Surface and bulk viscoelastic stability of solvent-stored bulk-fill resin-based composite.

OBJECTIVE: Investigate the effect of solvent-storage on surface hardness and bulk creep of fast photo-cured bulk-fill resin-based composite (RBC) compared to conventionally irradiated bulk-fill RBCs. METHODS: Three bulk-fill RBCs were studied: Tetric® PowerFill (fast photo-cured bulk-fill RBC) (TPF), Tetric EvoCeram® (EVO), and GrandioSO® x-tra (GSOx) (conventional). Disk-shaped specimens of clinically realistic thickness (4 mm) were prepared from each material for: Group A: surface measurements (18 mm diameter) and Group B: 4 mm diameter for bulk compressive creep measurements. Group A disks were light-cured from the upper 'occlusal' surface for either 3 s or 20 s according to the manufacturer's recommendation. Martens hardness (HM) of both top and bottom surfaces of each specimen were measured. Group B: 4 × 4 mm cylindrical specimens were fully cured to measure bulk creep (CB). A 20 MPa static compressive stress was applied for 2 h, followed by 2 h of unloading. Strain deformation was recorded continuously for 4 h. Both Martens and bulk creep studies were performed under the following storage conditions at 37 °C: (i) dry at 24 h post curing (baseline), and (ii) after 7 and 30 d of storage in two different media: distilled water (DW) and 75 % ethanol/water (75 % E/W). RESULTS: At baseline, HM for all materials ranged from 587 to 439 N/mm2 (top) and 398 to 342 N/mm2 (bottom). After 30 d of solvent-storage, more pronounced HM changes were observed, with the bottom surface being more affected. Normalised HM for TPF decreased by 44 % after 30 d in 75 % E/W. Maximum creep strain ranged from 1.1 % to 2.1 % at baseline, and after 30 d in 75 % E/W this increased from 1.9 % to 2.9 %. Depending on the material and storage condition, the percentage creep strain recovery after 30 d ranged between 65.2 % and 80 %. Increased filler loading in the bulk-fill RBCs decreased the creep strain magnitude and increased the surface hardness. SIGNIFICANCE: Solvent storage decreased the Martens hardness of both upper and lower surfaces and increased the bulk creep characteristics of bulk-fill RBCs. Nevertheless, there was a similar relative stability in surface hardness and viscoelastic stability of fast-cured PowerFill compared to conventionally irradiated RBCs.

Diversity of short-term DC outcomes in bulk-fill RBCs subjected to a 3 s high-irradiance protocol.

OBJECTIVES: To determine the short-term (5 min) initial effects of a high-irradiance light-curing (LC) protocol on light transmission (LT%), radiant exposure (RE) and degree of conversion (DC%) of different bulk-fill resin-based composites (RBCs). MATERIALS AND METHODS: Six bulk-fill composites with different viscosities were investigated: OBF (One Bulk Fill, 3 M), EB (Estelite bulkfill,Tokuyama), PFill, PFlow, ECeram and EFlow (PowerFill, Poweflow, Tetric EvoCeram bulkfill, Tetric Evoflow bulkfill, Ivoclar), subjected to different LC protocols: one ultra-high-intensity (3 W/cm2 -3 s via PowerCure LCU) and two conventional (1.2 W/cm2 -10 s and 20 s via PowerCure and Elipar S10 LCUs). Specimens (n = 5) were polymerized within their molds (ϕ5 mm × 4 mm depth) to determine LT% and RE at 4 mm using a MARC-LC spectrometer. For real-time DC% measurements by FTIR, similar molds were utilized. Data were analyzed by one-way ANOVA and Tukey post-hoc tests at 5 % significance. RESULTS: Regardless of the applied LC protocols, OBF and low-viscosity RBCs (EB, PFlow and EFlow) had the lowest and highest LT%, RE, DC% and RPmax, respectively. RE results of all RBCs were in the same sequence: Elipar-20 s > PCure-10 s > PCure-3 s. DC% of PFill and PFlow displayed no significant difference between the applied LC protocols (p > 0.05). The polymerization kinetic in all materials was well described by an exponential sum function (r2 varied between 0.85 and 0.98), showing a faster polymerization with the PCure-3 s protocol. SIGNIFICANCE: The measurement of LT% and DC% at 5 min gave an insight into the developing polymerization process. The initial response of these bulk-fill composite to a high-irradiation protocol varied depending on their composition and viscosity, being faster for low viscosity materials. Nevertheless, even though multiple resin composites are designed to be efficient during photopolymerization, care should be taken when selecting materials/curing protocol.

