Manipulation of individual graphene sheets/films into specific architectures at macroscopic scales is crucially important for practical uses of graphene. We present herein a versatile and robust method based on annealing of solid carbon precursors on nickel templates and thermo-assisted removal of poly(methyl methacrylate) under low vacuum of â¼0.6 Pa for fabrication of macroscopic, freestanding, and tubular graphene (TG) architectures. Specifically, the TG architectures can be obtained as individual and woven tubes with a diameter of â¼50 µm, a wall thickness in the range of 2.1-2.9 nm, a density of â¼1.53 mg·cm(-3), a thermal stability up to 600 °C in air, an electrical conductivity of â¼1.48 × 10(6) S·m(-1), and field emission current densities on the order of 10(4) A·cm(-2) at low applied electrical fields of 0.6-0.7 V·µm(-1). These properties show great promise for applications in flexible and lightweight electronics, electron guns, or X-ray tube sources.
RESUMO
We report a versatile method based on low vacuum annealing of cellulose acetate on nickel (Ni) surface for rapid fabrication of graphene and carbon nanotube (CNT)-graphene hybrid films with tunable properties. Uniform films mainly composed of tri-layer graphene can be achieved via a surface precipitation of dissociated carbon at 800 °C for 30 seconds under vacuum conditions of â¼0.6 Pa. The surface precipitation process is further found to be efficient for joining the precipitated graphene with pre-coated CNTs on the Ni surface, consequently, generating the hybrid films. As expected, the hybrid films exhibit substantial opto-electrical and field electron emission properties superior to their individual counterparts. The finding suggests a promising route to hybridize the graphene with diverse nanomaterials for constructing novel hybrid materials with improved performances.