InGaAs is a potential candidate for Si replacement in upcoming advanced technological nodes because of its excellent electron transport properties and relatively low interface defect density in dielectric gate stacks. Therefore, integrating InGaAs devices with the established Si platforms is highly important. Using template-assisted selective epitaxy (TASE), InGaAs nanowires can be monolithically integrated with high crystal quality, although the mechanisms of group III incorporation in this ternary material have not been thoroughly investigated. Here we present a detailed study of the compositional variations of InGaAs nanostructures epitaxially grown on Si(111) and Silicon-on-insulator substrates by TASE. We present a combination of XRD data and detailed EELS maps and find that the final Ga/In chemical composition depends strongly on both growth parameters and the growth facet type, leading to complex compositional sub-structures throughout the crystals. We can further conclude that the composition is governed by the facet-dependent chemical reaction rates at low temperature and low V/III ratio, while at higher temperature and V/III ratio, the incorporation is transport limited. In this case we see indications that the transport is a competition between Knudsen flow and surface diffusion.
RESUMO
Tunneling field-effect transistors (TunnelFET), a leading steep-slope transistor candidate, is still plagued by defect response, and there is a large discrepancy between measured and simulated device performance. In this work, highly scaled InAs/InxGa1-xAsySb1-y/GaSb vertical nanowire TunnelFET with ability to operate well below 60 mV/decade at technically relevant currents are fabricated and characterized. The structure, composition, and strain is characterized using transmission electron microscopy with emphasis on the heterojunction. Using Technology Computer Aided Design (TCAD) simulations and Random Telegraph Signal (RTS) noise measurements, effects of different type of defects are studied. The study reveals that the bulk defects have the largest impact on the performance of these devices, although for these highly scaled devices interaction with even few oxide defects can have large impact on the performance. Understanding the contribution by individual defects, as outlined in this letter, is essential to verify the fundamental physics of device operation, and thus imperative for taking the III-V TunnelFETs to the next level.