Biocompatibility analysis and chemical characterization of Mn-doped hydroxyapatite.

The present work studies the effect of Mn doping on the crystalline structure of the Hap synthesized by the hydrothermal method at 200 °C for 24 h, from Ca(OH)2 and (NH4)2HPO4, incorporating MnCl2 to 0.1, 0.5, 1.0, 1.5 and 2.0 %wt of Mn concentrations. Samples were characterized by the X-Ray Diffraction technique, which revealed the diffraction peaks that corresponded to the hexagonal and monoclinic phase of the Hap; it was observed that the average size of crystallite decreased from 23.67 to 22.69 nm as the concentration of Mn increased. TEM shows that in all samples, there are two distributions of particle sizes; one corresponds to nanorods with several tens of nanometers in length, and the other in which the diameter and length are very close. FTIR analysis revealed absorption bands corresponding to the PO4-3 and OH- groups characteristic of the Hap. It was possible to establish a substitution mechanism between the Mn and the ions of Ca+2 of the Hap. From the Alamar blue test, a cell viability of 86.88% ± 5 corresponding to the sample of Hap at 1.5 %wt Mn was obtained, considered non-cytotoxic according to ISO 10993-5. It also evaluated and demonstrated the good osteoinductive properties of the materials, which were verified by histology and immunofluorescence expression of osteogenic markers. Adhesion, viability, biocompatibility and osteoinductive properties, make these materials candidates for future applications in bone tissue engineering with likely uses in regenerative medicine.

Wet chemical synthesis of nanocrystalline hydroxyapatite flakes: effect of pH and sintering temperature on structural and morphological properties.

Wet chemical synthesis of hydroxyapatite (HAp) nanostructures was carried out with different solution pH values (9, 10 and 11) and sintering temperatures (300°C, 500°C, 700°C and 900°C). The effects of pH and sintering temperature on the structural and morphological properties of nanocrystalline HAp powders were presented. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and scanning electron microscopy (SEM) analysis were performed to obtain the crystalline structure, chemical composition, morphology and particle size of the HAp powders. The TEM analysis is used in order to observe the rod- and flake-like HAp structures. XRD confirms the presence of both HAp hexagonal and monetite phases, although the monetite phase was less abundant in the resultant powders. Increase in pH reduced the monetite phase and enhanced Ca/P ratio from 1.7 to 1.83. Additionally, an increment in sintering temperature increased the crystallite size from 20 to 56 nm. The SEM analysis revealed the formation of semi-spherical and flake-like HAp structures with preferential flake morphology. An increase in pH and sintering temperature resulted in the growth and coalescence of crystals resulting in a porous capsular morphology. The FTIR analysis confirmed the reduction of carbonate stretching modes with an increase in pH and H-O-H antisymmetric stretching mode is eliminated for powders sintered at 900°C confirming the formation of stable and porous HAp powders.