Ag0-Ginger Nanocomposites Integrated into Natural Hydrogelated Matrices Used as Antimicrobial Delivery Systems Deposited on Cellulose Fabrics.

In the textile, medical, and food industries, many of the applications have targeted the use of textile fabrics with antimicrobial properties. Obtaining eco-friendly coatings is of wide interest, especially for applications related to wound dressing or to food packaging. In order to obtain coatings with antimicrobial properties through environmentally friendly methods, a series of experiments were carried out on the use of natural polymers loaded with silver nanoparticles. In this study, coatings with antimicrobial properties were obtained by depositing natural composites based on rice flour, carob flour, or alginate on cotton fabrics. These antimicrobial coatings were multicomponent systems, in which the host matrix was generated via hydration of natural polymers. The nanocomposite obtained from the phytosynthesis of silver particles in ginger extract was embedded in hydrogel matrices. The multicomponent gels obtained by embedding silver nanoparticles in natural polymer matrices were deposited on cotton fabric and were studied in relation to nanoparticles and the type of host matrix, and the antimicrobial activity was evaluated. Fabrics coated with such systems provide a hydrophilic surface with antimicrobial properties and can therefore be used in various areas where textiles provide antibacterial protection.

Application of Lavandula angustifolia Mill. Extracts for the Phytosynthesis of Silver Nanoparticles: Characterization and Biomedical Potential.

Nanotechnology can offer a series of new "green" and eco-friendly methods for developing different types of nanoparticles, among which the development of nanomaterials using plant extracts (phytosynthesis) represents one of the most promising areas of research. This present study details the use of lavender flowers (Lavandula angustifolia Mill., well-known for their use in homeopathic applications) for the biosynthesis of silver nanoparticles with enhanced antioxidant and antibacterial properties. Several qualitative and quantitative assays were carried out in order to offer an image of the extracts' composition (the recorded total phenolics content varied between 21.0 to 40.9 mg GAE (gallic acid equivalents)/g dry weight (d.w.), while the total flavonoids content ranged between 3.57 and 16.8 mg CE (catechin equivalents)/g d.w.), alongside modern analytical methods (such as gas chromatography-mass spectrometry-GC-MS, quantifying 12 phytoconstituents present in the extracts). The formation of silver nanoparticles (AgNPs) using lavender extract was studied by UV-Vis spectroscopy, Fourier-transform infrared spectrometry (FTIR), scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)/zeta potential, with the selected nanoparticles having crystallite sizes of approx. 14.55 nm (AgNP-L2) and 4.61 nm, respectively (for AgNP-L4), and hydrodynamic diameters of 392.4 nm (for AgNP-L2) and 391.6 nm (for AgNP-L4), determined by DLS. A zeta potential of around -6.4 mV was displayed for both samples while presenting as large aggregates, in which nanoparticle clusters with dimensions of around 130-200 nm can be observed. The biomedical applications of the extracts and the corresponding phytosynthesized nanoparticles were evaluated using antioxidant and antimicrobial assays. The obtained results confirmed the phytosynthesis of the silver nanoparticles using Lavandula angustifolia Mill. extracts, as well as their antioxidant and antimicrobial potential.

Ganoderma lucidum-Mediated Green Synthesis of Silver Nanoparticles with Antimicrobial Activity.

"Green chemistry" is a simple and easily reproductible method that provides nanoparticles characterized by better stability and good dispersion in an aqueous solution. Nanoparticles can be synthesized by algae, bacteria, fungi, and plant extracts. Ganoderma lucidum is a commonly used medicinal mushroom with distinctive biological properties, such as antibacterial, antifungal, antioxidant, anti-inflammatory, anticancer, etc. In this study, aqueous mycelial extracts of Ganoderma lucidum were used to reduce AgNO3 to form silver nanoparticles (AgNPs). The biosynthesized nanoparticles were characterized by UV-visible spectroscopy, scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR) analysis. The maximum UV absorption was obtained at 420 nm, which represents the specific surface plasmon resonance band for biosynthesized silver nanoparticles. SEM images showed particles as predominantly spherical, while FTIR spectroscopic studies illustrated the presence of functional groups that can support the reducing of ion Ag+ to Ag(0). XRD peaks ratified the presence of AgNPs. The antimicrobial effectiveness of synthesized nanoparticles was tested against Gram-positive and Gram-negative bacterial and yeasts strains. The silver nanoparticles were effective against pathogens, inhibiting their proliferation, and thus reducing the risk to the environment and to public health.

Piezoelectric Biocomposites for Bone Grafting in Dentistry.

