RESUMO
Diglycidylether of vanillyl alcohol (DGEVA), in combination with mechanically recycled carbon fibers (RCFs), was used to make, via Radical-Induced Cationic Frontal Photopolymerization (RICFP), fully sustainable and bio-based conductive composites with good electrical conductivity and consequent Joule effect proprieties. Three different fiber lengths, using three different sieve sizes during the mechanical recycling process (0.2, 0.5, and 2.0 mm), were used in five different amounts (ranging from 1 to 25 phr). The samples were first characterized by dynamic mechanical thermal analysis (DMTA), followed byelectrical conductivity and Joule heating tests. More specifically, the mechanical properties of the composites increased when increasing fiber content. Furthermore, the composites obtained with the longest fibers showed the highest electrical conductivity, reaching a maximum of 11 S/m, due to their higher aspect ratio. In this context, the temperature reached by Joule effect was directly related to the electrical conductivity, and was able to reach an average and maximum temperatures of 80 °C and 120 °C, respectively, just by applying 6 V.
RESUMO
Graphene nanoplatelets (GNPs)/epoxy composites have been fabricated via gravity molding. The electrical and thermal properties of the composites have been studied with variable GNP type (C300, C500, and C750, whose surface areas are ~300, 500, and 750 m2/g, respectively), GNP loading (5, 10, 12, and 15 wt.%), and dispersion time via ultrasonication (0, 30, 60, and 120 min). By increasing the time of sonication of the GNP into the epoxy matrix, the electrical conductivity decreases, which is an effect of GNP fragmentation. The best results were observed with 10-12% loading and a higher surface area (C750), as they provide higher electrical conductivity, thereby preserving thermal conductivity. The influence of sonication over electrical conductivity was further analyzed via the study of the composite morphology by means of Raman spectroscopy and X-ray diffraction (XRD), providing information about the aspect ratio of GNPs. Moreover, electromagnetic shielding (EMI) has been studied up to 4 GHz. Composites with C750 and 120 min ultrasonication show the best performance in EMI shielding, influenced by their higher electrical conductivity.
RESUMO
The present study focuses on the multifunctional capabilities of carbon nanotube (CNT)-reinforced vitrimers. More specifically, the thermomechanical properties, the Joule effect heating capabilities, the electrical conductivity, the shape memory, and the chemical recycling capacity are explored as a function of the CNT content and the NH2/epoxy ratio. It is observed that the electrical conductivity increases with the CNT content due to a higher number of electrical pathways, while the effect of the NH2/epoxy ratio is not as prevalent. Moreover, the Tg of the material decreases when increasing the NH2/epoxy ratio due to the lower cross-link density, whereas the effect of the CNTs is more complex, in some cases promoting a steric hindrance. The results of Joule heating tests prove the suitability of the proposed materials for resistive heating, reaching average temperatures above 200 °C when applying 100 V for the most electrically conductive samples. Shape memory behavior shows an outstanding shape fixity ratio in every case (around 100%) and a higher shape recovery ratio (95% for the best-tested condition) when decreasing the NH2/epoxy ratio and increasing the CNT content, as both hinder the rearrangement of the dynamic bonds. Finally, the results of the recyclability tests show the ability to regain the nanoreinforcement for their further use. Therefore, from a multifunctional analysis, it can be stated that the proposed materials present promising properties for a wide range of applications, such as Anti-icing and De-icing Systems (ADIS), Joule heating devices for comfort or thermotherapy, or self-deployable structures, among others.
RESUMO
The Structural Health Monitoring (SHM) capabilities of a well-studied self-healing epoxy resin based on disulfide bonds, through the addition of carbon nanotubes (CNTs), are studied. Since these materials demonstrated, in recent works, a high dependency of the dynamic hardener content on the repair performance, this study aimed to analyze the effect of the vitrimeric chemistry on the electromechanical properties by studying different 2-aminophenyl disulfide (2-AFD) hardener and CNT contents. The electrical conductivity increases with both the CNT and AFD contents, in general. Moreover, an excess of AFD close to the stoichiometric ratio with a low CNT content improved the tensile strength by 45%, while higher AFD contents promoted its detriment by 41% due to a reduced crosslinking density. However, no significant difference in the mechanical properties was observed at a higher CNT content, regardless of the AFD ratio. The developed materials demonstrate a robust electromechanical response at quasi-static conditions. The sensitivity significantly increases at higher AFD ratios, from 0.69 to 2.22 for the 0.2 wt.%. CNT system, which is advantageous due to the enhanced repair performance of these vitrimeric materials with a higher hardener content. These results reveal the potential use of self-healing vitrimers as integrated SHM systems capable of detecting damages and self-repairing autonomously.
