K5Eu1-xTbx(MoO4)4 Phosphors for Solid-State Lighting Applications: Aperiodic Structures and the Tb3+ → Eu3+ Energy Transfer.

This paper describes the influence of sintering conditions and Eu3+/Tb3+ content on the structure and luminescent properties of K5Eu1-xTbx(MoO4)4 (KETMO). KETMO samples were synthesized under two different heating and cooling conditions. A K5Tb(MoO4)4 (KTMO) colorless transparent single crystal was grown by the Czochralski technique. A continuous range of solid solutions with a trigonal palmierite-type structure (α-phase, space group R3̅m) were presented only for the high-temperature (HT or α-) KETMO (0 ≤ x ≤ 1) prepared at 1123 K followed by quenching to liquid nitrogen temperature. The reversibility of the ß â†” α phase transition for KTMO was revealed by a differential scanning calorimetry (DSC) study. The low-temperature (LT)LT-K5Eu0.6Tb0.4(MoO4)4 structure was refined in the C2/m space group. Additional extra reflections besides the reflections of the basic palmierite-type R-subcell were present in synchrotron X-ray diffraction (XRD) patterns of LT-KTMO. LT-KTMO was refined as an incommensurately modulated structure with (3 + 1)D superspace group C2/m(0ß0)00 and the modulation vector q = 0.684b*. The luminescent properties of KETMO prepared at different conditions were studied and related to their structures. The luminescence spectra of KTMO samples were represented by a group of narrow lines ascribed to 5D4 → 7FJ (J = 3-6) Tb3+ transitions with the most intense emission line at 547 nm. The KTMO single crystal demonstrated the highest luminescence intensity, which was ∼20 times higher than that of LT-KTMO. The quantum yield λex = 481 nm for the KTMO single crystal was measured as 50%. The intensity of the 5D4 → 7F5 Tb3+ transition increased with the increase of x from 0.2 to 1 for LT and HT-KETMO. Emission spectra of KETMO samples with x = 0.2-0.9 at λex = 377 nm exhibited an intense red emission at ∼615 nm due to the 5D0 → 7F2 Eu3+ transition, thus indicating an efficient energy transfer from Tb3+ to Eu3+.

KTb(MoO4)2 Green Phosphor with K+-Ion Conductivity: Derived from Different Synthesis Routes.

The influence of different synthesis routes on the structure and luminescent properties of KTb(MoO4)2 (KTMO) was studied. KTMO samples were prepared by solid-state, hydrothermal, and Czochralski techniques. These methods lead to the following different crystal structures: a triclinic scheelite-type α-phase is the result for the solid-state method, and an orthorhombic KY(MoO4)2-type γ-phase is the result for the hydrothermal and Czochralski techniques. The triclinic α-KTMO phase transforms into the orthorhombic γ-phase when heated at 1273 K above the melting point, while KTMO prepared by the hydrothermal method does not show phase transitions. The influence of treatment conditions on the average crystallite size of orthorhombic KTMO was revealed by X-ray diffraction line broadening measurements. The electrical conductivity was measured on KTMO single crystals. The orthorhombic structure of KTMO that was prepared by the hydrothermal method was refined using synchrotron powder X-ray diffraction data. K+ cations are located in extensive two-dimensional channels along the c-axis and the a-axis. The possibility of K+ migration inside these channels was confirmed by electrical conductivity measurements, where strong anisotropy was observed in different crystallographic directions. The evolution of luminescent properties as a result of synthesis routes and heating and cooling conditions was studied and compared with data for the average crystallite size calculation and the grain size determination. All samples' emission spectra exhibit a strong green emission at 545 nm due to the 5D4 → 7F5 Tb3+ transition. The maximum of the integral intensity emission for the 5D4 → 7F5 emission under λex = 380 nm excitation was found for the KTMO crashed single crystal.