In this research, Hydroxyapatite-Potassium, Sodium Niobate-Chitosan (HA-KNN-CSL) biocomposites were synthesized, both as hydrogel and ultra-porous scaffolds, to offer two commonly used alternatives to biomaterials in dental clinical practice. The biocomposites were obtained by varying the content of low deacetylated chitosan as matrix phase, mesoporous hydroxyapatite nano-powder, and potassium-sodium niobate (K0.47Na0.53NbO3) sub-micron-sized powder. The resulting materials were characterized from physical, morpho-structural, and in vitro biological points of view. The porous scaffolds were obtained by freeze-drying the composite hydrogels and had a specific surface area of 18.4-24 m2/g and a strong ability to retain fluid. Chitosan degradation was studied for 7 and 28 days of immersion in simulated body fluid without enzymatic presence. All synthesized compositions proved to be biocompatible in contact with osteoblast-like MG-63 cells and showed antibacterial effects. The best antibacterial effect was shown by the 10HA-90KNN-CSL hydrogel composition against Staphylococcus aureus and the fungal strain Candida albicans, while a weaker effect was observed for the dry scaffold.

Multifunctional Finishing of Cotton Fabric with Curcumin Derivatives Coatings Obtained by Sol-Gel Method.

Textile materials with fluorescent, repellent, or antimicrobial properties are increasingly used in common applications. Obtaining multi-functional coatings is of wide interest, especially for applications related to signaling or to the medical field. In order to increase the performance (color properties, fluorescence lifetime, self-cleaning or antimicrobial properties) of textile materials with special uses, a series of research was carried out regarding the modification of surfaces with nanosols. In this study, coatings with multiple properties were obtained by depositing nanosols on cotton fabrics generated through sol-gel reactions. These multifunctional coatings are hybrid materials in which the host matrix is generated using tetraethylorthosilicate (TEOS) and network modifying organosilanes:dimethoxydimethylsilane (DMDMS) or dimethoxydiphenylsilane (DMDPS) in a 1:1 mass ratio. Two curcumin derivatives were embedded in siloxane matrices, a yellow one (CY) that is identical to bis-demethoxycurcumin (one of the natural constituents in turmeric) and a red dye (CR) that has a N,N-dimethylamino group grafted in position 4 of the dicinnamoylmethane skeleton of curcumin. The nanocomposites obtained by embedding curcumin derivatives in siloxane matrices were deposited on cotton fabric and studied in relation to the dye and the type of host matrix. Fabrics coated with such systems provide a hydrophobic surface, have fluorescent and antimicrobial properties, change color depending on the pH, and therefore can be used in various fields where textiles provide signaling properties, self-cleaning, or antibacterial protection. The coated fabrics maintained their good multifunctional properties even after several washing cycles.

Microbial Removal of Heavy Metals from Contaminated Environments Using Metal-Resistant Indigenous Strains.

Contamination of soil with heavy metals has become a matter of global importance due to its impact on agriculture, environmental integrity, and therefore human health and safety. Several microbial strains isolated from soil contaminated by long-term chemical and petrochemical activities were found to manifest various levels of tolerance to Cr, Pb, and Zn, out of which Bacillus marisflavi and Trichoderma longibrachiatum exhibited above-moderate tolerance. The concentrations of target heavy metals before and after bioremediation were determined using electrochemical screen-printed electrodes (SPE) modified with different nanomaterials. The morpho-structural SEM/EDX analyses confirmed the presence of metal ions on the surface of the cell, with metal uptake being mediated by biosorption with hydroxyl, carboxyl, and amino groups as per FTIR observations. T. longibrachiatum was observed to pose a higher bioremediation potential compared to B. marisflavi, removing 87% of Cr and 67% of Zn, respectively. Conversely, B. marisflavi removed 86% of Pb from the solution, compared to 48% by T. longibrachiatum. Therefore, the fungal strain T. longibrachiatum could represent a viable option for Cr and Zn bioremediation strategies, whereas the bacterial strain B. marisflavi may be used in Pb bioremediation applications.

Photocatalytic and Antibacterial Properties of Doped TiO2 Nanopowders Synthesized by Sol-Gel Method.

For environmental applications, nanosized TiO2-based materials are known as the most important photocatalyst and are intensively studied for their advantages such as their higher activity, lower price, and chemical and photoresist properties. Zn or Cu doped TiO2 nanoparticles with anatase crystalline structure were synthesized by sol-gel process. Titanium (IV) butoxide was used as a TiO2 precursor, with parental alcohol as a solvent, and a hydrolysing agent (ammonia-containing water) was added to obtain a solution with pH 10. The gels were characterized by TG/DTA analysis, SEM, and XPS. Based on TG/DTA results, the temperature of 500 °C was chosen for processing the powders in air. The structure of the samples thermally treated at 500 °C was analysed by XRD and the patterns show crystallization in a single phase of TiO2 (anatase). The surface of the samples and the oxidation states was investigated by XPS, confirming the presence of Ti, O, Zn and Cu. The antibacterial activity of the nanoparticle powder samples was verified using the gram-positive bacterium Staphylococcus aureus. The photocatalytic efficiency of the doped TiO2 nanopowders for degradation of methyl orange (MO) is here examined in order to evaluate the potential applications of these materials for environmental remediation.