RESUMO
The manufacturing of Diels-Alder (D-A) crosslinked epoxy nanocomposites is an emerging field with several challenges to overcome: the synthesis is complex due to side reactions, the mechanical properties are hindered by the brittleness of these bonds, and the content of carbon nanotubes (CNT) added to achieve electroactivity is much higher than the percolation thresholds of other conventional resins. In this work, we develop nanocomposites with different D-A crosslinking ratios (0, 0.6, and 1.0) and CNT contents (0.1, 0.3, 0.5, 0.7, and 0.9 wt.%), achieving a simplified route and avoiding the use of solvents and side reactions by selecting a two-step curing method (100 °C-6 h + 60 °C-12 h) that generates the thermo-reversible resins. These reversible nanocomposites show ohmic behavior and effective Joule heating, reaching the dissociation temperatures of the D-A bonds. The fully reversible nanocomposites (ratio 1.0) present more homogeneous CNT dispersion compared to the partially reversible nanocomposites (ratio 0.6), showing higher electrical conductivity, as well as higher brittleness. For this study, the nanocomposite with a partially reversible matrix (ratio 0.6) doped with 0.7 CNT wt.% was selected to allow us to study its new smart functionalities and performance due to its reversible network by analyzing self-healing and thermoforming.
RESUMO
The zinc alkaline battery is one of the most popular sources of portable electrical energy, with more than 300,000 tons being consumed per year. Accordingly, it is critical to recycle its components. In this work, we propose the use of zinc oxide (ZnO) microparticles recovered from worn-out batteries as fillers of epoxy resins. These nanocomposites can be used as protective coatings or pigments and as structural composites with high thermal stability. The addition of ceramic nanofillers, such as ZnO or/and TiO2, could enhance the thermal and mechanical properties, and the hardness and hydrophobicity, of the epoxy resins, depending on several factors. Accordingly, different nanocomposites reinforced with recycled ZnO and commercial ZnO and TiO2 nanoparticles have been manufactured with different nanofiller contents. In addition to the different ceramic oxides, the morphology and size of fillers are different. Recycled ZnO are"desert roses" such as microparticles, commercial ZnO are rectangular parallelepipeds nanoparticles, and commercial TiO2 are smaller spherical nanoparticles. The addition of ceramic fillers produces a small increase of the glass transition temperature (<2%), together with an enhancement of the barrier effect of the epoxy resin, reducing the water diffusion coefficient (<21%), although the maximum water uptake remains constant. The nanocomposite water absorption is fully reversible by subsequent thermal treatment, recovering its initial thermomechanical behavior. The water angle contact (WCA) also increases (~12%) with the presence of ceramic particles, although the highest hydrophobicity (35%) is obtained when the epoxy resin reinforced with recycled flowerlike ZnO microparticles is etched with acid stearic and acetic acid, inducing the corrosion of the ZnO on the surface and therefore the increment of the surface roughness. The presence of desert rose ZnO particles enhances the de lotus effect.
RESUMO
This paper presents a process where carbon fibers and hydrogen can be recovered simultaneously through a two-stage thermal treatment of an epoxy-carbon fiber composite. For this purpose, some pieces of epoxy resin reinforced with carbon fiber fabrics have been fabricated and, after curing, have been pyrolyzed in an installation consisting of two reactors. In the first one, the thermal decomposition of the resin takes place, and in the second one, the gases and vapors coming from the first reactor are thermally treated. Once this process is completed, the solid generated is oxidized with air to eliminate the resin residues and carbonaceous products from the fibers surface. The recovered carbon fiber fabrics have been reused to make new cured parts and their electrical and mechanical properties have been measured. The results show that it is possible to obtain carbon fiber fabrics that can be processed as they leave the recycling process and that retain 80% of the tensile modulus, 70% of the flexural strength, and 50% of the interlaminar shear strength. At the same time, a gaseous stream with more than 66% by volume of hydrogen can be obtained, reaching a maximum of 81.7%.
RESUMO
In this paper, a novel carbon nanotube (CNT) polycaprolactone (PCL), epoxy, and glass fiber (GF) composite is reported. Here, the nanoreinforced composites show a flexural strength increase of around 30%, whereas the interlaminar shear strength increases by 10-15% in comparison to unenhanced samples. This occurs because the addition of the CNTs induces a better PCL/epoxy/GF interaction. Furthermore, the nanoparticles also give novel functionalities to the multiscale composite, such as strain and damage monitoring. Here, the electrical response of the tensile- and compressive-subjected faces was simultaneously measured during flexural tests as well as the transverse conductivity in interlaminar tests, showing an exceptional capability for damage detection. Moreover, it was observed that the electrical sensitivity increases with PCL content due to a higher efficiency of the dispersion process that promotes the creation of a more uniform electrical network.
