RESUMO
Degradable phosphate glasses have shown favorable properties for tissue engineering. By changing the composition of the glasses, the degradation rate, and ion release are controllable. Zinc oxide can function as a glass network modifier and has been shown to play a positive role in bone formation. Also, phosphate glasses can easily be processed into microspheres, which can be used as microcarriers. This study aims to develop zinc phosphate glasses microspheres and explore the optimized size and composition for applications in bone tissue engineering. Zinc-titanium-calcium-sodium phosphate glasses with 0, 1, 3, 5, or 10 mol % zinc oxide were prepared and processed into microspheres. The smaller microspheres ranged in size from 50 to 106 µm, while the larger ones ranged from 106 to 150 µm. The characteristics of glasses were examined. The osteoblastic cell line MC3T3-E1 was cultured on the surface of microspheres and the cell viability was examined. To evaluate osteogenic differentiation, Alizarin Red S staining, quantitative reverse transcription polymerase chain reaction, and western blot analysis were performed after 14 days. Different sizes of zinc phosphate glass microspheres were successfully made. The glass microspheres with <10 mol % zinc oxide were able to support the adhesion and proliferation of MC3T3-E1 cell lines. The relative gene expression of BMP2 was significantly upregulated in the smaller glass microspheres containing 3 mol % zinc oxide (26-fold, p < .001) and both sizes of microspheres containing 5 mol % zinc oxide (smaller: 27-fold, p < .001; larger: 35-fold, p < .001). Additionally, cluster formation was observed in glass microspheres after 14 days, and the mineralization of MC3T3-E1 cell lines was promoted. Based on these findings, the glass microspheres containing 3-5 mol % of zinc oxide can promote osteogenic differentiation for MC3T3-E1 cells.
RESUMO
INTRODUCTION: Osteogenic and angiogenic properties of synthetic bone grafts play a crucial role in the restoration of bone defects. Angiogenesis is recognised for its support in bone regeneration, particularly in larger defects. The objective of this study is to evaluate the new bone formation and neovascularisation of a 3D-printed isosorbide-based novel CSMA-2 polymer in biomimetic gyroid structures. METHODS: The gyroid scaffolds were fabricated by 3D printing CSMA-2 polymers with different hydroxyapatite (HA) filler concentrations using the digital light processing (DLP) method. A small animal subcutaneous model and a rat calvaria critical-size defect model were performed to analyse tissue compatibility, angiogenesis, and new bone formation. RESULTS: The in vivo results showed good biocompatibility of the 3D-printed gyroid scaffolds with no visible prolonged inflammatory reaction. Blood vessels were found to infiltrate the pores from day 7 of the implantation. New bone formation was confirmed with positive MT staining and BMP-2 expression, particularly on scaffolds with 10% HA. Bone volume was significantly higher in the CSMA-2 10HA group compared to the sham control group. DISCUSSION AND CONCLUSIONS: The results of the subcutaneous model demonstrated a favourable tissue response, including angiogenesis and fibrous tissue, indicative of the early wound healing process. The results from the critical-size defect model showcased new bone formation, as confirmed by micro-CT imaging and immunohistochemistry. The combination of CSMA-2 as the 3D printing material and the gyroid as the 3D structure was found to support essential events in bone healing, specifically angiogenesis and osteogenesis.