Highlighting Bacteria with Calcifying Abilities Suitable to Improve Mortar Properties.

Biomineralization, the use of microorganisms to produce calcium carbonate, became a green solution for application in construction materials to improve their strength and durability. The calcifying abilities of several bacteria were investigated by culturing on a medium with urea and calcium ions. The characterization of the precipitates from bacterial cultures was performed using X-ray diffraction, Fourier transform infrared spectroscopy, and thermogravimetric analysis. The formation of carbonate crystals was demonstrated by optical and scanning electron microscopy. Water absorption and compressive strength measurements were applied to mortars embedded with sporal suspension. The efficiency of the supplementation of mortar mixtures with bacterial cells was evaluated by properties, namely the compressive strength and the water absorption, which are in a relationship of direct dependence, the increase in compressive strength implying the decrease in water absorption. The results showed that Bacillus subtilis was the best-performing bacterium, its introduction into the mortar producing an increase in compressive strength by 11.81% and 9.50%, and a decrease in water absorption by 11.79% and 10.94%, after 28 and 56 days of curing, respectively, as compared to standards. The exploitation of B. subtilis as a calcifying agent can be an interesting prospect in construction materials.

Fungal Based Biopolymer Composites for Construction Materials.

Environmental contamination, extensive exploitation of fuel sources and accessibility of natural renewable resources represent the premises for the development of composite biomaterials. These materials have controlled properties, being obtained through processes operated in mild conditions with low costs, and contributing to the valorization of byproducts from agriculture and industry fields. A novel board composite including lignocelullosic substrate as wheat straws, fungal mycelium and polypropylene embedded with bacterial spores was developed and investigated in the present study. The bacterial spores embedded in polymer were found to be viable even after heat exposure, helping to increase the compatibility of polymer with hydrophilic microorganisms. Fungal based biopolymer composite was obtained after cultivation of Ganoderma lucidum macromycetes on a mixture including wheat straws and polypropylene embedded with spores from Bacillus amyloliquefaciens. Scanning electron microscopy (SEM) and light microscopy images showed the fungal mycelium covering the substrates with a dense network of filaments. The resulted biomaterial is safe, inert, renewable, natural, biodegradable and it can be molded in the desired shape. The fungal biocomposite presented similar compressive strength and improved thermal insulation capacity compared to polystyrene with high potential to be used as thermal insulation material for applications in construction sector.

Preparation and Characterization of Silica Nanoparticles and of Silica-Gentamicin Nanostructured Solution Obtained by Microwave-Assisted Synthesis.

In this research work, silica nanoparticles and silica-gentamicin nanostructured solution were synthesized by using the microwave-assisted synthesis, in basic medium, using two silane precursors (tetraethylorthosilicate and octyltriethoxysilane) and the antibiotic (gentamicin sulfate). The prepared materials were characterized through Fourier transform infrared (FTIR) spectroscopy, TGA analysis, transmission electron microscopy (TEM), and atomic force microscopy (AFM) to investigate the morphology and structure. Antimicrobial studies of the silica-gentamicin nanostructured solution versus silica nanoparticles were performed against Pseudomonas aeruginosa, Staphylococcus aureus, and Escherichia coli. FTIR spectra showed that the gentamicin has been loaded to the silica nanoparticles. AFM analysis showed that the morphology of the silica-gentamicin nanostructured solution has changed, and agglomerations of particles are present at the surface. Antimicrobial testing, performed using the diffusion method through spot inoculation, indicates that the silica-gentamicin nanostructured solution exhibited activity against the resistant strain. The obtained silica-gentamicin solution can be used as biochemical agent for the prevention and treatment of microorganisms which are deposited on different surfaces (e.g., glass, plastic, ceramic).

Modeling the Properties of Curcumin Derivatives in Relation to the Architecture of the Siloxane Host Matrices.

