On the structural evolution of nanoporous optically transparent CuO photocathodes upon calcination for photoelectrochemical applications.

Copper oxides are promising photocathode materials for solar hydrogen production due to their narrow optical band gap energy allowing broad visible light absorption. However, they suffer from severe photocorrosion upon illumination, mainly due to copper reduction. Nanostructuring has been proven to enhance the photoresponse of CuO photocathodes; however, there is a lack of precise structural control on the nanoscale upon sol-gel synthesis and calcination for achieving optically transparent CuO thin film photoabsorbers. In this study, nanoporous and nanocrystalline CuO networks were prepared by a soft-templating and dip-coating method utilizing poly(ethylene oxide)-block-poly(propylene oxide)-block-poly(ethylene oxide) (Pluronic® F-127) as a structure-directing agent, resulting for the first-time in uniformly structured, crack-free, and optically transparent CuO thin films. The photoelectrochemical properties of the nanoporous CuO frameworks were investigated as a function of the calcination temperature and film thickness, revealing important information about the photocurrent, photostability, and photovoltage. Based on surface photovoltage spectroscopy (SPV), the films are p-type and generate up to 60 mV photovoltage at 2.0 eV (0.050 mW cm-2) irradiation for the film annealed at 750 °C. For these high annealing temperatures, the nanocrystalline domains in the thin film structure are more developed, resulting in improved electronic quality. In aqueous electrolytes with or without methyl viologen (as a fast electron acceptor), CuO films show cathodic photocurrents of up to -2.4 mA cm-2 at 0.32 V vs. RHE (air mass (AM) 1.5). However, the photocurrents were found to be entirely due to photocorrosion of the films and decay to near zero over the course of 20 min under AM 1.5 illumination. These fundamental results on the structural and morphological development upon calcination provide a direction and show the necessity for further (surface) treatment of sol-gel derived CuO photocathodes for photoelectrochemical applications. The study demonstrates how to control the size of nanopores starting from mesopore formation at 400 °C to the evolution of macroporous frameworks at 750 °C.

Molybdenum Phosphide Quantum Dots Encapsulated by P/N-Doped Carbon for Hydrogen Evolution Reaction in Acid and Alkaline Electrolytes.

A facile and eco-friendly strategy is presented for synthesizing novel nanocomposites, with MoP quantum dots (QDs) as cores and graphitic carbon as shells, these nanoparticles are dispersed in a nitrogen and phosphorus-doped porous carbon and carbon nanotubes (CNTs) substrates (MoP@NPC/CNT). The synthesis involves self-assembling reactions to form single-source precursors (SSPs), followed by pyrolysis at 900 °C in an inert atmosphere to obtain MoP@NPC/CNT-900. The presence of carbon layers on the MoP QDs effectively prevents particle aggregation, enhancing the utilization of active MoP species. The optimized sample, MoP@NPC/CNT-900, exhibits remarkable electrocatalytic activity and durability for the hydrogen evolution reaction (HER). It demonstrates a low overpotential of 155 mV at 10 mA cm-2 , a small Tafel slope of 76 mV dec-1 , and sustained performance over 20 hours in 0.5 M H2 SO4 . Furthermore, the catalyst shows excellent activity in 1 M KOH, with a relatively low overpotential of 131 mV and long-term durability under constant current input. The exceptional HER activity can be attributed to several factors: the superior performance of MoP QDs, the large surface area and good conductivity of the carbon substrates, and the synergistic effect between MoP and carbon species.

A facile strategy for reclaiming discarded graphite and harnessing the rate capabilities of graphite anodes.

