Control of H-Related Defects in γ-MnO2 in a Hydrothermal Synthesis.

Manganese dioxide is a good candidate for effective energy storage and conversion as it possesses rich electrochemistry. The compound also shows a wide polymorphism. The γ-variety, an intergrowth of ß- and R-MnO2, has been extensively studied in several types of batteries (e.g., Zn/MnO2, Li-ion) and is a common electrode material for commercial batteries. It is well known that the insertion of protons thermodynamically stabilizes γ-MnO2 with respect to ß-MnO2. Protons can enter the structure either by forming groups of 4 hydroxyls around a Mn4+ vacancy, called a Ruetschi defect, or by forming a hydroxyl group near a Mn3+ ion, called a Coleman defect. These defects differently affect the electrochemistry of manganese oxide, and tailoring their amount in the structure can be used to tune the material properties. Previous studies have addressed the proton insertion process, but the role of the synthesis pathway on the amount of defects created is not well understood. We here investigate how the parameters in a hydrothermal synthesis of γ-MnO2 nanoparticles influence the amount and type of H-related defects. Structural investigations are carried out using Pair Distribution Function analysis, X-ray absorption spectroscopy, thermogravimetric analysis, and inelastic neutron scattering. We demonstrate the possibility to control the amount and type of defects introduced during the synthesis. While the amount of Ruetschi defects increases with synthesis temperature, it decreases with extended synthesis time, along with the amount of Coleman defects. Moreover, we discuss the arrangement of the defects in the γ-MnO2 nanoparticles.

Sub-second pair distribution function using a broad bandwidth monochromator.

Here the use of a broad energy bandwidth monochromator, i.e. a pair of B4C/W multilayer mirrors (MLMs), is demonstrated for X-ray total scattering (TS) measurements and pair distribution function (PDF) analysis. Data are collected both on powder samples and from metal oxo clusters in aqueous solution at various concentrations. A comparison between the MLM PDFs and those obtained using a standard Si(111) double-crystal monochromator shows that the measurements yield MLM PDFs of high quality which are suitable for structure refinement. Moreover, the effects of time resolution and concentration on the quality of the resulting PDFs of the metal oxo clusters are investigated. PDFs of heptamolybdate clusters and tungsten α-Keggin clusters from X-ray TS data were obtained with a time resolution down to 3 ms and still showed a similar level of Fourier ripples to PDFs obtained from 1 s measurements. This type of measurement could thus open up faster time-resolved TS and PDF studies.

Surfactant-Free Colloidal Syntheses of Gold-Based Nanomaterials in Alkaline Water and Mono-alcohol Mixtures.

Gold nanoparticles (Au NPs) and gold-based nanomaterials combine unique properties relevant for medicine, imaging, optics, sensing, catalysis, and energy conversion. While the Turkevich-Frens and Brust-Schiffrin methods remain the state-of-the-art colloidal syntheses of Au NPs, there is a need for more sustainable and tractable synthetic strategies leading to new model systems. In particular, stabilizers are almost systematically used in colloidal syntheses, but they can be detrimental for fundamental and applied studies. Here, a surfactant-free synthesis of size-controlled colloidal Au NPs stable for months is achieved by the simple reduction of HAuCl4 at room temperature in alkaline solutions of low-viscosity mono-alcohols such as ethanol or methanol and water, without the need for any other additives. Palladium (Pd) and bimetallic Au x Pd y NPs, nanocomposites and multimetallic samples, are also obtained and are readily active (electro)catalysts. The multiple benefits over the state-of-the-art syntheses that this simple synthesis bears for fundamental and applied research are highlighted.

Polymorphism and solid solutions of trimethylammonium monocarboranes.

Metal closo-boranes have recently received significant attention as solid-state electrolytes due to their high thermal and electrochemical stability, and the weak interaction between the cat- and anion, facilitating fast ionic conductivity. Here we report a synthesis method for obtaining a novel mixed closo-carborane compound, [NH(CH3)3][(CB8H9)0.26(CB9H10)0.66(CB11H12)0.08]. The crystal structures are investigated for [NH(CH3)3][CB9H10] and [NH(CH3)3][(CB8H9)0.26(CB9H10)0.66(CB11H12)0.08], revealing that the latter forms a solid solution isostructural to [NH(CH3)3][CB9H10]. The compounds exhibit polymorphism as a function of temperature, and we report the discovery of four polymorphs of [NH(CH3)3][CB9H10] and four isostructural solid solution [NH(CH3)3][(CB8H9)0.26(CB9H10)0.66(CB11H12)0.08], along with a high-temperature decomposition intermediate of the latter. The α-polymorph is an ordered structure, with increasing amounts of disorder for the ß- and γ-polymorphs, while the high temperature δ- and ε-polymorphs at T > 476 K are fully disordered on both the cation and anion site. These new compounds may be used as precursors for new types of solid-state ionic conductors.