Synthesis of Diblock and Triblock Polymers from Cyclooctadiene and Norbornene Via ROMP in Miniemulsion.

The synthesis of diblock and triblock linear polyolefins via ring opening metathesis polymerization (ROMP) in an aqueous nanoparticle dispersion is presented. The different block polyolefins are synthesized from the cyclic olefins 1,5-cyclooctadiene and norbornene (NB), using a water-soluble TEGylated ruthenium alkylidene catalyst, yielding the structures PCOD-b-PNB, PNB-b-PCOD, and PCOD-b-PNB-b-PCOD. High monomer conversion (>90%), monitored by NMR, is achieved in relatively short times (≈1 h) for the polymerization of each block. The livingness of the system, essential to obtain block copolymers, is confirmed by gel permeation chromatography. Latex particles' size during the multiple steps range between 90 and 150 nm. The results demonstrate that it is possible to obtain nanoparticle latexes from ROMP-based monomers with block copolymer architectures, creating the opportunity to copolymerize olefins bearing different functional groups for the synthesis of new materials.

Polymerization-Induced Self-Assembly (PISA) of 1,5-Cyclooctadiene Using Ring Opening Metathesis Polymerization.

Ring opening metathesis polymerization (ROMP) is a technique that allows the synthesis of well-defined linear polyolefins. Polymerization-induced self-assembly (PISA) involves the synthesis of amphiphilic block copolymers: a hydrophilic block is first polymerized homogeneously in solution (usually water) followed by polymerization of a second hydrophobic block, resulting in a diblock copolymer that self-assembles. In this communication, preliminary results of the development of PISA for the synthesis of amphiphilic block linear polyolefins via ROMP using a water-soluble PEGylated ruthenium alkylidene catalyst are presented. In the first step, a water-soluble modified-norbornene monomer was polymerized in water, then 1,5-cyclooctadiene was added to the system to produce amphiphilic block polyolefins. By varying the concentrations of hydrophilic versus hydrophobic monomer, stable latexes with final particles of ≈200 nm diameter were prepared.