RESUMO
The discovery of two-dimensional electron gases at the heterointerface between two insulating perovskite-type oxides, such as LaAlO(3) and SrTiO(3), provides opportunities for a new generation of all-oxide electronic devices. Key challenges remain for achieving interfacial electron mobilities much beyond the current value of approximately 1,000 cm(2) V(-1) s(-1) (at low temperatures). Here we create a new type of two-dimensional electron gas at the heterointerface between SrTiO(3) and a spinel γ-Al(2)O(3) epitaxial film with compatible oxygen ions sublattices. Electron mobilities more than one order of magnitude higher than those of hitherto-investigated perovskite-type interfaces are obtained. The spinel/perovskite two-dimensional electron gas, where the two-dimensional conduction character is revealed by quantum magnetoresistance oscillations, is found to result from interface-stabilized oxygen vacancies confined within a layer of 0.9 nm in proximity to the interface. Our findings pave the way for studies of mesoscopic physics with complex oxides and design of high-mobility all-oxide electronic devices.
RESUMO
We report that Bi2Se3 thin films can be epitaxially grown on SrTiO3 substrates, which allow for very large tunablity in carrier density with a back gate. The observed low field magnetoconductivity due to weak antilocalization (WAL) has a very weak gate-voltage dependence unless the electron density is reduced to very low values. Such a transition in WAL is correlated with unusual changes in longitudinal and Hall resistivities. Our results suggest a much suppressed bulk conductivity at large negative gate voltages and a possible role of surface states in the WAL phenomena.