Guidance on the assessment of biocompatibility of biomaterials: Fundamentals and testing considerations.

BACKGROUND: Assessing the biocompatibility of materials is crucial for ensuring the safety and well-being of patients by preventing undesirable, toxic, immune, or allergic reactions, and ensuring that materials remain functional over time without triggering adverse reactions. To ensure a comprehensive assessment, planning tests that carefully consider the intended application and potential exposure scenarios for selecting relevant assays, cell types, and testing parameters is essential. Moreover, characterizing the composition and properties of biomaterials allows for a more accurate understanding of test outcomes and the identification of factors contributing to cytotoxicity. Precise reporting of methodology and results facilitates research reproducibility and understanding of the findings by the scientific community, regulatory agencies, healthcare providers, and the general public. AIMS: This article aims to provide an overview of the key concepts associated with evaluating the biocompatibility of biomaterials while also offering practical guidance on cellular principles, testing methodologies, and biological assays that can support in the planning, execution, and reporting of biocompatibility testing.

Effects of two dentifrices on the surface properties and staining susceptibility of polymer-based materials.

PURPOSE: This study examined the effect of whitening and abrasive regular dentifrices on the surface characteristics and stain susceptibility of polymer-based CAD-CAM blocks subjected to artificial toothbrushing abrasion (TB). MATERIALS AND METHODS: Two resin composite blocks [CeraSmart (CS) and Grandio Blocs (GB)], one polymer-infiltrated ceramic [Vita Enamic (VE)], and one direct resin composite [GrandioSO (RC)] were used to produce 60 specimens. The baseline mass, gloss, roughness, Vickers hardness (Hv), and color were measured after 7 days of water storage. The specimens were then separated into three TB treatment groups (n = 5): water control (C), regular daily dentifrice (R), and whitening dentifrice (W). Measurements were repeated post-TB (20,000 cycles). All specimens were immersed in coffee, and the CIE ΔE00 was measured after 1, 7, and 14 days. Two-way, one-way ANOVA, and Tukey's post hoc tests were performed to determine any significant differences between the materials and TB groups. To determine the stain resistance, repeated measures of ANOVA, one-way ANOVA, and Tukey's post hoc tests were used (α = 0.05). RESULTS: The R and W mass changes were minimal (-3.77 to 3.16 g%). W reduced the gloss of all the materials by 12.6%-65%. All materials in W were slightly rougher (Ra, 0.107-0.144 µm) than those in R (Ra, 0.049-0.072 µm). The ΔE00 ranged from 0.6 to 1.6 in W and 0.4 to 1.4 in R. VE was the hardest material at baseline (Hv = 362), whereas brushing and staining lowered Hv in all TB groups (282.8-300.6). After brushing in W, VE, and RC were more susceptible to coffee stains than were CS and GB. CONCLUSIONS: The whitening dentifrice roughened CAD-CAM specimens, reducing gloss, yet lightened some materials. Polymer-infiltrated ceramic and direct resin composite specimens brushed with abrasive regular or whitening dentifrice resulted in more intense staining than the CAD-CAM resin composites.

Characterization of dental light-curing resin composites incorporating multiple modified low-shrink monomers.

OBJECTIVE: Polymerization shrinkage poses a significant challenge in dental resin composites. The objective of this study is to introduce spiroorthocarbonate monomer 3,9-dimethylene-1,3,5,7-tetraoxa-spiro[5,5]undecane (BMSOC) and epoxy resin monomer 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate (ECHM-ECHC) into bisphenol-S-bis(3-methacrylato-2-hydroxy propyl)ether (BisS-GMA) based resin composites to develop composites with reduced shrinkage properties. METHODS: BMSOC and BisS-GMA were synthesized and thoroughly mixed with ECHM-ECHC, followed by inorganic fillers and photoinitiators. Based on the composition of the resin matrix, five groups of experimental composites were prepared, with traditional bisphenol A-dimethacrylate glycidyl ester (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) based composite serving as the control. The polymerization properties, including degree of conversion (DC) and polymerization shrinkage (PS), as well as marginal microleakage, wettability, flexural strength (FS), flexural modulus (FM), and biocompatibility were evaluated. RESULTS: The results demonstrated that compared with the control group, the PS of BisS-GMA based composites containing BMSOC and ECHM-ECHC were significantly reduced (P < 0.05), and the lowest PS (0.96 ± 0.08 %) was observed when the ratio of BisS-GMA: (Epoxy + BMSOC) was 4:6. Additionally, the experimental composites also exhibited improved DC, minimal microleakage, low hydrophilicity, enhanced mechanical properties, qualified in vivo biocompatibility, and slight/moderate in vitro biocompatibility. SIGNIFICANCE: The resin composites incorporating multiple modified low-shrink monomers are promising for dental applications to prevent various clinical problems caused by PS and extend restoration longevity.

