Adhesives free bark panels: An alternative application for a waste material.

The proportion of bark in tree trunks is in the range of ~ 10-20%. This large amount of material is currently mainly considered as a by- or even waste-product by the timber processing industry. Recently, efforts towards the use of bark have been made, e.g. as a raw material to harvest different chemical compounds or as an additive for wood particle boards. Our motivation for this work was to keep the bark in an almost natural state and explore alternative processes and applications for use. The traditional method of de-barking tree trunks by peeling was used to harvest large bark pieces. Two pieces of peeled bark were placed crosswise, with the rhytidom side (outer bark) facing each other. After different conditioning steps, bark pieces were hot pressed to panels without adding adhesives. These experiments on bark samples of different Central European tree species suggest that production of panels with species dependent properties is possible and feasible. This is a step towards producing sustainable panels by using a natural waste material, while retaining its beneficial structure and its natural chemical composition.

Cellulose lattice strains and stress transfer in native and delignified wood.

Small specimens of spruce wood with different degrees of delignification were studied using in-situ tensile tests and simultaneous synchrotron X-ray diffraction to reveal the effect of delignification and densification on their tensile properties at relative humidities of 70-80 %. In addition to mechanical properties, these analyses yield the ratio of strains in the cellulose crystals and in the bulk, which reflects the stress-transfer to crystalline cellulose. While the specific modulus of elasticity slightly increases from native wood by partial or complete delignification, the lattice strain ratio does not show a significant change. This could indicate a compensatory effect from the decomposition of the amorphous matrix by delignification and from a tighter packing of cellulose crystals that would increase the stress transfer. The reduced strain to failure and maximum lattice strain of delignified specimens suggests that the removal of lignin affects the stress-strain behavior with fracture at lower strain levels.

Advanced materials design based on waste wood and bark.

Trees belong to the largest living organisms on Earth and plants in general are one of our main renewable resources. Wood as a material has been used since the beginning of humankind. Today, forestry still provides raw materials for a variety of applications, for example in the building industry, in paper manufacturing and for various wood products. However, many parts of the tree, such as reaction wood, branches and bark are often discarded as forestry residues and waste wood, used as additives in composite materials or burned for energy production. More advanced uses of bark include the extraction of chemical substances for glues, food additives or healthcare, as well as the transformation to advanced carbon materials. Here, we argue that a proper understanding of the internal fibrous structure and the resulting mechanical behaviour of these forest residues allows for the design of materials with greatly varying properties and applications. We show that simple and cheap treatments can give tree bark a leather-like appearance that can be used for the construction of shelters and even the fabrication of woven textiles. This article is part of the theme issue 'Bio-derived and bioinspired sustainable advanced materials for emerging technologies (part 1)'.