Graphite negative electrodes are unbeaten hitherto in lithium-ion batteries (LiBs) due to their unique chemical and physical properties. Thus, the increasing scarcity of graphite resources makes smart recycling or repurposing of discarded graphite particularly imperative. However, the current recycling techniques still need to be improved upon with urgency. Herein a facile and efficient hydrometallurgical process is reported to effectively regenerate aged (39.5 %, 75 % state-of-health, SOH) scrapped graphite (SG) from end-of-life lithium-ion batteries. Ultimately, the first cycle reversible capacity of SG1 (SOH = 39.5 %) improved from 266 mAh/g to 337 mAh/g while 330 mAh/g (98 %) remain after 100 cycles at 0.5 C. The reversible capacity for the first cycle of SG2 (SOH = 75 %) boosted from 335 mAh/g to 366 mAh/g with the capacity retention of 99.3 % after 100 cycles at 0.5 C, which is comparable with the benchmark commercial graphite. The regenerated graphites RG1 and RG2 exhibit excellent output characteristics even increasing the rate up to 4 C. This is the best rate level reported in the literature to date. Finally, the diffusion coefficient of Li ions during deintercalation and intercalation in the regenerated graphites have been measured by galvanostatic intermittent titration technique (GITT), determining values 2 orders-of-magnitude higher than that of the spent counterparts. Taking advantage of the synergistic effect of acid leaching and heat treatment, this strategy provides a simple and up-scalable method to recycle graphitic anodes.

Sol-Gel-Derived Ordered Mesoporous High Entropy Spinel Ferrites and Assessment of Their Photoelectrochemical and Electrocatalytic Water Splitting Performance.

The novel material class of high entropy oxides with their unique and unexpected physicochemical properties is a candidate for energy applications. Herein, it is reported for the first time about the physico- and (photo-) electrochemical properties of ordered mesoporous (CoNiCuZnMg)Fe2 O4 thin films synthesized by a soft-templating and dip-coating approach. The A-site high entropy ferrites (HEF) are composed of periodically ordered mesopores building a highly accessible inorganic nanoarchitecture with large specific surface areas. The mesoporous spinel HEF thin films are found to be phase-pure and crack-free on the meso- and macroscale. The formation of the spinel structure hosting six distinct cations is verified by X-ray-based characterization techniques. Photoelectron spectroscopy gives insight into the chemical state of the implemented transition metals supporting the structural characterization data. Applied as photoanode for photoelectrochemical water splitting, the HEFs are photostable over several hours but show only low photoconductivity owing to fast surface recombination, as evidenced by intensity-modulated photocurrent spectroscopy. When applied as oxygen evolution reaction electrocatalyst, the HEF thin films possess overpotentials of 420 mV at 10 mA cm-2 in 1 m KOH. The results imply that the increase of the compositional disorder enhances the electronic transport properties, which are beneficial for both energy applications.

Single-Source-Precursor Derived Transition Metal Alloys Embedded in Nitrogen-Doped Porous Carbons as Efficient Oxygen Evolution Electrocatalysts.

Carbon supported metallic nanomaterials are of great interest due to their low-cost, high durability and promising functional performance. Herein, a highly active oxygen evolution reaction (OER) electrocatalyst comprised of defective carbon shell encapsulated metal (Fe, Co, Ni) nanoparticles and their alloys supported on in-situ formed N-doped graphene/carbon nanotube hybrid is synthesized from novel single-source-precursors (SSP). The precursors are synthesized by a facile one-pot reaction of tannic acid with polyethylenimine and different metal ions and subsequent pyrolysis of the SSP. Benefiting from the heteroatom doping of carbon and formation of well-encapsulated metal/alloy nanoparticles, the obtained FeNi@NC-900 catalyst possesses lowest overpotentials of 310 mV to achieve a current density of 10 mA cm-2 for OER with a small Tafel slope value of 45 mV dec-1 , indicating excellent catalytic performance due to the following features: (1) A synergistic electronic effect among metal alloy nanoparticles, nitrogen-doped carbon, and entangled carbon nanotubes; (2) penetration of electrolyte is promoted towards the active sites through the porous structure of the formed mesoporous carbon clusters; (3) the unique core-shell nanostructure of the hybrid material effectively curbs the degradation of electrocatalyst by protecting the alloy nanoparticles from harsh electrolyte. This work advances an inexpensive and facile method towards the development of transition metal-based hybrid material for potential energy storage and conversion.