RESUMO
Among the unique opportunities and developments that are currently being triggered by the fourth industrial revolution, developments in cutting tools have been following the trend of an ever more holistic control of manufacturing processes. Sustainable manufacturing is at the forefront of tools development, encompassing environmental, economic, and technological goals. The integrated use of sensors, data processing, and smart algorithms for fast optimization or real time adjustment of cutting processes can lead to a significant impact on productivity and energy uptake, as well as less usage of cutting fluids. Diamond is the material of choice for machining of non-ferrous alloys, composites, and ultrahard materials. While the extreme hardness, thermal conductivity, and wear resistance of CVD diamond coatings are well-known, these also exhibit highly auspicious sensing properties through doping with boron and other elements. The present study focuses on the thermal response of boron-doped diamond (BDD) coatings. BDD coatings have been shown to have a negative temperature coefficient (NTC). Several approaches have been adopted for monitoring cutting temperature, including thin film thermocouples and infrared thermography. Although these are good solutions, they can be costly and become impractical for certain finishing cutting operations, tool geometries such as rotary tools, as well as during material removal in intricate spaces. In the scope of this study, diamond/WC-Co substrates were coated with BDD by hot filament chemical vapor deposition (HFCVD). Scanning electron microscopy, Raman spectroscopy, and the van der Pauw method were used for morphological, structural, and electrical characterization, respectively. The thermal response of the thin diamond thermistors was characterized in the temperature interval of 20-400 °C. Compared to state-of-the-art temperature monitoring solutions, this is a one-step approach that improves the wear properties and heat dissipation of carbide tools while providing real-time and in-situ temperature monitoring.
RESUMO
Cobalt-cemented carbide micro-end mills were coated with diamond grown by chemical vapor deposition (CVD), with the purpose of micro-machining cemented carbides. The diamond coatings were designed with a multilayer architecture, alternating between sub-microcrystalline and nanocrystalline diamond layers. The structure of the coatings was studied by transmission electron microscopy. High adhesion to the chemically pre-treated WC-7Co tool substrates was observed by Rockwell C indentation, with the diamond coatings withstanding a critical load of 1250 N. The coated tools were tested for micro-end-milling of WC-15Co under air-cooling conditions, being able to cut more than 6500 m over a period of 120 min, after which a flank wear of 47.8 µm was attained. The machining performance and wear behavior of the micro-cutters was studied by scanning electron microscopy and energy-dispersive X-ray spectroscopy. Crystallographic analysis through cross-sectional selected area electron diffraction patterns, along with characterization in dark-field and HRTEM modes, provided a possible correlation between interfacial stress relaxation and wear properties of the coatings. Overall, this work demonstrates that high adhesion of diamond coatings can be achieved by proper combination of chemical attack and coating architecture. By preventing catastrophic delamination, multilayer CVD diamond coatings are central towards the enhancement of the wear properties and mechanical robustness of carbide tools used for micro-machining of ultra-hard materials.