Microstructure and Chlorine Ion Corrosion Performance in Bronze Earring Relics.

Chlorine ions play an important role in the corrosion of bronzeware. This study employs techniques such as XRD, OM, SEM, EBSD, and electrochemical testing to analyze the microstructure, crystal structure, chemical composition, and corrosion performance of bronze earrings unearthed at the Xindianzi site in Inner Mongolia. The results indicate the presence of work-hardened structures, including twinning and equiaxed crystals, on the earrings' surface. With an increase in chloride ion concentration in NaCl solutions from 10-3 mol/L to 1 mol/L, the corrosion current density of the bronze earrings increased from 2.372 × 10-7 A/cm2 to 9.051 × 10-7 A/cm2, demonstrating that the alloy's corrosion rate escalates with chloride ion concentration. A 3-day immersion test in 0.5% NaCl solution showed the formation of a passivation layer of metal oxides on the earrings' surface. These findings underscore the significance of the impact chloride ions have on the corrosion of copper alloys, suggesting that activating the alloy's reactive responses can accelerate the corrosion process and provide essential insights into the corrosion mechanisms of bronze artifacts in chloride-containing environments.

The Corrosion Properties of Bronze Alloys in NaCl Solutions.

Chloride ions play an important role in the corrosion of bronze through their active reactivity to copper alloys. The corrosion behavior of bronze alloys in NaCl solution was investigated by using X-ray diffraction (XRD), a scanning electron microscope (SEM), and electrochemical tests, with a special emphasis on the corrosion resistance of the α and δ phases in Cu-20 wt%Sn bronze alloys. The experimental results show that the corrosion current density of Cu-20 wt%Sn bronze alloys increases from 1.1 × 10-7 A/cm2 to 2.7 × 10-6 A/cm2 with the increase in the chloride ion concentration from 10-3 mol/L to 1 mol/L. After a soaking duration of 30 days, the matrix corrosion depth reaches 50 µm. The α phase of the alloys is easily corroded in NaCl solution, while the δ phase with high Sn content has strong corrosion resistance. This study provides relevant data for the analysis and protection of ancient bronze alloys.

The Enhanced Red Emission and Improved Thermal Stability of CaAlSiN3:Eu2+ Phosphors by Using Nano-EuB6 as Raw Material.

Synthesizing phosphors with high performance is still a necessary work for phosphor-converted white light-emitting diodes (W-LEDs). In this paper, three series of CaAlSiN3:Eu2+ (denoted as CASN:Eu2+) phosphors using Eu2O3, EuN and EuB6 as raw materials respectively are fabricated by under the alloy precursor normal pressure nitridation synthesis condition. We demonstrate that CASN:Eu2+ using nano-EuB6 as raw material shows higher emission intensity than others, which is ascribed to the increment of Eu2+ ionic content entering into the crystal lattice. An improved thermal stability can also be obtained by using nano-EuB6 due to the structurally stable status, which is assigned to the partial substitution of Eu-O (Eu-N) bonds by more covalent Eu-B ones that leads to a higher structural rigidity. In addition, the W-LEDs lamp was fabricated to explore its possible application in W-LEDs based on blue LEDs. Our results indicate that using EuB6 as raw materials can provide an effective way of enhancing the red emission and improving the thermal stability of the CASN:Eu2+ red phosphor.