Achieving property enhancements in dental resin composites via reduced concentrations of camphorquinone within a ternary initiator system.

OBJECTIVES: The study aimed to assess the impact of diphenyliodonium hexafluorophosphate (DPI) on the physicochemical properties of experimental resin composites (ECRs) featuring reduced concentrations of camphorquinone (CQ)/amine. METHODS: Five concentrations of CQ (0.125, 0.25, 0.5, 0.75, and 1 mol%) with dimethylaminoethyl amine benzoate (EDAB) in a 1:2 mol% ratio (CQ:EDAB) were incorporated into a 50:50 mass% monomer blend of bisphenol glycidyl methacrylate (BisGMA) and triethyleneglycol dimethacrylate (TEGDMA). An additional 5 groups with the same CQ:EDAB concentrations had 0.5 mol% DPI added. Each resin group contained 60 wt% of 0.7 µm barium-alumino-silicate glass. Light transmission (n = 3), real-time degree of polymerization (n = 3), temperature change during polymerization (n = 5), polymerization shrinkage strain (n = 3), flexural strength, and modulus (n = 12), as well as water sorption and solubility (n = 5), were evaluated. Data were analyzed using two-way ANOVA and Tukey's post-hoc test (α = 0.05). RESULTS: Light transmission was reduced in groups containing 0.125 and 0.25 mol% of CQ without DPI. DPI increased temperature, degree and rate of polymerization, despite the reduction in CQ/amine concentration. Additionally, there was an increase in polymerization shrinkage strain, flexural strength and modulus, and a reduction in water sorption and solubility in ECRs with DPI, even with lower concentrations of CQ/EDAB. SIGNIFICANCE: DPI improved the assessed properties of composites across various concentrations of CQ/EDAB, showing the benefit of reducing the quantity of CQ used without compromising the properties and curing of the resin composites.

Do strength of zirconia-abutment-interfaces depend on cement, zirconia type and titanium abutment dimensions?

OBJECTIVES: Part 1 of this study investigates the influence of zirconia types, chimney heights, and gingival heights on the strength of the zirconia-abutment-interface. Part 2 extends the analysis to include adhesive brands and macro-retentions. METHODS: In Part 1, the study utilized three zirconia types (700 MPa, 1000 MPa, 1200 MPa) to fabricate 234 screw-retained zirconia crowns with varying chimney heights (3.5 mm, 4.1 mm, 5 mm) and gingival heights (0.65 mm, 1.2 mm, 3 mm) of the titanium abutments. All adherend surfaces underwent sandblasting with aluminum oxide before cementation with a specific resin cement. In Part 2, the investigation of 240 screw-retained zirconia crowns focused on a single zirconia type (1000 MPa) with chimney heights of 3.5 mm and 5 mm and a gingival height of 0.65 mm of the titanium abutments, cemented with three different resin cements. All adherent surfaces underwent sandblasting with aluminum oxide before cementation, whereas 120 out of 240 abutments received additional macro retentions. Storage in water at 37 °C for 24 h preceded the tensile test. RESULTS: The study revealed a substantial impact of chimney height and zirconia type on the bond strength of the zirconia-abutment-interface. Neither adhesive brands nor macro retentions significantly impacted the bond strength. Fracture incidence was significantly influenced by gingival height and zirconia type in part 1, whereas in part 2 smaller chimney heights correlated with a higher fracture incidence. SIGNIFICANCE: This study contributes insights into the complex interplay of factors influencing the zirconia-abutment-interface. The results provide a foundation for refining clinical approaches, emphasizing the importance of chimney height and zirconia type in achieving successful anterior gap implant restorations.

Effect of polymerisation protocols on water sorption, solubility and hygroscopic expansion of fast-cure bulk-fill composite.

