RESUMO
W-Bi2O3 composites were fabricated using the hot isostatic pressing technique for the first time. The duration of the samples sintering was 3 minutes under conditions of high pressure and temperature. The study of microstructural features and chemical composition of sintered samples was carried out using scanning electron microscopy and energy-dispersive X-ray spectroscopy, respectively. The effect of temperature on the quality of the obtained W-Bi2O3 composites is determined. The densest samples were obtained at a pressure of 5 GPa and temperatures of 25 °C and 500 °C, the densities of which were 18.10 and 17.85 g cm-3, respectively. It is presented that high temperature exposure during sintering adversely affects both the composite density and microstructure due to the redox reaction accompanied by the reduction of Bi and the oxidation of W. The results of the W-Bi2O3 structure study using X-ray diffraction analysis showed that all samples included the main bulk-centered cubic W phase. The presence of the WO2 phase is noted only when the sintering temperature is increased up to 850 °C, which is confirmed by the appearance of diffraction peaks that correspond to 111 and 22-2 crystallographic planes. The shielding efficiency of the W-Bi2O3 composite against gamma radiation using the Phy-X/PSD software was evaluated. A Co60 isotope with an energy of 0.826-2.506 MeV was used as a source of gamma radiation. The calculation results were compared with those for Pb and Bi. Key shielding parameters such as the linear attenuation coefficient, half-value layer, tenth-value layer, mean free path, and effective atomic number are determined. The calculation results revealed that the W-Bi2O3 composite surpasses Pb and Bi in its shielding properties, which makes it promising for use as a prospective material for radiation shielding applications.
RESUMO
This study announces the anomalous phase separation in CoNiP alloy electroplating. The observed phenomenon of the formation of magnetic bubbles was described for the first time for this triple CoNiP system. This study briefly covers all stages of magnetic bubble formation, starting from the formation of an amorphous phosphor-rich sublayer, followed by nucleation centers, and finally cobalt-rich bubbles. An explanation for the anomalous mechanism of bubble formation was found in the effects of additives and the phenomena of depolarization and superpolarization.
RESUMO
The W-Cu composites with nanosized grain boundaries and high effective density were fabricated using a new fast isostatic hot pressing method. A significantly faster method was proposed for the formation of W-Cu composites in comparison to the traditional ones. The influence of both the high temperature and pressure conditions on the microstructure, structure, chemical composition, and density values were observed. It has been shown that W-Cu samples have a polycrystalline well-packed microstructure. The copper performs the function of a matrix that surrounds the tungsten grains. The W-Cu composites have mixed bcc-W (sp. gr. Im 3¯ m) and fcc-Cu (sp. gr. Fm 3¯ m) phases. The W crystallite sizes vary from 107 to 175 nm depending on the sintering conditions. The optimal sintering regimes of the W-Cu composites with the highest density value of 16.37 g/cm3 were determined. Tungsten-copper composites with thicknesses of 0.06-0.27 cm have been fabricated for the radiation protection efficiency investigation against gamma rays. It has been shown that W-Cu samples have a high shielding efficiency from gamma radiation in the 0.276-1.25 MeV range of energies, which makes them excellent candidates as materials for radiation protection.