Effect of ethanol/TEOS ratios and amount of ammonia on the properties of copper-doped calcium silicate nanoceramics.

Calcium magnesium silicate glasses could be suggested for the synthesis of scaffolds for hard tissue regeneration, as they present a high residual glassy phase, high hardness values and hydroxyapatite-forming ability. The use of trace elements in the human body, such as Cu, could improve the biological performance of such glasses, as Cu is known to play a significant role in angiogenesis. Nano-bioceramics are preferable compared to their micro-scale counterparts, because of their increased surface area, which improves both mechanical properties and apatite-forming ability due to the increased nucleation sites provided, their high diffusion rates, reduced sintering time or temperature, and high mechanical properties. The aim of the present work was the evaluation of the effect of different ratios of Ethanol/TEOS and total amount of the inserted ammonia to the particle size, morphology and bioactive, hemolytic and antibacterial behavior of nanoparticles in the quaternary system SiO2-CaO-MgO-CuO. Different ratios of Ethanol/TEOS and ammonia amount affected the size and morphology of bioactive nanopowders. The optimum materials were synthesized with the highest ethanol/TEOS ratio and ammonia amount as verified by the enhanced apatite-forming ability and antibacterial and non-hemolytic properties.

In vitro evaluation of the shear bond strength and bioactivity of a bioceramic cement for bonding monolithic zirconia.

STATEMENT OF PROBLEM: Adhesive cementation is the most common bonding strategy for zirconia restorations. Although cementation with a bioactive luting agent has been proposed as an alternative, how the bond strength compares is unclear. PURPOSE: The purpose of this in vitro study was to evaluate shear bond strength after cementing a monolithic zirconia ceramic to human dentin with a bioceramic cement, compare it with a traditional cement, and evaluate its bioactive properties. MATERIAL AND METHODS: A total of 120 dentin specimens and 120 yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) (BruxZir) cylindrical specimens were used. Zirconia and dentin specimens were randomly divided into 8 study groups (n=15) based on 2 luting cement types (a bioceramic cement or glass ionomer cement as control), 2 airborne-particle abrasion protocols (50 µm or 110 µm), and 2 water storage durations (24 hours or 30 days). After the shear bond strength test using a universal machine at a crosshead speed of 1 mm/min, fracture patterns were evaluated under a stereomicroscope and a scanning electron microscope. Strength values were statistically analyzed with a 3-factor ANOVA model (α=.05). Bioactivity was evaluated in simulated body fluid (SBF). RESULTS: The control glass ionomer cement achieved significantly greater shear bond strength compared with the tested bioceramic cement. Mean bond strength values ranged from 2.52 MPa to 5.23 MPa for the bioceramic cement tested and from 4.20 MPa to 6.61 MPa for the control cement. The duration of water storage played a significant role in the bond strength, with groups stored for 30 days reaching higher bond strength values, whereas the particle size of airborne-particle abrasion did not have a significant effect. Failure types were primarily mixed. No apatite formation was recorded on the surface of the specimens even after 30 days of immersion in SBF. CONCLUSIONS: The evaluated cement did not develop apatite in SBF, and its bond strength values were below the control glass ionomer cement.

Evaluation of the micro-mechanical and bioactive properties of bioactive glass-dental porcelain composite.

The aim of this study was to evaluate microhardness and elastic modulus of a novel sol-gel derived dental ceramic - 58S bioactive glass composite (BP67: Bioactive Glass:33.3%, Dental Ceramic:66.7%) BP671 material by micro-indentation and to investigate its microstructure and bioactivity. The research hypotheses were that the values of microhardness (1) and elastic modulus (2) of the novel bioceramic composite and the commercial dental ceramic will be of the same order. The experimental sol-gel derived ceramics showed similar microstructural characteristics to a commercial feldspathic porcelain, and presence of additional calcium phosphate phases, which contributed its bioactivity. The formation of an apatite-like layer on the materials' surface observed by Fourier Transform Infrared (FTIR)2 spectroscopy, X-ray Diffraction (XRD)3 and Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS)4 techniques after 12 days of maintenance in Conventional Simulated Body Fluid (cSBF)5 solution. The BP67 exhibited values of microhardness and modulus of elasticity which were not statistically significant different compared to dental ceramic, indicating the adequate mechanical integrity of the material. The results of this study suggest that the novel bioactive composite could be potentially applied in prosthetic dentistry, while its thermal and optical properties should be investigated in future studies.

Sol-Gel Derived Mg-Based Ceramic Scaffolds Doped with Zinc or Copper Ions: Preliminary Results on Their Synthesis, Characterization, and Biocompatibility.

Glass-ceramic scaffolds containing Mg have shown recently the potential to enhance the proliferation, differentiation, and biomineralization of stem cells in vitro, property that makes them promising candidates for dental tissue regeneration. An additional property of a scaffold aimed at dental tissue regeneration is to protect the regeneration process against oral bacteria penetration. In this respect, novel bioactive scaffolds containing Mg(2+) and Cu(2+) or Zn(2+), ions known for their antimicrobial properties, were synthesized by the foam replica technique and tested regarding their bioactive response in SBF, mechanical properties, degradation, and porosity. Finally their ability to support the attachment and long-term proliferation of Dental Pulp Stem Cells (DPSCs) was also evaluated. The results showed that conversely to their bioactive response in SBF solution, Zn-doped scaffolds proved to respond adequately regarding their mechanical strength and to be efficient regarding their biological response, in comparison to Cu-doped scaffolds, which makes them promising candidates for targeted dental stem cell odontogenic differentiation and calcified dental tissue engineering.