Unlocking the Potential of Lignocellulosic Biomass Dragon Fruit (Hylocereus polyrhizus) in Bioplastics, Biocomposites and Various Commercial Applications.

Dragon fruit, also called pitaya or pitahaya, is in the family Cactaceae. It is found in two genera: 'Selenicereus' and 'Hylocereus'. The substantial growth in demand intensifies dragon fruit processing operations, and waste materials such as peels and seeds are generated in more significant quantities. The transformation of waste materials into value-added components needs greater focus since managing food waste is an important environmental concern. Two well-known varieties of dragon fruit are pitaya (Stenocereus) and pitahaya (Hylocereus), which are different in their sour and sweet tastes. The flesh of the dragon fruit constitutes about two-thirds (~65%) of the fruit, and the peel is approximately one-third (~22%). Dragon fruit peel is believed to be rich in pectin and dietary fibre. In this regard, extracting pectin from dragon fruit peel can be an innovative technology that minimises waste disposal and adds value to the peel. Dragon fruit are currently used in several applications, such as bioplastics, natural dyes and cosmetics. Further research is recommended for diverging its development in various areas and maturing the innovation of its usage.

Thermal, flammability, and antimicrobial properties of arrowroot (Maranta arundinacea) fiber reinforced arrowroot starch biopolymer composites for food packaging applications.

Using the solution casting method, a novel biodegradable thermoplastic arrowroot (Maranta arundinacea) starch (TPAS) films containing arrowroot fiber (AF) at different concentrations (0, 2, 4, 6, 8, and 10 wt%) were developed and characterized in terms of thermal, antibacterial activity, water vapor permeability (WVP), biodegradability, and light transmittance properties. The TPAS/AF-10 biocomposite film revealed a higher degradation temperature (313.02 °C) than other biocomposite films, indicating better thermal stability. Furthermore, increasing AF concentration led to a significant (p < 0.05) reduction in the linear burning rate and WVP of the biocomposite films from 248.9 to 115.2 mm/min and 8.18 × 10-10 ×g. s-1.m-1. Pa-1 to 5.20 × 10-10 ×g. s-1.m-1. Pa-1, respectively. The addition of fibers in the surface structure had a significant impact on remarkable drop in opacity (91.1 to 74.1%). In addition, the incorporation of AF and control film showed an insignificant effect against three pathogenic bacteria, including Staphylococcus aureus (ATCC 43300), Escherichia coli (ATCC 25922), and Bacillus subtilis (B29). The soil burial findings demonstrated that the weight loss of TPAS/AF biocomposite films was significantly higher than TPAS film. Overall, the reinforcement of arrowroot fiber with TPAS film improved the properties of biocomposites for environmentally friendly food packaging applications.

Physical, Mechanical, and Morphological Performances of Arrowroot (Maranta arundinacea) Fiber Reinforced Arrowroot Starch Biopolymer Composites.

This research is driven by stringent environmental legislation requiring the consumption and use of environmentally friendly materials. In this context, this paper is concerned with the development and characterization of thermoplastic arrowroot starch (TPAS) based biocomposite films by incorporating arrowroot fiber (AF) (0-10%) into a glycerol plasticized matrix by using the solution casting method. Developed TPAS/AF composite films were investigated, such as physical, morphological (FESEM), tensile, and tear strength characteristics. The tensile and tear strengths of TPAS/AF composites were increased significantly from 4.77 to 15.22 MPa and 0.87 to 1.28 MPa, respectively, as compared to the control TPAS films, which were 2.42 MPa and 0.83 MPa, respectively, while elongation was significantly decreased from 25.57 to 6.21% compared to control TPAS film, which was 46.62%. The findings revealed that after the fiber was reinforced, the mechanical properties were enhanced, and the optimum filler content was 10%. Regardless of fiber loadings, the results of water absorption testing revealed that the composite films immersed in seawater and rainwater absorbed more water than distilled water. Overall, the results of this research focus on providing information on biopolymer composite film and revealing the great potential it has for the food packaging industry.

Effect of glycerol plasticizer loading on the physical, mechanical, thermal, and barrier properties of arrowroot (Maranta arundinacea) starch biopolymers.

This research was set out to explore the development of arrowroot starch (AS) films using glycerol (G) as plasticizer at the ratio of 15, 30, and 45% (w/w, starch basis) using solution casting technique. The developed films were analyzed in terms of physical, structural, mechanical, thermal, environmental, and barrier properties. The incorporation of glycerol to AS film-making solution reduced the brittleness and fragility of films. An increment in glycerol concentration caused an increment in film thickness, moisture content, and solubility in water, whereas density and water absorption were reduced. The tensile strength and modulus of G-plasticized AS films were reduced significantly from 9.34 to 1.95 MPa and 620.79 to 36.08 MPa, respectively, while elongation at break was enhanced from 2.41 to 57.33%. FTIR analysis revealed that intermolecular hydrogen bonding occurred between glycerol and AS in plasticized films compared to control films. The G-plasticized films showed higher thermal stability than control films. The cross-sectional micrographs revealed that the films containing 45% glycerol concentration had higher homogeneity than 15% and 30%. Water vapour permeability of plasticized films increased by an increase in glycerol concentrations. The findings of this research provide insights into the development of bio-degradable food packaging.