OBJECTIVE: This study examines the effect of two light-curing protocols from a LED polywave light curing unit (LCU) on water sorption, solubility, and hygroscopic expansion of fast and conventional bulk-fill resin-based composites (RBCs) aged in distilled water for 120 d. METHODS: Three bulk-fill RBCs materials were studied: Tetric PowerFill® (fast photo-polymerised composite) (TPF), Tetric EvoCeram bulk-fill (EVO), and GrandioSo x-tra bulk-fill (GSO) (conventional photo-polymerised composites). Specimens were prepared within a 3D-printed resin mold (8-mm diameter x 4-mm height) and light-cured from one side only with 2 modes of polywave LCU (Bluephase® PowerCure): 3 s mode and for 20 s in "Standard" mode. Water sorption and solubility were measured at fixed time intervals for 120 d of distilled water storage, then reconditioned to dry to measure desorption for 75 d, all at 37 ± 1 °C. Hygroscopic (volumetric) expansion was recorded at the same time intervals up to 120 d. Data were analysed through SPSS using Two-way ANOVA, One-way ANOVA, independent t-tests, and Tukey's post-hoc correction tests (p < 0.05). RESULTS: TPF, when irradiated for 3 s demonstrated minimal water sorption (0.83%), solubility (1.01 µg/mm3), and least volumetric expansion (1.64%) compared to EVO and GSO. While EVO showed the highest water sorption (1.03%) and solubility (1.95 µg/mm3) at 3 s. GSO had the lowest sorption (0.67%) and (0.56%) in 3 s and 20 s protocols, respectively. Nevertheless, all the sorption and solubility data were within the ISO 4049 limits. SIGNIFICANCE: For TPF, fast (3 s) polymerisation did not increase either water sorption or solubility, compared with 20 s irradiation. However, with the two comparative bulk-fill composites, fast cure increased water sorption by 15-25% and more than doubled solubility. These findings were consistent with the lesser volumetric expansions observed for Tetric PowerFill at both the fast and standard protocols, indicating its relative stability across polymerisation protocols.

Biomechanical reinforcement by CAD-CAM materials affects stress distributions of posterior composite bridges: 3D finite element analysis.

OBJECTIVES: This 3D finite element analysis study aimed to investigate the effect of reinforcing CAD-CAM bars on stress distribution in various components of a posterior composite bridge. METHODS: A virtual model mimicking the absence of an upper second premolar was created, featuring class II cavity preparations on the proximal surfaces of the adjacent abutment teeth surrounding the edentulous space. Five distinct finite element analysis (FEA) models were generated, each representing a CAD-CAM reinforcing bar material: 3-YTZP (IPS. emax ZirCAD MO; Zr), lithium disilicate (IPS e.max CAD; EX), nano-hybrid resin composite (Grandio Blocs; GB), Fibre-reinforced composite (Trilor; Tri), and polyetheretherketone (PEEK). A veneering resin composite was employed to simulate the replacement of the missing premolar (pontic). In the FEA, an axial force of 600 N and a transverse load of 20 N were applied at the center of the pontic. Subsequently, maximum von Mises (mvM) and maximum principal stresses (σmax) were computed across various components of the generated models. Additionally, shear stresses at the interface between the CAD-CAM bars and the veneering resin composite were determined. RESULTS: CAD-CAM materials with high modulus of elasticity, such as Zr and EX, exhibited the highest mvM stresses and shear stresses while transferring the lowest stress to the veneering resin composite in comparison to other materials. Conversely, PEEK demonstrated the lowest mvM stresses but produced the highest stresses within the veneering resin composite. There was a uniform distribution of mvM stresses in the remaining tooth structure among all groups, except for a noticeable elevation in the molar region of Zr and EX groups. SIGNIFICANCE: Reinforcing CAD-CAM bar materials with a high modulus of elasticity, such as Zr and EX, may result in debonding failures at the connector sites of posterior composite bridges. Conversely, GB, PEEK, and Tri have the potential to cause fracture failures at the connectors rather than debonding.

Evaluating the effect of functionally graded materials on bone remodeling around dental implants.

OBJECTIVES: This study evaluates the potential for osseointegration and remodeling of customized dental implants made from Titanium-Hydroxyapatite Functionally Graded Material (Ti-HAP FGM) with optimized geometry, using the finite element method (FEM). METHODS: The study utilized CT scan images to model and assemble various geometrical designs of dental implants in a mandibular slice. The mechanical properties of Ti-HAP FGMs were computed by varying volume fractions (VF) of hydroxyapatite (0-20%), and a bone remodeling algorithm was used to evaluate the biomechanical characteristics of the ultimate bone configuration in the peri-implant tissue. RESULTS: The findings of the FEA reveal that osseointegration improves with changes in the density and mechanical properties of the bone surrounding Ti-HAP implants, which are influenced by the varying VF of hydroxyapatite in the FGM. SIGNIFICANCE: Increasing the hydroxyapatite fraction improves osseointegration, and appropriate length and diameter selection of Ti-HAP dental implants contribute to their stability and longevity.

