RESUMO
INTRODUCTION: To evaluate the push-out bond strength (POBS) of AH Plus sealer to root dentin and the adhesive interface quality after calcium hydroxide (Ca(OH)2) intracanal dressing removal with different final irrigation protocols. METHOD: After root canal instrumentation and irrigation, 40 root canals were filled with Ca(OH)2 and sealed. After 14 days, the specimens were randomly distributed according to the irrigation protocols for Ca(OH)2 removal (n = 10): GH2O (control) - distilled water; GNaOCl - 1% NaOCl; GEDTA - 17% EDTA; GEDTA + NaOCl - 17% EDTA + 1% NaOCl. The root canals were filled with AH Plus sealer and gutta-percha. After 7 days, the roots were sectioned into dentin slices and submitted to POBS test and analysis of the adhesive interface under scanning electron microscope. The POBS data were statistically evaluated (analysis of variance and Tukey test). The Kruskal-Wallis and Mann-Whitney tests were used to analyze the adhesive interface (α = 0.05). RESULTS: GH2O, GNaOCl, and GEDTA + NaOCl had similar POBS values, with higher values on the apical third, in comparison with other thirds (P < .05). A homogeneous and free-of-gaps adhesive interface was observed for GH2O, GNaOCl, and GEDTA + NaOCl, with difference between GH2O and GEDTA (P < .05). GH2O and GEDTA + NaOCl presented higher sealer tags formation (P < .05). CONCLUSION: The final rinse with EDTA for Ca(OH)2 dressing removal had a negative effect on the POBS of the filling material to root dentin. The use of EDTA followed by NaOCl had results similar to the distilled water, providing uniform and free-of-gaps adhesive interface, and a higher number of sealer tags.
Assuntos
Hidróxido de Cálcio , Colagem Dentária , Dentina , Resinas Epóxi , Materiais Restauradores do Canal Radicular , Irrigantes do Canal Radicular , Irrigação Terapêutica , Hidróxido de Cálcio/química , Humanos , Dentina/efeitos dos fármacos , Materiais Restauradores do Canal Radicular/química , Resinas Epóxi/química , Colagem Dentária/métodos , Irrigação Terapêutica/métodos , Cavidade Pulpar/efeitos dos fármacos , Microscopia Eletrônica de Varredura , Hipoclorito de Sódio/química , Ácido Edético , Preparo de Canal Radicular/métodos , Análise do Estresse Dentário , Teste de MateriaisRESUMO
To evaluate the effect of ultrasonic activation of the endodontic sealer on its intratubular penetration and bond strength to irradiated root dentin. Forty human teeth were distributed into 4 groups (n = 10), according to the radiation therapy (RT) exposure-70 Gy-and ultrasonic activation (UA) of the endodontic sealer: RT/UA-irradiated teeth and sealer UA; RT/no-UA-irradiated teeth and no sealer UA; no-RT/UA-non-irradiated teeth and sealer UA and no-RT/no-UA-non-irradiated teeth and no sealer UA. Push-out bond strength test was performed in a Universal Testing Machine. Failure modes and adhesive interface were analyzed under Scanning Electron Microscopy. The data were statistically compared (two-way-ANOVA and posthoc Games-Howell test; Fisher's exact test - α = 5%). The different experimental conditions (radiation and UA) and the root third had a significant effect on push-out bond strength, and the interaction of these factors was significant (p < 0.05). UA of the sealer significantly increased its bond strength to both irradiated and non-irradiated dentin (p < 0.05). The irradiated groups mostly presented adhesive-type failure of the sealer (p < 0.01). Regardless of the irradiation, the ultrasonically activated groups showed a more homogeneous adhesive interface, with the presence of sealer tags in greater density and depth. Ultrasonic activation enhanced the intratubular penetration and the bond strength of the endodontic sealer to irradiated dentin. The impact of ultrasonic activation of the endodontic sealer on teeth undergoing radiotherapy is a gap in the scientific literature that needs to be bridged.
Assuntos
Colagem Dentária , Dentina , Teste de Materiais , Microscopia Eletrônica de Varredura , Materiais Restauradores do Canal Radicular , Humanos , Materiais Restauradores do Canal Radicular/química , Colagem Dentária/métodos , Dentina/efeitos da radiação , Técnicas In Vitro , Análise do Estresse Dentário , Propriedades de Superfície , Ultrassom , Raiz Dentária/efeitos da radiaçãoRESUMO
Abstract Few long-term studies assess the discoloration induced by hydraulic calcium silicate-based cement on dental structures. In addition, as far as we know, no long-term study has assessed the discoloration induced by these cement on composite resin. Objective This in vitro study aimed to assess, during a period of two years, the discoloration potential of different hydraulic calcium silicate-based cements (hCSCs) on the enamel/dentin structure and composite resin restoration. Methodology A total of 40 enamel/dentin discs were obtained from bovine incisors, and 40 composite resin discs (10 mm in diameter × 2 mm thick) were fabricated. A 0.8 mm-deep cavity was made in the center of each disc and filled with the following hCSCs (n=10): Original MTA (Angelus); MTA Repair HP (Angelus); NeoMTA Plus (Avalon); and Biodentine (Septodont). An initial color measurement was performed (T0 - baseline). After 7, 15, 30, 45, 90, 300 days, and two years, new color measurements were performed to determine the color (ΔE00), lightness (ΔL'), chroma (ΔC'), hue differences (ΔH'), and whiteness index (WID). Results For enamel/dentin, the ΔE00 was significant among groups and periods (p<0.05). NeoMTA Plus had the greatest ΔE00. The NeoMTA Plus group had the greatest ΔE00 after two years for composite resin. Significant reduction in lightness was observed for all groups after two years (p<0.05). The most significant WID values were observed after 30 days for Biodentine (enamel/dentin) and MTA Repair HP groups (composite resin) (p<0.05). Conclusions The hCSCs changed the colorimetric behavior of both substrates, leading to greater darkening over time. The Bi2O3 in the Original MTA seems relevant in the short periods of color change assessment.