RESUMO
Syzgium cumini (L.) Skeels powder (S. cumini powder), also known as Jamun, is well-known for its various medical and health benefits. It is especially recognized for its antidiabetic and antioxidant properties. Thus, S. cumini powder is used in various industries, such as the food and cosmetic industries. In this work, the fruit of S. cumini was utilized; its seeds were extracted, dried, and ground into powder. The ground powders were subjected to various techniques such as physicochemical tests, Fourier transform infrared (FTIR) spectroscopy, X-ray diffractometry (XRD), particle size analysis, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and antioxidant analysis. From the physicochemical tests, it was revealed that the jamun seed filler contained cellulose (43.28%), hemicellulose (19.88%), lignin (23.28%), pectin (12.58%), and wax (0.98%). The FTIR analysis supported these results. For instance, a peak at 2889 cm-1 was observed and associated with CH stretching, typically found in methyl and methylene groups, characteristic of cellulose and hemicellulose structures. The XRD results demonstrated that the crystallinity index of the jamun seed filler was 42.63%. The particle analysis indicated that the mean (average) particle size was 25.34 µm. This observation was ensured with SEM results. The EDX spectrum results showed the elemental composition of the fillers. Regarding thermal degradation, the jamun seed filler had the ability to withstand temperatures of up to 316.5 °C. Furthermore, endothermic and exothermic peaks were observed at 305 °C and 400 °C, respectively. Furthermore, the antioxidant property of the powder displayed a peak scavenging activity of 91.4%. This comprehensive study not only underscores the viability of S. cumini powder as a sustainable and effective particulate filler in polymer composites but also demonstrates its potential to enhance the mechanical properties of composites, thereby offering significant implications for the development of eco-friendly materials in various industrial applications.
RESUMO
Coated silver nanoparticles (Ag NPs) are currently receiving interest because of their numerous uses in various fields of electronics, antimicrobials, manufacturing sectors, optical science, and pharmaceuticals. Among others, it gained significant attention in the power electronic system. The goal of the proposed study is to use a cost-effective coating material for solar panels; to accomplish this, silver nanoparticles were synthesized from the leaves of the Rosy Periwinkle plants. Green synthesis and characterization, such as Ultraviolet Visible Spectrometer (UV-Vis) analysis, Scanning Electron Microscopy (SEM), Energy Dispersive X-ray Spectroscopy (EDX), and Fourier Transform Infrared Spectroscopy (FTIR), were carried out after the silver nanoparticles have been collected prior coating. As a consequence, the effectiveness is determined based on the conductivity test, and the resulting Ag NPs are then applied to the c-si layer of the solar panel. Additionally, a modelling and experimental analysis are performed in this study to ascertain the suggested framework's ability to measure energy before and after coating panels with Ag NPs. Specifically, the Voltage Current (VI) and Power Voltage (PV) characteristics were validated in this study for analyzing the effectiveness and the obtained results revealed that the coating of green synthesized Ag NPs generated 2 % more power than the reference solar panel under the same conditions. Further, hardware testing and simulation were both used to confirm the outcomes and effectiveness of the suggested method. The open circuit voltage (Voc), short circuit current (Isc), maximum peak voltage (Vmp), maximum peak current (Imp), and efficiency are taken into account when assessing how well the suggested system performs at tracking. Moreover, the current density characteristics were evaluated with respect to various irradiation conditions for both the typical solar as well as Ag NPs coated panels. From the observation, it is noted that the efficiency level of coated panel was improved up to 19.20 %, 18 %, and 17.20 % for the irradiations of 200 W/m2, 500 W/m2, and 1000 W/m2 respectively.
RESUMO
Fillers or particulate fillers find a growing utilization as reinforcement material in polymer composites due to their ability to enhance the properties of the ensuing composites. The discarded seed in sapodilla fruit is available in abundant and the shell of the seed can be used as a reinforcing filler. The primary goal of this study is to extract and characterize the sapodilla seed shell powder (SSS) physically and chemically in order to assess its potential for reinforcement as a particulate filler in polymer composites. The sapodilla seed shell filler was characterized experimentally by Physio-chemical analysis, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Energy dispersive X-ray analysis (EDAX). The morphology and the filler size were determined by Scanning electron microscopy (SEM) and Particle size analysis. The thermal degradation behaviour was evaluated by Thermogravimetric analysis (TGA).