Bond Strength, Microleakage, Microgaps, and Marginal Adaptation of Self-adhesive Resin Composites to Tooth Substrates with and without Preconditioning with Universal Adhesives.

PURPOSE: This study investigated and compared the bond strengths, microleakage, microgaps, and marginal adaptation of self-adhesive resin composites (SAC) to dentin with or without universal adhesives. MATERIALS AND METHODS: Dentin surfaces of 75 molars were prepared for shear and microtensile bond strength testing (SBS and µTBS). Silicon molds were used to build up direct restorations using the following materials to form 5 groups: 1. Surefil One; 2. Prime&Bond active Universal Adhesive + Surefil One; 3. Vertise Flow; 4. OptiBond Universal + Vertise Flow; 5. Scotchbond Universal + Filtek Z500 (control group). Bonded specimens were thermocycled 10,000x before being tested either for SBS or µTBS using a universal testing machine at a crosshead speed of 0.5 mm/min. Direct mesial and distal class-II cavities were created on 100 sound premolars, with the gingival margin of distal cavities placed below CEJ and restored according to the five groups. After thermocycling, microleakage scores were assessed following immersion of restored premolars in 2% methylene blue dye for 24 h, while marginal gaps and adaptation percentages were investigated on epoxy resin replicas under SEM at magnifications of 2000X and 200X, respectively. Results were statistically analyzed with parametric and non-parametric tests as applicable, with a level of significance set at α = 0.05. RESULTS: Bond strengths, microleakage scores, microgaps, and percent marginal adaptation of Surefil One and Vertise Flow were significantly (p < 0.001) inferior to the control group. Dentin preconditioning with universal adhesives significantly increased the study parameter outcomes of Surefil One and Vertise Flow, yet they were still significantly below the performance of the control group. CONCLUSION: Conventional resin composite outperformed the SAC whether applied solely or in conjunction with their corresponding universal adhesives.

Synthesis of a novel monomer "DDTU-IDI" for the development of low-shrinkage dental resin composites.

OBJECTIVE: The current dental resin composites often suffer from polymerization shrinkage, which can lead to microleakage and potentially result in recurring tooth decay. This study presents the synthesis of a novel monomer, (3,9-diethyl-1,5,7,11-tetraoxaspiro[5,5]undecane-3,9-diyl)bis(methylene) bis((2-(3-(prop-1-en-2-yl)phenyl)propan-2-yl)carbamate) (DDTU-IDI), and evaluates its effect in the formulation of low-shrinkage dental resin composites. METHODS: DDTU-IDI was synthesized through a two-step reaction route, with the initial synthesis of the required raw material monomer 3,9-diethyl-3,9-dihydroxymethyl-1,5,7,11-tetraoxaspiro-[5,5] undecane (DDTU). The structures were confirmed using Fourier-transform infrared (FT-IR) spectroscopy and hydrogen nuclear magnetic resonance (1HNMR) spectroscopy. Subsequently, DDTU-IDI was incorporated into Bis-GMA-based composites at varying weight percentages (5, 10, 15, and 20 wt%). The polymerization reaction, degree of conversion, polymerization shrinkage, mechanical properties, physicochemical properties and biocompatibility of the low-shrinkage composites were thoroughly evaluated. Furthermore, the mechanical properties were assessed after a thermal cycling test with 10,000 cycles to determine the stability. RESULTS: The addition of DDTU-IDI at 10, 15, and 20 wt% significantly reduced the polymerization volumetric shrinkage of the experimental resin composites, without compromising the degree of conversion, mechanical and physicochemical properties. Remarkably, at a monomer content of 20 wt%, the polymerization shrinkage was reduced to 1.83 ± 0.53%. Composites containing 10, 15, and 20 wt% DDTU-IDI exhibited lower water sorption and higher contact angle. Following thermal cycling, the composites exhibited no significant decrease in mechanical properties, except for the flexural properties. SIGNIFICANCE: DDTU-IDI has favorable potential as a component which could produce volume expansion and increase rigidity in the development of low-shrinkage dental resin composites. The development of low-shrinkage composites containing DDTU-IDI appears to be a promising strategy for reducing polymerization shrinkage, thereby potentially enhancing the longevity of dental restorations.

Recent advances in additive manufacturing of patient-specific devices for dental and maxillofacial rehabilitation.

