughout the material without exhibiting strong sensitivity to weak magnetic fields. Our combined magnetization, magneto-optical, microscopy and X-ray investigations show that the supercurrent density is mostly determined by flux pinning, rather than by the grain boundary connectivity. Our results therefore suggest that this new superconductor class is not compromized by weak-link problems, a conclusion of significance for practical applications if higher temperature analogues of this compound can be discovered.