RESUMO
Bio-composites are easy to manufacture and environmentally friendly, could reduce the overall cost and provide lightweight due to the low density of the natural fibers. In a bid to compete with the synthetic fiber reinforced composites, a single natural fiber composite may not be a good choice to obtain optimal properties. Hence, hybrid composites are produced by adding two or more natural fibers together to obtain improved properties, such as mechanical, physical, thermal, water absorption, acoustic and dynamic, among others. Regarding thermal stability, the composites showed a significant change by varying the individual fiber compositions, fiber surface treatments, addition of fillers and coupling agents. The glass transition temperature and melting point obtained from the thermomechanical analysis and differential scanning calorimetry are not the same values for several hybrid composites, since the volume variation was not always parallel with the enthalpy change. However, the difference between the temperature calculated from the thermomechanical analysis and differential scanning calorimetry was lower. Significantly, this critical reviewed study has a potential of guiding all composite designers, manufacturers and users on right selection of composite materials for thermal applications, such as engine components (covers), heat shields and brake ducts, among others.
Assuntos
Celulose/química , Vidro/química , Teste de Materiais , Estresse Mecânico , Resistência à TraçãoRESUMO
This work focuses on the fabrication of hybrid bio-composites using green epoxy as the matrix material, hemp (H) and sisal (S) fibre mats as the reinforcements. The hybrid composite with sisal/hemp fibres were fabricated by cost effective hand lay-up technique, followed by hot press with different stacking sequences. Static properties of the composites such as tensile, compressive, inter-laminar shear strengths (ILSS) and hardness were examined. The physical properties such as density, void content, water absorption and thickness swelling were also analyzed. The experimental results indicate that hybrid composites exhibited minor variation in tensile strength when the stacking sequence was altered. The hybrid composite with the intercalated arrangement (HSHS) exhibited the highest tensile modulus when compared with the other hybrid counterparts. Hybrid composites (SHHS and HSSH) offered 40% higher values of compressive strength than the other layering arrangements. HHHH sample exhibited the highest ILSS value of 4.08â¯MPa. Typical failure characteristics of the short beam test such as inter-laminar shear cracks in the transverse direction, micro-buckling and fibre rupture were also observed.
Assuntos
Cannabis/química , Resinas Epóxi/química , Força Compressiva , Dureza , Teste de Materiais/métodos , Pressão , Resistência ao Cisalhamento , Resistência à Tração , Água/químicaRESUMO
As the annual production of the solid waste generable in the form of spent coffee bean powder (SCBP) is over 6 million tons, its utilization in the generation of green energy, waste water treatment and as a filler in biocomposites is desirable. The objective of this article is to analyze the possibilities to valorize coffee bean powder as a filler in cellulose matrix. Cellulose matrix was dissolved in the relatively safer aqueous solution mixture (8% LiOH and 15% Urea) precooled to -12.5°C. To the cellulose solution (SCBP) was added in 5-25wt% and the composite films were prepared by regeneration method using ethyl alcohol as a coagulant. Some SCBP was treated with aq. 5% NaOH and the composite films were also prepared using alkali treated SCBP as a filler. The films of composites were uniform with brown in color. The cellulose/SCBP films without and with alkali treated SCBP were characterized by FTIR, XRD, optical and polarized optical microscopy, thermogravimetric analysis (TGA) and tensile tests. The maximum tensile strength of the composite films with alkali treated SCBP varied between (106-149MPa) and increased with SCBP content when compared to the composites with untreated SCBP. The thermal stability of the composite was higher at elevated temperatures when alkali treated SCBP was used. Based on the improved tensile properties and photo resistivity, the cellulose/SCBP composite films with alkali treated SCBP may be considered for packaging and wrapping of flowers and vegetables.