OBJECTIVES: Customization and the production of patient-specific devices, tailoring the unique anatomy of each patient's jaw and facial structures, are the new frontiers in dentistry and maxillofacial surgery. As a technological advancement, additive manufacturing has been applied to produce customized objects based on 3D computerized models. Therefore, this paper presents advances in additive manufacturing strategies for patient-specific devices in diverse dental specialties. METHODS: This paper overviews current 3D printing techniques to fabricate dental and maxillofacial devices. Then, the most recent literature (2018-2023) available in scientific databases reporting advances in 3D-printed patient-specific devices for dental and maxillofacial applications is critically discussed, focusing on the major outcomes, material-related details, and potential clinical advantages. RESULTS: The recent application of 3D-printed customized devices in oral prosthodontics, implantology and maxillofacial surgery, periodontics, orthodontics, and endodontics are presented. Moreover, the potential application of 4D printing as an advanced manufacturing technology and the challenges and future perspectives for additive manufacturing in the dental and maxillofacial area are reported. SIGNIFICANCE: Additive manufacturing techniques have been designed to benefit several areas of dentistry, and the technologies, materials, and devices continue to be optimized. Image-based and accurately printed patient-specific devices to replace, repair, and regenerate dental and maxillofacial structures hold significant potential to maximize the standard of care in dentistry.

Thermography and conversion of fast-cure composite photocured with quad-wave and laser curing lights compared to a conventional curing light.

OBJECTIVES: This study investigated effects of the different emittance-mode protocols from three light curing units (LCUs): (i) a Laser (Monet); (ii) a quad-wave (PinkWave); (iii) a conventional LED (Elipar S10) on the temperature rise (ΔT) and degree of conversion (DC) when photo-curing fast or conventional bulk-fill resin-based composites (RBC). The aim was to correlate ΔT and DC, and the radiant exposure delivered to RBC specimens. METHODS: A 3D-printed resin mold of 4 mm depth was filled with two bulk-fill RBCs: Tetric PowerFill® (fast photo-polymerised composite) (TPF) or Tetric EvoCeram® Bulk-Fill (EVO). Three LCUs were used: (i) Monet laser for 1 s and 3 s (MONET-1 s, MONET-3 s); (ii) PinkWave quad-wave used for 3 s in Boost mode (PW-3 s) and for 20 s in standard mode (PW-20 s); (iii) Elipar S10 for 5 s (S10-5 s) and for 20 s in standard mode (S10-20 s). 2-dimensional temperature maps were obtained before, during and for 60 s after the LCU had turned off using a thermal imaging camera. Thermal changes were analysed at five depths: (0, 1, 2, 3, and 4 mm from the top surface of the RBC). The maximum temperature rise (Tmax) and the mean temperature rise (ΔT) were determined. Cylindrical-shaped specimens were prepared from each material using a stainless-steel split mold (4 × 4 mm) and light-cured with the same protocols. The DC was measured for 120 s and at 1 h after LCU had turned off using Fourier Transform Infrared Spectroscopy (FTIR). Data were analysed using Three-way ANOVA, One-way ANOVA, independent t-tests, and Tukey post-hoc tests (p < 0.05). RESULTS: Radiant exposures delivered by the various irradiation protocols were between 4.5-30.3 J/cm2. Short exposure times from MONET-1 s and PW-3 s delivered the lowest radiant exposures (4.5 and 5.2 J/cm2, respectively) and produced the lowest ΔT and DC. The longer exposure times in the standard modes of PW-20 s, S10-20 s, and MONET-3 s produced the highest Tmax, ΔT, and DC for both composites. The ΔT range among composites at different depths varied significantly (31.7-49.9 °C). DC of TPF ranged between 30-65% and in EVO between 15.3-56%. TPF had higher Tmax, ΔT for all depths and DC compared to EVO, across the LCU protocols (p < 0.05), except for PW-20 s and MONET-3 s. The coronal part of the restorations (1-2 mm) had the highest ΔT. There was a positive correlation between ΔT and DC at 4-mm depth after 120 s SIGNIFICANCE: Longer, or standard, exposure times of the LCUs delivered greater radiant exposures and had higher DC and ΔT compared to shorter or high-irradiance protocols. The fast photo-polymerised RBC had comparatively superior thermal and conversion outcomes when it received a high irradiance for a short time (1-5 s) compared to the conventional Bulk-Fill RBC.

Biomechanical behavior and Weibull survival of CAD-CAM endocrowns with different marginal designs: A 3D finite element analysis.

