To Analyse the Erosive Potential of Commercially Available Drinks on Dental Enamel and Various Tooth Coloured Restorative Materials - An In-vitro Study.

INTRODUCTION: With the enormous change in life style pattern of a common man through the past few decades, there has been proportional variation in the amount and frequency of consumption of drinks. An increased consumption of these drinks will concurrently increase enamel surface roughness by demineralization, resulting in hypersensitivity and elevated caries risk. AIM: The present study was designed to evaluate the erosive potential of commercially available drinks on tooth enamel and various tooth coloured restorative materials. MATERIALS AND METHODS: Extracted human teeth were taken and divided into four groups i.e. tooth enamel, glass ionomer cement, composite and compomer. Four commercially available drinks were chosen these were Coca -Cola, Nimbooz, Frooti and Yakult. The pH of each drink was measured. Each group was immersed in various experimental drinks for a period of 14 days. The erosive potential of each drink was measured by calculating the change in average surface roughness of these groups after the immersion protocol in various drinks. The data analysis was done by One Way Anova, Post-Hoc Bonferroni, and paired t -test. RESULTS: Group II-GIC showed highest values for mean of change in average surface roughness and the values were statistically significant (p<0.001) with tooth enamel, composite and compomer (p=0.002). Coca-cola showed the highest erosive potential and Yakult showed the lowest, there was no statistical significant difference between the results shown by Yakult and Frooti. CONCLUSION: Characteristics which may promote erosion of enamel and tooth coloured restorative materials were surface texture of the material and pH of the drinks.

Prevalence, causes, and correlates of traumatic dental injuries among seven-to-twelve-year-old school children in Dera Bassi.

AIM: The paper aims to present a study conducted in Dera Bassi, Mohali, India. The purpose of the study was to ascertain the prevalence of traumatic dental injuries (TDI) in children of age group 7-12 years in private schools in Gulabgarh village. MATERIAL #ENTITYSTARTX00026; METHOD: Age & sex distribution, etiological factors, risk factors and cause of injury were the parameters taken into consideration. The data collected was processed and analyzed using the SPSS statistical software program. RESULTS: The overall prevalence of dental trauma was 14.5%, amongst the 880 subjects examined, out of which, 63.2% males and 36.4% females were found to be affected. The maxillary central incisor was found to be most commonly affected tooth (43.8%). The most common cause of injury reported was fall during playing (37.5%). CONCLUSION: Enamel fracture was most prevalent (50%). No risk factor was significantly higher than others; however children with Angle's class II div 1 malocclusion exhibited greater risk factor for traumatic injuries.

In vitro evaluation of the effect of post system and length on the fracture resistance of endodontically treated human anterior teeth.

OBJECTIVES: The aim of this study was to evaluate the effect of post system and length on the fracture resistance of endodontically treated human anterior teeth. MATERIAL AND METHOD: Seventy-five extracted human incisors were endodontically treated, out of which 60 were decoronated 2 mm above the cementoenamel junction and divided into two experimental groups based on the type of post system to be used: glass fiber post (GFP) and Ribbond fiber post groups (RFP). Endodontically treated human anterior teeth in which no post was placed served as control group. Each group was divided into two subgroups according to the length of post space: 5 and 10 mm and all the samples were restored with metal crowns. The fracture resistance was measured by applying loads at an angle of 130° to the long axis of teeth in an Instron universal testing machine. RESULTS: The results revealed that GFP group at 10-mm post space length showed the significantly highest fracture resistance (740.2133 N) among all groups and subgroups. Decrease in post length resulted in the decrease in fracture resistance in GFP group (425.1867 N), whereas in group RFP 5-mm subgroup (299.6200 N) showed significantly higher fracture resistance than 10-mm subgroup (216.9300 N) but lesser than the control (437.8733 N) in both the subgroups. CONCLUSION: Glass fiber posts efficiently increase the fracture resistance of an endodontically treated tooth but the determination of optimal post length is also essential. CLINICAL RELEVANCE: The present investigation highlights the significance of using glass fiber posts in the restoration of endodontically treated teeth. Endodontically treated teeth restored with glass fiber posts showed increased fracture strength and favorable mode of fracture, and are therefore highly recommended to achieve better clinical outcomes.