Effects of Interfacial Electron Transport on Field Electron Emission from Carbon Nanotube Paste Emitters.

Field electron emission from carbon nanotubes (CNT) is preceded by the transport of electrons from the cathode metal to emission sites. Specifically, a supporting layer indispensable for adhesion of CNT paste emitters onto the cathode metal would impose a potential barrier, depending on its work function and interfacial electron transport behaviors. In this paper, we investigated the supporting layer of silicon carbide and nickel nanoparticles reacted onto a Kovar alloy (Fe-Ni-Co) cathode substrate, which has been adopted for reliable CNT paste emitters. The X-ray diffraction, X-ray photoelectron spectroscopy, ultraviolet photoelectron spectroscopy, and electrical conductivity measurements showed that the reaction of silicon carbide and nickel nanoparticles on the Kovar metal strongly depends upon the post-vacuum-annealing conditions and can be classified into two procedures of a diffusion-induced reaction (DIR) and a diffusion-limited reaction (DLR). The prolonged annealing at 750 °C for 5 h before the main annealing of the CNT paste emitters at 800 °C for 5 min led to the DIR that has enhanced the Ni silicide phase and a lower potential barrier for the interfacial electron transport, resulting in increased and weakly temperature-dependent field electron emission from the CNT paste emitters. On the other hand, the DLR with only the main anneal of the CNT paste emitters at 800 °C for 5 min gave rise to a higher potential barrier for the electron transport and so lower and strongly temperature-dependent field electron emission. From the results of the interfacial electron transport for the DIR and DLR mechanisms in the CNT paste emitters, we concluded that the ambient temperature dependency of field electron emission from CNT tips in the moderate range of up to 400 °C, still controversial, is mainly attributed to the supporting layer of the CNT emitter rather than its intrinsic electron emission.

Enhanced interfacial reaction of silicon carbide fillers onto the metal substrate in carbon nanotube paste for reliable field electron emitters.

Adhesion of carbon nanotube (CNT) onto a cathode substrate is very crucial for field electron emitters that are operating under high electric fields. As a supporting precursor of CNT field emitters, we adopted silicon carbide (SiC) nano-particle fillers with Ni particles and then enhanced interfacial reactions onto Kovar-alloy substrates through the optimized wet pulverization process of SiC aggregates for reliable field electron emitters. As-purchased SiC aggregates were efficiently pulverized from 20 to less than 1 micro-meter in a median value (D50). CNT pastes for field emitters were distinctively formulated by a mixing process of the pulverized SiC aggregates and pre-dispersed CNTs. X-ray photoelectron spectroscopy studies showed that the optimally pulverized SiC-CNT paste-emitter had a stronger Si 2p3/2 signal in the Ni2Si phase than the as-purchased one. The Si 2p3/2 signal would represent interfacial reaction of the SiC nano-particle onto Ni from the CNT paste and the Kovar substrate, forming the supporting layer for CNT emitters. The optimal paste-emitter even in a vacuum-sealed tube exhibited a highly reliable field emission current with a high current density of 100 mA cm-2 for over 50 h along with good reproducibility. The enhanced interfacial reaction of SiC filler onto the metal substrates could lead to highly reliable field electron emitters for vacuum electronic devices.

Field emission behavior of boron nitride nanotubes.

The field emission properties of boron nitride nanotube (BNNT) field emitters according to vacuum pressure were demonstrated. During the short-term emission operation, the field emission behaviors were almost similar, regardless of the vacuum pressure, even though the turn-on electric field of the BNNT field emitter was slightly increased as the vacuum pressure increased. On the other hand, during the long-term emission operation, both the degradation and fluctuations of the emission current of the BNNT field emitters were dramatically increased as the vacuum pressure increased. The degradation of field emission properties of the BNNT emitters according to vacuum pressure is mainly attributed to the ion bombardment effect, rather than the oxidation effect. The field emission behavior under Ar ambient also strongly demonstrates that the degradation and the fluctuation of the emission current are largely dependent on the ion bombardment effect.

High-performance field emission of carbon nanotube paste emitters fabricated using graphite nanopowder filler.