OBJECTIVES: To evaluate and compare the effect of tooth preparation designs and different CADCAM. materials on stress distribution and Weibull survival probability of endocrowns. applied to root canal-treated lower first permanent molar using the 3D finite element. analysis method. METHODS: A root canal-treated lower first permanent molar was prepared for endocrowns with a. butt joint or with a ferrule design by placing, circumferentially, a 1-mm wide shoulder. finish line. The prepared molar was scanned for the two designs and modeled on a 3D. Finite element model. Monolithic zirconia (IPS e.max ZirCAD MT, FCZ), lithium. disilicate (IPS e.max CAD, EX), and nano-ceramic resin composite (Lava Ultimate, LU). CAD-CAM materials were used for each preparation to design the virtual endocrown. A. total of six models were built according to the different tooth preparation designs and. endocrown materials. An occlusal load of 600 N and a transverse load of 20 N in. magnitude that simulates the average occlusal load was directed toward the occlusal. surfaces. von Mises and maximum principle values were evaluated Weibull risk-ofrupture. analysis was used to analyze the survival probability of the restorations and. tooth in the different models. RESULTS: The highest von Mises were found in the butt joint design for FCZ, EX, and LU (45.3. MPa, 35.2 MPa, and 24.2 MPa, respectively) compared to the ferrule design for the. same materials (42.6 MPa, 31.2 MPa, and 23.6 MPa, respectively). For von Mises. stress distribution in the remaining part of tooth structure (dentin), the highest stresses. were found in LUFerrule which was closely similar to LUButt joint (135.4 MPa and. 134.7 MPa, respectively), followed by EXFerrule and FCZFerrule (132.2 MPa and. 131.7 MPa, respectively), while the lowest stresses were found in EXButt joint and. FCZButt joint (129.0 MPa and 128.4 MPa, respectively). Shear stresses within the. resin cement were the highest in FCZ and EX compared to LU. EX was found to be the. most reliable material with the highest survival probability, while FCZ showed the. lowest survival probability according to the Weibull risk-of-fracture results. SIGNIFICANCE: Materials with high elastic modulus transfer more stresses to the endocrown and less. to the remaining tooth structure. Endocrown tooth preparation with ferrule design has. better stress distribution and magnitude compared to the butt joint design.

Temperature rise in photopolymerized adhesively-bonded resin composite: A thermography study.

OBJECTIVES: To assess visually and quantitatively the contributions of the adhesive layer photopolymerization and the subsequent resin composite increment to spatio-temporal maps of temperature at five different cavity locations, subjected to two irradiance curing protocols: standard and ultra-high. METHODS: Caries-free molars were used to obtain 40, 2 mm thick dentin slices, randomly assigned to groups (n = 5). These slices were incorporated within 3D-printed model cavites, 4 mm deep, restored with Adhese® Universal bonding agent and 2 mm thick Tetric® Powerfill resin composite, and photocured sequentially, as follows: G1: control-empty cavity; G2: adhesive layer; G3 composite layer with no adhesive; and G4 composite layer with adhesive. The main four groups were subdivided based on two curing protocols, exposed either to standard 10 s (1.2 W/cm2) or Ultra high 3 s (3 W/cm2) irradiance modes using a Bluephase PowerCure LCU. Temperature maps were obtained, via a thermal imaging camera, and numerically analyzed at 5 locations. The data were analyzed using two-way ANOVA followed by multiple one-way ANOVA, independent t-tests and Tukey post-hoc tests (α = 0.05). Tmax, ΔT, Tint (integrated area under the curve) and time-to-reach-maximum-temperature were evaluated. RESULTS: Two-way ANOVA showed that there was no significant interaction between light-curing time and location on the measured parameters (p > 0.05), except for the time-to-reach-maximum-temperature (p < 0.05). Curing the adhesive layer alone with the 10 s protocol resulted in a significantly increased pulpal roof temperature compared to 3 s cure (p < 0.05). Independent T-tests between G3 and G4, between 3 s and 10 s, confirmed that the adhesive agent caused no significant increases (p > 0.05) on the measured parameters. The ultra-high light-curing protocol significantly increased ΔT in composite compared to 10 s curing (p < 0.05). SIGNIFICANCE: When the adhesive layer was photocured alone in a cavity, with a 2 mm thick dentin floor, the exothermal release of energy resulted in higher temperatures with a 10 s curing protocol, compared to a 3 s high irradiance. But when subsequently photocuring a 2 mm layer of composite, the resultant temperatures generated at pulpal roof location from the two curing protocols were similar and therefore there was no increased hazard to the dental pulp from the immediately prior adhesive photopolymerization, cured via the ultra-high irradiation protocol.

Properties of model E-glass fiber composites with varying matrix monomer ratios.

