RESUMO
This article presents new research on producing lignin nanoparticles (LNPs) using the antisolvent nanoprecipitation method. Acetone (90%) served as the lignin solvent and water (100%) as the antisolvent, using five types of lignins from various sources. Comprehensive characterization techniques, including NMR, GPC, FTIR, TEM, and DLS, were employed to assess both lignin and LNP properties. The antioxidant activity of the LNPs was evaluated as well. The results demonstrated the successful formation of spherical nanoparticles below 100 nm with initial lignin concentrations of 1 and 2%w/v. The study highlighted the crucial role of lignin purity in LNP formation and colloidal stability, noting that residual carbohydrates adversely affect efficiency. This method offers a straightforward, environmentally friendly approach using cost-effective solvents, applicable to diverse lignin sources. The innovation of this study lies in its demonstration of a cost-effective and eco-friendly method to produce stable, nanometric-sized spherical LNPs. These LNPs have significant potential as reinforcement materials due to their reinforcing capability, hydrophilicity, and UV absorption. This work underscores the importance of starting material purity for optimizing the process and achieving the desired nanometric dimensions, marking a pioneering advancement in lignin-based nanomaterials.
RESUMO
The tannin extract of Cissus dinklagei was used in the preparation of a 3 % paraformaldehyde resin for the manufacture of particleboard. This tannin is of the procyanidin type associated with furan residues. The modulus of elasticity of the resin obtained after the thermomechanical analysis is 3825 MPa. The TGA performed on the panels obtained shows three degradation zones with a thermal stability zone between 74 and 210 °C. These panels have good thermomechanical properties. The values of the best density, internal bond, modulus of elasticity in flexion (MOE) and resistance to flexion (MOR) are respectively 658 kg/m3; 0.52 MPa; 2035.4 MPa; 16.3 MPa. These results classify this panel for generalinterior construction and furniture uses according to the NF EN 312 standard.
RESUMO
The growing interest in environmentally friendly materials is leading to a re-evaluation of natural fibers for industrial applications in order to meet sustainability and low-cost objectives, especially for thermal insulation of buildings. This paper deals with the chemical and physical characterization of fibers extracted from seagrass (Posidonia oceanica) and alfa grass (Stipa tenacissima) for a possible substitution of synthetic materials for thermal insulation. Hemp (Cannabis sativa), a fiber broadly used, was also studied for comparison. The parameters characterized include porosity, thermal degradation, elemental composition, skeletal and particle density of the fibers as well as investigation of the thermal conductivity of fiber-based panels. Several technologies were involved in investigating these parameters, including mercury intrusion, thermogravimetric analysis, fluorescence spectroscopy, and fluid pycnometry. The fibers showed a degradation temperature between 316 and 340 °C for Posidonia, between 292 and 326 °C for alfa, and between 300 and 336 °C for hemp fibers. A high porosity allied with a reduced pore size was revealed for Posidonia (77%, 0.54 µm) compared to hemp (75%, 0.61 µm) and alfa (57%, 2.1 µm) raw fibers, leading to lower thermal conductivity values for the nonwoven panels based on Posidonia (0.0356-0.0392 W/m.K) compared to alfa (0.0365-0.0397 W/m.K) and hemp (0.0387-0.0427 W/m.K). Bulk density, operating temperature, and humidity conditions have been shown to be determining factors for the thermal performance of the panels.