Attenuating the Polysulfide Shuttle Mechanism by Separator Coating.

Lithium-sulfur batteries have a high energy density but lack cycle stability to reach market maturity. This is mainly due to the polysulfide shuttle mechanism, i. e., the leaching of active material from the cathode into the electrolyte and subsequent side reactions. We demonstrate how to attenuate the polysulfide shuttle by magnetron sputtering molybdenum oxysulfide, manganese oxide, and chromium oxide onto microporous polypropylene separators. The morphology of the amorphous coatings was analyzed by SEM and XRD. Electrochemical cyclization quantified how these coatings improved Coulombic efficiency and cycle stability. These tests were conducted in half cells. We compare the different performances of the different coatings with the known chemical and adsorption properties of the respective coating materials.

AFM as an analysis tool for high-capacity sulfur cathodes for Li-S batteries.

In this work, material-sensitive atomic force microscopy (AFM) techniques were used to analyse the cathodes of lithium-sulfur batteries. A comparison of their nanoscale electrical, electrochemical, and morphological properties was performed with samples prepared by either suspension-spraying or doctor-blade coating with different binders. Morphological studies of the cathodes before and after the electrochemical tests were performed by using AFM and scanning electron microscopy (SEM). The cathodes that contained polyvinylidene fluoride (PVDF) and were prepared by spray-coating exhibited a superior stability of the morphology and the electric network associated with the capacity and cycling stability of these batteries. A reduction of the conductive area determined by conductive AFM was found to correlate to the battery capacity loss for all cathodes. X-ray diffraction (XRD) measurements of Li2S exposed to ambient air showed that insulating Li2S hydrolyses to insulating LiOH. This validates the significance of electrical ex-situ AFM analysis after cycling. Conductive tapping mode AFM indicated the existence of large carbon-coated sulfur particles. Based on the analytical findings, the first results of an optimized cathode showed a much improved discharge capacity of 800 mA·g(sulfur)(-1) after 43 cycles.

In situ recording of particle network formation in liquids by ion conductivity measurements.

The formation of fractal silica networks from a colloidal initial state was followed in situ by ion conductivity measurements. The underlying effect is a high interfacial lithium ion conductivity arising when silica particles are brought into contact with Li salt-containing liquid electrolytes. The experimental results were modeled using Monte Carlo simulations and tested using confocal fluorescence laser microscopy and ζ-potential measurements.