Effects of Different Tooth Conditioners on the Bonding of Universal Self-etching Adhesive to Enamel.

PURPOSE: To investigate the effects of several etching products prior to the application of a one-step self-etch adhesive (1-SEA) or two-step self-etch adhesive (2-SEA) on enamel by microshear bond strength (µSBS) testing and observation of the adhesive-enamel interface. MATERIALS AND METHODS: Ground human enamel surfaces were randomly assigned to one of eight groups according to the combination of surface treatments (either no conditioner [NC], ME [Multi Etchant], EC [Enamel Conditioner], or KE [K-etchant Gel]) and adhesive (ADU [Adhese Universal] or SE2 [Clearfil SE Bond 2]). All groups were further divided into two subgroups: 0 or 10,000 thermal cycles (TC). Then, the µSBS test was performed. The adhesive-enamel interface after acid-base challenge and the surface structure after conditioner application were also observed. RESULTS: With 10,000 TCs, there was no statistically significant difference between ME-ADU and NC-ADU. On the other hand, the µSBS of EC-ADU or KE-ADU was significantly higher than that of NC-ADU, while that of ME-SE2 was significantly lower than NC-SE2. There was no significant difference between EC-SE2, NC-SE2, and KE-SE2. Formation of an acid-base resistance zone (ABRZ) was confirmed in all groups. However, funnel-shaped erosion, which indicates interfacial defects, was observed in the NC-ADU, ME-ADU, and ME-SE2 groups. CONCLUSION: For enamel bonding, application of EC or KE prior to ADU increased the bond strength and created a stable adhesive-enamel interface. On the other hand, SE2 also had stable shear bond strength and interface without the use of conditioners. However, ME decreased the bonding performance of SE2.

Influence of primer contamination on the bonding interface of enamel pre-etched with phosphoric acid.

In this study, the influence of primer contamination on enamel bonding was analyzed. Adper Scotchbond Multi-Purpose (SMP), CLEARFIL SE Bond 2 (SE2), Scotchbond Universal (SBU) Adhesive, and Scotchbond Etchant (35% phosphoric acid; PA) were used. Ground bovine enamels were divided into eight groups based on the bonding protocols. The bonding interfaces after an acid-base challenge were observed via scanning electron microscopy to determine the acid-base resistant zone (ABRZ). Moreover, the bonding interfaces after the nanoleakage challenge were analyzed via energy-dispersive X-ray spectroscopy. ABRZ was observed in all the samples except PA_ONLY (applied PA etching, No primer and No adhesive resin). The funnel-shaped erosion was detected only in X_SBU (applied SBU without PA etching). The nanoleakage test revealed silver patterns in some groups. The nanoleakage, i.e., the penetration of the silver ions, was detected in the groups wherein primer was applied on PA-pre-etched enamel.

Effect of repair systems on dentin bonding performance.

The purpose of this study was to investigate the influence of phosphoric acid etching, metal primer or silane coupling agent application on dentin bonding performance of a 2-step self-etch adhesive system. Human dentin surfaces were prepared and divided into four groups depending on the pre-treatment method: no pretreatment (Clearfil SE Bond 2, CONTROL); 40% phosphoric acid (K-Etchant GEL, K); metal primer (Alloy Primer, AP); or silane coupling agent (Porcelain Bond Activator, PB). The specimens were sectioned into beams, separated into 2 subgroups (n=20): no thermocyling or thermocycled (TC), and subjected to a µTBS test and an acid-base challenge for SEM observation. Statistically lower results were observed between K and AP groups, PB and CONTROL, and PB with/without TC (p<0.05). SEM images at the dentin-adhesive interface revealed that all groups produced an acid-base resistant zone (ABRZ), with a funnel-shaped erosion under the ABRZ for the K group.

The effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using the resin-coating technique.

This study evaluated the effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using resin-coating technique. Scotchbond Universal Adhesive and Filtek Supreme Ultra Flowable were applied to bovine dentin. Forty-five specimens were divided into the following three groups according to the temporary sealing materials: Cav-: CAVITON EX, Vas-: COCOA BUTTER and FIT SEAL, and Sep-: Washable SEP and FIT SEAL. Each material was placed on resin-coated dentin. After 1-week water storage, one of the following three cleaning protocols was performed: -WA: washed with water, -BR: brushed with PRESSAGE, and -AF: cleaned with AIR-FLOW. Microtensile bond strength test and EDS analysis were conducted. Irrespective of the cleaning protocol used, Washable SEP demonstrated less residual debris on resin-coated dentin, resulting in high bond strength. Regardless of the temporary sealing material applied, AIR-FLOW demonstrated less residual debris, resulting in high bond strength.

Effects of Different Tooth Conditioners on the Bonding of Universal Self-etching Adhesive to Dentin.

PURPOSE: To investigate the effect of different etching products used prior to the application of universal self-etching adhesive on dentin bonding. MATERIALS AND METHODS: The etching products Multi Etchant (ME), Enamel Conditioner (EC), and K-etchant GEL (KE) were used as pre-treatments prior to the application of the one-bottle self-etching adhesive Adhese Universal (AU). Ground human dentin surfaces were randomly divided into four treatment groups: 1. control (CT; AU without con-ditioner); 2. ME; 3. EC; 4. KE. Microtensile bond strength (µTBS) tests with a thermocycling challenge (0-TC or 10,000-TC) were carried out and the morphological attributes of the adhesive-dentin interface were observed after an acid-base challenge using SEM to observe the acid-base resistant zone (ABRZ). RESULTS: The KE group had a statistically significantly lower µTBS than did the ME and EC groups at 0-TC, and than the CT, ME, and EC groups at 10,000-TC (p < 0.05). An ABRZ was observed in all groups but had partially disappeared in KE. A funnel-shaped area of erosion was also observed at the junction of the dentin and bonding layer in the CT, ME, and EC groups, while the hybrid layer was thicker in the KE group with no evidence of erosion. CONCLUSION: The application of ME or EC did not reduce the microtensile bond strength and resulted in ABRZ formation, while the ABRZ was partially reduced in the KE group.