RESUMO
p-type Ag-N dual acceptor doped ZnO thin films with long electrical stability were deposited by DC magnetron reactive co-sputtering technique. After deposition, the films were annealed at 400 °C for one hour in a nitrogen-controlled atmosphere. The deposited films were amorphous. However, after annealing, they crystallize in the typical hexagonal wurtzite structure of ZnO. The Ag-N dual acceptors were incorporated substitutionally in the structure of zinc oxide, and achieving that; the three samples presented the p-type conductivity in the ZnO. Initial electrical properties showed a low resistivity of from 1 to 10-3 Ω·cm, Hall mobility of tens cm2/V·s, and a hole concentration from 1017 to 1019 cm-3. The electrical stability analysis reveals that the p-type conductivity of the ZnO:Ag,N films is very stable and does not revert to n-type, even after 36 months of aging. These results reveal the feasibility of using these films for applications in short-wavelength or transparent optoelectronic devices.
RESUMO
The electron transport layer (ETL) plays a crucial role in solar cell technology, particularly in perovskite solar cells (PSCs), where nanostructured TiO2 films have been investigated as superior ETLs compared to compact TiO2. In this study, we explored the nanocolumnar growth of TiO2 in the anatase phase for bilayer thin films by DC reactive magnetron sputtering (MS) technique and glancing-angle deposition (GLAD). For the growth of the compact TiO2 layer, it was found that the crystalline quality of the films is strongly dependent on the sputtering power, and the samples deposited at 120 and 140 W are those with the best crystalline quality. However, for the nanocolumnar layer, the reactive atmosphere composition determined the best crystalline properties. By optimizing the growth parameters, the formation of TiO2 nanocolumns with a cross-sectional diameter ranging from 50 to 75 nm was achieved. The average thickness of the films exceeded 12.71 ± 0.5 µm. All nanostructured films were grown at a constant GLAD angle of 70°, and after deposition, the measured inclination angle of the nanocolumns is very close to this, having values between 68 and 80°. Furthermore, a correlation was observed between the quality of the initial layer and the enhanced growth of the TiO2 nanocolumns. All bilayer films are highly transparent, allowing light to pass through up to 90%, and present a band gap with values between 3.7 and 3.8 eV. This article offers the experimental parameters for the fabrication of a nanocolumnar TiO2 using the magnetron sputtering technique and the glancing-angle deposition configuration.
RESUMO
Interleukin-6 (IL-6) is a cytokine with wide-ranging biological effects, playing an important role on the immune system and inflammatory responses. Therefore, it is important to develop alternative, highly sensitive and reliable analytical methodologies for the accurate detection of this biomarker in biological fluids. Graphene substrates (GS), such as pristine graphene (G), graphene oxide (GO), and reduced graphene oxide (rGO), have shown great benefits for biosensing and in the development of novel biosensor devices. In this work, we present a proof of concept for the development of a new analytical platform for the specific recognition of human interleukin-6, that is based on the coffee-ring formation of monoclonal antibodies of interleukin-6 (mabIL-6) onto amine functionalized GS. The prepared GS/mabIL-6/IL-6 systems were successfully used to show that IL-6 was specifically and selectively adsorbed onto the area of the mabIL-6 coffee-ring. Raman imaging was confirmed as a versatile tool to investigate different antigen-antibody interactions and their surface distribution. This experimental approach can be used to develop a wide variety of substrates for antigen-antibody interaction allowing the specific detection of an analyte in a complex matrix.