Carbon nanotube (CNT) paste emitters were fabricated using graphite nanopowder filler. The CNT paste emitters consist of CNTs as the emitting material, graphite nanopowder as the filler and a graphite rod as the cathode. Rather than metal or inorganic materials, graphite nanopowder was adapted as a filler material to make the CNT paste emitters. After fabricating the emitters, sandpaper treatment was applied to increase the density of emission sites. The CNT paste emitters showed a high field emission performance, for example a high emission current of 8.5 mA from a cylindrical emitter with a diameter of 0.7 mm (corresponding to a current density of 2.2 A cm-2) and an extremely stable emission current at 1 mA (260 mA cm-2 for 20 h). Interestingly, after a number of electrical arcing events, the emitters still showed a high emission current of 5-8 mA (higher than 1 A cm-2). In addition to the sound electrical and thermal properties of the graphite filler, effective mechanical adhesion of the CNTs onto the graphite cathode induced by the use of the graphite nanopowder filler contributed the excellent field emission properties of the CNT paste emitters.

High-Performance Field-Emission Properties of Boron Nitride Nanotube Field Emitters.

Boron nitride nanotubes (BNNTs) have attracted considerable attention as a field emission material because of their high mechanical strength, high negative electron affinity, and high oxidation resistance. Nevertheless, the obtained field-emission properties of BNNTs have indicated poor emission performance, which is a very high turn-on electric field with a low emission current. We fabricated BNNT field emitters and investigated their field-emission properties. The field-emission properties of the BNNT field emitters were considerably enhanced compared to those of other BN nanomaterial-based field emitters. The turn-on and the threshold electric fields of the BNNT field emitter were 3.1 and 5.4 V/µm at the gap distance of 750 µm, respectively. Both the turn-on and the threshold electric fields of the BNNT field emitters were decreased by increasing the gap distance between the emitter tip and the anode electrode. Degradation of the emission current during field emission operation for 20 h showed no significant difference according to the gap distance. Emission current fluctuation of the BNNT field emitters showed that the smaller gap was more unstable than the larger gap. The enhanced emission properties are mainly attributed to the small diameter, high-quality, and straight structure of BNNTs as well as the stable network formation of the BNNT film with good mechanical and electrical contact between the BNNTs and the cathode electrode. The remarkable emission performance of the BNNT field emitters might have promising applications for various field-emission devices.

Highly reliable field electron emitters produced from reproducible damage-free carbon nanotube composite pastes with optimal inorganic fillers.

Highly reliable field electron emitters were developed using a formulation for reproducible damage-free carbon nanotube (CNT) composite pastes with optimal inorganic fillers and a ball-milling method. We carefully controlled the ball-milling sequence and time to avoid any damage to the CNTs, which incorporated fillers that were fully dispersed as paste constituents. The field electron emitters fabricated by printing the CNT pastes were found to exhibit almost perfect adhesion of the CNT emitters to the cathode, along with good uniformity and reproducibility. A high field enhancement factor of around 10,000 was achieved from the CNT field emitters developed. By selecting nano-sized metal alloys and oxides and using the same formulation sequence, we also developed reliable field emitters that could survive high-temperature post processing. These field emitters had high durability to post vacuum annealing at 950 °C, guaranteeing survival of the brazing process used in the sealing of field emission x-ray tubes. We evaluated the field emitters in a triode configuration in the harsh environment of a tiny vacuum-sealed vessel and observed very reliable operation for 30 h at a high current density of 350 mA cm(-2). The CNT pastes and related field emitters that were developed could be usefully applied in reliable field emission devices.

A vacuum-sealed compact x-ray tube based on focused carbon nanotube field-emission electrons.

We report on a fully vacuum-sealed compact x-ray tube based on focused carbon nanotube (CNT) field-emission electrons for various radiography applications. The specially designed two-step brazing process enabled us to accomplish a good vacuum level for the stable and reliable operation of the x-ray tube without any active vacuum pump. Also, the integrated focusing electrodes in the field-emission electron gun focused electron beams from the CNT emitters onto the anode target effectively, giving a small focal spot of around 0.3 mm with a large current of above 50 mA. The active-current control through the cathode electrode of the x-ray tube led a fast digital modulation of x-ray dose with a low voltage of below 5 V. The fabricated compact x-ray tube showed a stable and reliable operation, indicating good maintenance of a vacuum level of below 5 × 10(-6) Torr and the possibility of field-emission x-ray tubes in a stand-alone device without an active pumping system.