The xerogels based on the aqueous solutions of urea in potassium silicate liquid glass (PSLG) were produced by CO2 bubbling and investigated. The structure and chemical composition of the obtained materials were analyzed. Using the SEM, XRD, IR-FT, DSC, and low energy local EDS analysis, it was recognized that the dried gels (xerogels) contained three forms of urea: oval crystals of regular shape appeared onto the surface of xerogel particles; fibrous crystals were located in the silicate matrix; and molecules/ions were incorporated into the silicate matrix. It was shown that an increase in [(NH2)2CO] in the gel-forming system promoted increased contents in crystalline forms of urea as well as the diameter of the fiber-shaped urea crystals. A rate of the urea release in water from the granulated xerogels containing 5.8, 12.6, and 17.9 wt.% of urea was determined by the photometric method. It was determined that the obtained urea-containing xerogels were characterized with a slow release of urea, which continued up to 120 days, and could be used as controlled release fertilizers containing useful nutrients (N, K).
RESUMO
Low-temperature (350 °C) vitrification in a KNO3-NaNO3-KHSO4-NH4H2PO4 system, containing various additives to improve the chemical durability of the obtained material, was investigated. It was shown that a glass-forming system with 4.2-8.4 wt.% Al nitrate admixtures could form stable and transparent glasses, whereas the addition of H3BO3 produced a glass-matrix composite containing BPO4 crystalline inclusions. Mg nitrate admixtures inhibited the vitrification process and only allowed obtaining glass-matrix composites with combinations with Al nitrate and boric acid. Using ICP and low-energy EDS point analyses, it was recognized that all the obtained materials contained nitrate ions in their structure. Various combinations of the abovementioned additives favored liquid phase immiscibility and crystallization of BPO4, KMgH(PO3)3, with some unidentified crystalline phases in the melt. The mechanism of the vitrification processes taking place in the investigated systems, as well as the water resistance of the obtained materials, was analyzed. It was shown that the glass-matrix composites based on the (K,Na)NO3-KHSO4-P2O5 glass-forming system, containing Al and Mg nitrates and B2O3 additives, had increased water resistance, in comparison with the parent glass composition, and could be used as controlled-release fertilizers containing the main useful nutrients (K, P, N, Na, S, B, and Mg).