RESUMO
Electrical and electromechanical properties of hybrid graphene nanoplatelet (GNP)/carbon nanotube (CNT)-reinforced composites were analyzed under two different sonication conditions. The electrical conductivity increases with increasing nanofiller content, while the optimum sonication time decreases in a low viscosity media. Therefore, for samples with a higher concentration of GNPs, an increase of sonication time of the hybrid GNP/CNT mixture generally leads to an enhancement of the electrical conductivity, up to values of 3 S/m. This means that the optimum sonication process to achieve the best performances is reached in the longest times. Strain sensing tests show a higher prevalence of GNPs at samples with a high GNP/CNT ratio, reaching gauge factors of around 10, with an exponential behavior of electrical resistance with applied strain, whereas samples with lower GNP/CNT ratio have a more linear response owing to a higher prevalence of CNT tunneling transport mechanisms, with gauge factors of around 3-4.
RESUMO
Electromechanical sensing devices, based on resins doped with carbon nanotubes, were developed by digital light processing (DLP) 3D printing technology in order to increase design freedom and identify new future and innovative applications. The analysis of electromechanical properties was carried out on specific sensors manufactured by DLP 3D printing technology with complex geometries: a spring, a three-column device and a footstep-sensing platform based on the three-column device. All of them show a great sensitivity of the measured electrical resistance to the applied load and high cyclic reproducibility, demonstrating their versatility and applicability to be implemented in numerous items in our daily lives or in industrial devices. Different types of carbon nanotubes-single-walled, double-walled and multi-walled CNTs (SWCNTs, DWCNTs, MWCNTs)-were used to evaluate the effect of their morphology on electrical and electromechanical performance. SWCNT- and DWCNT-doped nanocomposites presented a higher Tg compared with MWCNT-doped nanocomposites due to a lower UV light shielding effect. This phenomenon also justifies the decrease of nanocomposite Tg with the increase of CNT content in every case. The electromechanical analysis reveals that SWCNT- and DWCNT-doped nanocomposites show a higher electromechanical performance than nanocomposites doped with MWCNTs, with a slight increment of strain sensitivity in tensile conditions, but also a significant strain sensitivity gain at bending conditions.
RESUMO
A performance mapping of GNP/epoxy composites was developed according to their electromechanical and electrothermal properties for applications as strain sensors and Joule heaters. To achieve this purpose, a deep theoretical and experimental study of the thermal and electrical conductivity of nanocomposites has been carried out, determining the influence of both nanofiller content and sonication time. Concerning dispersion procedure, at lower contents, higher sonication times induce a decrease of thermal and electrical conductivity due to a more prevalent GNP breakage effect. However, at higher GNP contents, sonication time implies an enhancement of both electrical and thermal properties due to a prevalence of exfoliating mechanisms. Strain monitoring tests indicate that electrical sensitivity increases in an opposite way than electrical conductivity, due to a higher prevalence of tunneling mechanisms, with the 5 wt.% specimens being those with the best results. Moreover, Joule heating tests showed the dominant role of electrical mechanisms on the effectiveness of resistive heating, with the 8 wt.% GNP samples being those with the best capabilities. By taking the different functionalities into account, it can be concluded that 5 wt.% samples with 1 h sonication time are the most balanced for electrothermal applications, as shown in a radar chart.
RESUMO
Mechanical and strain sensing capabilities of carbon nanotube (CNT) reinforced composites manufactured by digital light processing (DLP) 3D printing technology have been studied. Both CNT content and a post-curing treatment effects have been analyzed. It has been observed that post-curing treatment has a significant influence on mechanical properties, with an increase of Young's modulus and glass transition temperature whereas their effect in electrical properties is not so important. Furthermore, the strain sensing tests show a linear response of electrical resistance with applied strain, with higher values of sensitivity when decreasing CNT content due to a higher interparticle distance. Moreover, the electrical sensitivity of bending tests is significantly lower than in tensile ones due to the compression subjected face effect. Therefore, the good gauge factor values (around 2-3) and the high linear response proves the applicability of the proposed nanocomposites in structural health monitoring applications.
RESUMO
The electrical response of NH2-functionalized graphene nanoplatelets composite materials under strain was studied. Two different manufacturing methods are proposed to create the electrical network in this work: (a) the incorporation of the nanoplatelets into the epoxy matrix and (b) the coating of the glass fabric with a sizing filled with the same nanoplatelets. Both types of multiscale composite materials, with an in-plane electrical conductivity of ~10-3 S/m, showed an exponential growth of the electrical resistance as the strain increases due to distancing between adjacent functionalized graphene nanoplatelets and contact loss between overlying ones. The sensitivity of the materials analyzed during this research, using the described procedures, has been shown to be higher than commercially available strain gauges. The proposed procedures for self-sensing of the structural composite material would facilitate the structural health monitoring of components in difficult to access emplacements such as offshore wind power farms. Although the sensitivity of the multiscale composite materials was considerably higher than the sensitivity of metallic foils used as strain gauges, the value reached with NH2 functionalized graphene nanoplatelets coated fabrics was nearly an order of magnitude superior. This result elucidated their potential to be used as smart fabrics to monitor human movements such as bending of fingers or knees. By using the proposed method, the smart fabric could immediately detect the bending and recover instantly. This fact permits precise monitoring of the time of bending as well as the degree of bending.