OBJECTIVE: To evaluate properties of fiber-reinforced-composites (FRC) containing Bis-EMA/UDMA monomers but identical dispersed phase (60% wt BaSi glass power +10% wt E-glass fibre). METHODS: A control (Group A), monomer mixture comprising 60% Bis-GMA, 30% TEGDMA, and 10% PMMA (typical FRC monomers) was used. The following monomer mass fractions were mixed: 50% bis-GMA plus 50% of different ratios of Bis-EMA+UDMA to produce consistent formulations (Groups B-E) of workable viscosities was also studied. Flexural strength (FS), fracture toughness (KIC), water sorption (SP), solubility (SL) and hygroscopic expansion (HE) were measured. FS and KIC specimens were stored for 1, 7 d, and 30 d in water at 37 °C. SP/SL specimens were water-immersed for 168d, weighed at intervals, then dried for 84 d at 37 °C. To analyze differences in FS, and KIC, a two-way ANOVA and Tukey post-hoc tests (α = 0.05) were conducted. For SP/SL, and HE, one-way ANOVA with subsequent Tukey post-hoc tests (α = 0.05) were utilized. RESULTS: FS and KIC for groups A, D, E decreased progressively after 1 d. Groups B and C (highest amounts of Bis-EMA) did not decrease significantly. The modified matrix composites performed significantly better than the control group for SP and HE. The control group outperformed the experimental composites only for SL with up to 250% higher SL for group E (6.9 µg/mm) but still below the maximum permissible threshold of 7.5 µg/mm. SIGNIFICANCE: EXPERIMENTAL: composites with highest amounts of Bis-EMA showed improved hydrolytic stability and overall enhancement in several clinically-relevant properties. This makes them potential candidates for alternative matrices to a semi-interpenetrating network in fiber-reinforced composites.

Application and limitations of configuration factor (C-factor) in stress analysis of dental restorations.

OBJECTIVE: The configuration factor (C-factor) is an index used to evaluate the relationship between cavity configuration and the development of polymerization shrinkage stress in dental restorations. Although C-factor has been widely researched, its correlation with stress analysis in dental restorations remains controversial. This review aims to discuss the application and limitations of C-factor and define the restricted conditions under which the C-factor "rule of thumb" is applicable. METHODS: A thorough literature review was conducted on the application and limitations of C-factor in stress analysis of dental restorations. This was principally based on MEDLINE/PubMed and Web of Science databases and a review of the relevant studies and publications in scientific papers in international peer-reviewed journals for the specific topic of C-factor and polymerization shrinkage. RESULTS: The C-factor alone cannot provide an accurate prediction of the shrinkage stress of restorations and the mechanical behavior of material-tooth interfaces. C-factor is only applicable under one condition not typically seen in clinical practice: low, near-rigid compliance. SIGNIFICANCE: Conditions for the application of C-factor have been explicitly defined. A more accurate and precise understanding and utilization of the C-factor is of benefit as it contributes to better understanding of polymerization shrinkage behavior of restorations.

Luting laminate veneers: Do resin-composites produce less polymerization stress than resin cements?

OBJECTIVES: Regular composites could produce less polymerization stress than resin cements when luting laminate veneers but there is no proper evidence to support this theory. The current study aimed to determine the degree of conversion, volumetric shrinkage, polymerization stress and the resultant elastic moduli of materials currently used for adhesive cementation and to determine possible correlations. METHODS: The study considered (i) regular resin composites (Admira Fusion, Gradia, Grandioso, Palfique, Sirius Z, Viscalor and Z100) at room and pre-warmed (PW) at 69ºC, (ii) flowable composites (Sigma Flow and Grandioso Flow); (iii) solely light-activated cements (AllCem Veneer, Variolink Esthetic and RelyX Veneer); and (iv) one dual-activated resin cement (SpeedCEM). Degree of conversion (DC, n = 3) was accessed with FTIR 1 h after irradiation. Bonded-disk and Bioman II instruments were used to access polymerization shrinkage strain and shrinkage stress, respectively, for 60 min at 23 ± 1◦C (n = 3). The elastic modulus was determined by 3-point bending flexural test (n = 6). The results were submitted to analyse s of variance, Tukey's, and correlation tests. RESULTS: For regular composites, the pre-warming did not affect DC, shrinkage and modulus but significantly increased the stress magnitude. Correlation tests indicated a significant relationship only between stress and polymerization shrinkage (r = 0.811343). SIGNIFICANCE: Regular composites can produce less polymerization stress than resin cements when luting laminate veneers. Polymerization stress was dependent on the shrinkage magnitude, but not on the degree of conversion nor the elastic modulus.