RESUMO
Invisible orthodontic aligners are having a great impact on tooth movement in an aesthetic and effective way. Different techniques, models, and clinical aspects have been studied for their proper use. However, the aim of this research has been to determine the effect of the shaping process on mechanical properties and their bacterial behavior. For this study, 40 original polyurethane plates and 40 identical models, obtained by hot forming the original plates, were used. The static tensile mechanical properties were studied with a Zwick testing machine using testing speeds of 5 mm/min at a temperature of 37 °C. The original plate and the aligner have been studied with a creep test by subjecting the samples to a constant tension of 30 N, and determining the elongation using a long-distance, high-resolution microscope at different time periods between 1 and 720 h. Studies of water absorption has been realized with artificial saliva for 5 h. Bacterial cultures of Streptococcus oralis and Actinomyces viscosus strains were grown on the original plates and on new and used models, to determine the proliferation of each bacterium through metabolic activity, colony-forming units, and LIVE/DEAD assays. The mechanical results showed an increase in the strength of the inserts with respect to the models obtained from 3.44 to 3.95 MPa in the elastic limit and a lower deformation capacity. It has been proven that the transition zone in the creep curves lasts longer in the original plate, producing the rapid increase in deformation at a shorter time (400 h) in the aligner. Therefore, the shaping process reduces the time of dental correction exerted by the aligner. The results of the bacterial culture assays show an increase in the number of bacterial colonies when the aligners have been used and when the polyurethane is conformed due to the internal energy of the model, with respect to the original polyurethane. It has been observed that between the original plate and the aligner there are no statistically significant differences in water absorption and therefore the forming process does not affect water absorption. A slight increase in water absorption can be observed, but after five hours of exposure, the increase is very small.
RESUMO
Titanium mini-implants are used as anchorage for orthodontic tooth movements. However, these implants present problems due to the infection of surrounding tissues. The aim of this work was to obtain a polyethylene glycol (PEG) layer by plasma in order to achieve a bacteriostatic surface. Titanium surfaces were activated by argon plasma and, after, by PEG plasma with different powers (100, 150 and 200 W) for 30 and 60 min. The roughness was determined by white light interferometer microscopy and the wettability was determined by the contact angle technique. Surface chemical compositions were characterized by X-ray photoelectron spectroscopy (XPS) and cytocompatibility and cell adhesion studies were performed with fibroblast (hFFs) and osteoblast (SAOS-2) cells. Bacterial cultures with Spectrococcus Sanguinis and Lactobacillus Salivarius were performed, and bacterial colonization was determined. The results showed that plasma treatments do not affect the roughness. Plasma makes the surfaces more hydrophilic by decreasing the contact angles from 64.2° for titanium to 5.2° for argon-activated titanium, with values ranging from 12° to 25° for the different PEG treatments. The plasma has two effects: the cleaning of the surface and the formation of the PEG layer. The biocompatibility results were, for all cases, higher than 80%. The polymerization treatment with PEG reduced the adhesion of hFFs from 7000 to 6000 and, for SAOS-2, from 14,000 to 6500, for pure titanium and those treated with PEG, respectively. Bacterial adhesion was also reduced from 600 to 300 CFU/mm2 for Spetrococcuns Sanguinis and from 10,000 to 900 CFU/mm2 for Lactobacillus Salivarius. The best bacteriostatic treatment corresponded to PEG at 100 W and 30 s. As a consequence, the PEG coating would significantly prevent the formation of bacterial biofilm on the surface of titanium mini-implants.