Colloidal polymers from dipolar assembly of cobalt-tipped CdSe@CdS nanorods.

The synthesis of a modular colloidal polymer system based on the dipolar assembly of CdSe@CdS nanorods functionalized with a single cobalt nanoparticle "tip" (CoNP-tip) is reported. These heterostructured nanorods spontaneously self-assembled via magnetic dipolar associations of the cobalt domains. In these assemblies, CdSe@CdS nanorods were carried as densely grafted side chain groups along the dipolar NP chain to form bottlebrush-type colloidal polymers. Nanorod side chains strongly affected the conformation of individual colloidal polymer bottlebrush chains and the morphology of thin films. Dipolar CoNP-tipped nanorods were then used as "colloidal monomers" to form mesoscopic assemblies reminiscent of traditional copolymers possessing segmented and statistical compositions. Investigation of the phase behavior of colloidal polymer blends revealed the formation of mesoscopic phase separated morphologies from segmented colloidal copolymers. These studies demonstrated the ability to control colloidal polymer composition and morphology in a manner observed for classical polymer systems by synthetic control of heterostructured nanorod structure and harnessing interparticle dipolar associations.

Directing the deposition of ferromagnetic cobalt onto Pt-tipped CdSe@CdS nanorods: synthetic and mechanistic insights.

A methodology providing access to dumbbell-tipped, metal-semiconductor and metal oxide-semiconductor heterostructured nanorods has been developed. The synthesis and characterization of CdSe@CdS nanorods incorporating ferromagnetic cobalt nanoinclusions at both nanorod termini (i.e., dumbbell morphology) are presented. The key step in the synthesis of these heterostructured nanorods was the decoration of CdSe@CdS nanorods with platinum nanoparticle tips, which promoted the deposition of metallic CoNPs onto Pt-tipped CdSe@CdS nanorods. Cobalt nanoparticle tips were then selectively oxidized to afford CdSe@CdS nanorods with cobalt oxide domains at both termini. In the case of longer cobalt-tipped nanorods, heterostructured nanorods were observed to self-organize into complex dipolar assemblies, which formed as a consequence of magnetic associations of terminal CoNP tips. Colloidal polymerization of these cobalt-tipped nanorods afforded fused nanorod assemblies from the oxidation of cobalt nanoparticle tips at the ends of nanorods via the nanoscale Kirkendall effect. Wurtzite CdS nanorods survived both the deposition of metallic CoNP tips and conversion into cobalt oxide phases, as confirmed by both XRD and HRTEM analysis. A series of CdSe@CdS nanorods of four different lengths ranging from 40 to 174 nm and comparable diameters (6-7 nm) were prepared and modified with both cobalt and cobalt oxide tips. The total synthesis of these heterostructured nanorods required five steps from commercially available reagents. Key synthetic considerations are discussed, with particular emphasis on reporting isolated yields of all intermediates and products from scale up of intermediate precursors.

Magnetic self-assembly of gold nanoparticle chains using dipolar core-shell colloids.

The preparation of gold nanoparticle (AuNP) assemblies was conducted by the synthesis and dipolar assembly of ferromagnetic core-shell nanoparticles composed of AuNP cores and cobalt NP shells. Dissolution of metallic Co phases with mineral acids afforded self-assembled AuNP chains and bracelets.

Synthesis and colloidal polymerization of ferromagnetic Au-Co nanoparticles into Au-Co3O4 nanowires.

The preparation of cobalt oxide nanowires with gold nanoparticle (AuNP) inclusions (Au-Co(3)O(4) nanowires) via colloidal polymerization of dipolar core-shell NPs is reported. Polystyrene-coated ferromagnetic NPs composed of a dipolar metallic cobalt shell and a gold NP core (PS-AuCoNPs) were synthesized by thermolysis of octacarbonyldicobalt [Co(2)(CO)(8)] in the presence of AuNP seeds and polymeric ligands. The colloidal polymerization process of these dipolar PS-AuCoNPs comprises dipolar nanoparticle assembly and solution oxidation of preorganized NPs to form interconnected cobalt oxide nanowires via the nanoscale Kirkendall effect, with AuNP inclusions in every repeating unit of the one-dimensional mesostructure. Calcination of the polymer-coated nanowires afforded polycrystalline Au-Co(3)O(4) nanowires that were determined to be electroactive. Nanocomposite materials were characterized by transmission electron microscopy, field-emission scanning electron microscopy, X-ray diffraction, vibrating sample magnetometry, and cyclic voltammetry. We demonstrate that the optical and electrochemical properties of Au-Co(3)O(4) nanowires are significantly enhanced in comparison with hollow Co(3)O(4) nanowires prepared via colloidal polymerization.

Colloidal polymerization of polymer-coated ferromagnetic nanoparticles into cobalt oxide nanowires.

The preparation of polystyrene-coated cobalt oxide nanowires is reported via the colloidal polymerization of polymer-coated ferromagnetic cobalt nanoparticles (PS-CoNPs). Using a combination of dipolar nanoparticle assembly and a solution oxidation of preorganized metallic colloids, interconnected nanoparticles of cobalt oxide spanning micrometers in length were prepared. The colloidal polymerization of PS-CoNPs into cobalt oxide (CoO and Co(3)O(4)) nanowires was achieved by bubbling O(2) into PS-CoNP dispersions in 1,2-dichlorobenzene at 175 degrees C. Calcination of thin films of PS-coated cobalt oxide nanowires afforded Co(3)O(4) metal oxide materials. Transmission electron microscopy (TEM) revealed the formation of interconnected nanoparticles of cobalt oxide with hollow inclusions, arising from a combination of dipolar assembly of PS-CoNPs and the nanoscale Kirkendall effect in the oxidation reaction. Using a wide range of spectroscopic and electrochemical characterization techniques, we demonstrate that cobalt oxide nanowires prepared via this novel methodology were electroactive with potential applications as nanostructured electrodes for energy storage.