Research in the field of natural dyes has constantly focused on methods of conditioning curcumin and diversifying their fields of use. In this study, hybrid materials were obtained from modified silica structures, as host matrices, in which curcumin dyes were embedded. The influence of the silica network structure on the optical properties and the antimicrobial activity of the hybrid materials was monitored. By modifying the ratio between phenyltriethoxysilane:diphenyldimethoxysilane (PTES:DPDMES), it was possible to evaluate the influence the organosilane network modifiers had on the morphostructural characteristics of nanocomposites. The nanosols were obtained by the sol-gel method, in acid catalysis. The nanocomposites obtained were deposited as films on a glass support and showed a transmittance value (T measured at 550 nm) of around 90% and reflectance of about 11%, comparable to the properties of the uncovered support. For the coatings deposited on PET (polyethylene terephthalate) films, these properties remained at average values of T550 = 85% and R550 = 11% without significantly modifying the optical properties of the support. The sequestration of the dye in silica networks reduced the antimicrobial activity of the nanocomposites obtained, by comparison to native dyes. Tests performed on Candida albicans fungi showed good results for the two curcumin derivatives embedded in silica networks (11-18 mm) by using the spot inoculation method; in comparison, the alcoholic dye solution has a spot diameter of 20-23 mm. In addition, hybrids with the CA derivative were the most effective (halo diameter of 17-18 mm) in inhibiting the growth of Gram-positive bacteria, compared to the curcumin derivative in alcoholic solution (halo diameter of 21 mm). The results of the study showed that the presence of 20-40% by weight DPDMES in the composition of nanosols is the optimal range for obtaining hybrid films that host curcumin derivatives, with potential uses in the field of optical films or bioactive coatings.

Effects of Foliar Treatment with a Trichoderma Plant Biostimulant Consortium on Passiflora caerulea L. Yield and Quality.

The influence of spore concentration on the ability of a Trichoderma consortium to colonize the Passiflora caerulea phyllosphere was evaluated by determining the effects of foliar treatments with two spore concentrations, in two repeated treatments, on the morphological, physiological, and ultrastructural characteristics, and on the yield and quality of P. caerulea. The studied crop quality features were related to its nutraceutical use: the accumulation of polyphenols and flavonoids, antioxidant activity, and effects on mouse fibroblast L929 cells. The Trichoderma consortium consisted of two strains, T. asperellum T36b and T. harzianum Td50b, and the concentrations used were 106 colony forming units (cfu)/mL and 108 cfu/mL. As a reference treatment, a commercial product that was based on herbs and algal extracts was used. As compared to the negative control, the treatment with the Trichoderma consortium at 108 cfu/mL concentration determines the accumulation of higher level of polyphenols and flavonoids and increased antioxidant activity. This enhancement of P. caerulea quality characteristics after treatment with the higher concentration of Trichoderma consortium was associated with larger leaves, increased number and size of chloroplasts, improved plant physiology characteristics, and an increased yield. The treatment with high concentration of Trichoderma consortium spores promotes phyllosphere colonization and benefits both crop yield and quality.

Degradation of keratin substrates by keratinolytic fungi

Background: The hydrolysis of keratin wastes by microorganisms is considered a biotechnological alternative for recycling and valorization through keratinolytic microorganisms. Despite their resistant structure, keratin wastes can be efficiently degraded by various microorganisms through the secretion of keratinases, which are promising enzymes for several applications, including detergents, fertilizers, and leather and textile industry. In an attempt to isolate keratinolytic microorganisms that can reach commercial exploitation as keratinase producers, the current work assesses the dynamics of keratin biodegradation by several keratinolytic fungal strains isolated from soil. The activity of fungal strains to degrade keratin substrates was evaluated by SEM, FTRIR-ATR spectra and TGA analysis. Results: SEM observations offered relevant information on interactions between microorganism and structural elements of hair strands. FTIR spectra of the bands at 1035­1075 cm-1 assigned to sulfoxide bond appeared because of S­S bond breaking, which demonstrated the initiation of keratin biodegradation. According to TGA, in the second zone of thermal denaturation, where keratin degradation occurs, the highest weight loss of 71.10% was obtained for sample incubated with Fusarium sp. 1A. Conclusions: Among the tested strains, Fusarium sp. 1A was the most active organism in the degradation process with the strongest denaturation of polypeptide chains. Because keratinolytic microorganisms and their enzymes keratinases represent a subject of scientific and economic interest because of their capability to hydrolyze keratin, Fusarium sp. 1A was selected for further studies.

New Strigolactone Mimics as Exogenous Signals for Rhizosphere Organisms.

The importance of strigolactones in plant biology prompted us to synthesize simplified strigolactone mimics effective as exogenous signals for rhizosphere organisms. New strigolactone mimics easily derived from simple and available starting materials in significant amounts were prepared and fully characterized. These compounds contain an aromatic or heterocyclic ring, usually present in various bioactive molecules, connected by an ether link to a furan-2-one moiety. The new synthesized strigolactone mimics were confirmed to be active on plant pathogenic fungi and parasitic weed seeds.