RESUMO
The reversible and durable operation of sodium metal batteries at low temperatures (LT) is essential for cold-climate applications but is plagued by dendritic Na plating and unstable solid-electrolyte interphase (SEI). Current Coulombic efficiencies of sodium plating/stripping at LT fall far below 99.9%, representing a significant performance gap yet to be filled. Here, the solvation structure of the conventional 1 m NaPF6 in diglyme electrolyte by facile cyclic ether (1,3-dioxolane, DOL) dilution is efficiently reconfigured. DOL diluents help shield the Na+-PF6 - Coulombic interaction and intermolecular forces of diglyme, leading to anomalously high Na+-ion conductivity. Besides, DOL participates in the solvation sheath and weakens the chelation of Na+ by diglyme for facilitated desolvation. More importantly, it promotes concentrated electron cloud distribution around PF6 - in the solvates and promotes their preferential decomposition. A desired inorganic-rich SEI is generated with compositional uniformity, high ionic conductivity, and high Young's modulus. Consequently, a record-high Coulombic efficiency over 99.9% is achieved at an ultralow temperature of -55 °C, and a 1 Ah capacity pouch cell of initial anode-free sodium metal battery retains 95% of the first discharge capacity over 100 cycles at -25 °C. This study thus provides new insights for formulating electrolytes toward increased Na reversibility at LT.
RESUMO
The rapid development of modern consumer electronics is placing higher demands on the lithium cobalt oxide (LiCoO2 ; LCO) cathode that powers them. Increasing operating voltage is exclusively effective in boosting LCO capacity and energy density but is inhibited by the innate high-voltage instability of the LCO structure that serves as the foundation and determinant of its electrochemical behavior in lithium-ion batteries. This has stimulated extensive research on LCO structural stabilization. Here, it is focused on the fundamental structural understanding of LCO cathode from long-term studies. Multi-scale structures concerning LCO bulk and surface and various structural issues along with their origins and corresponding stabilization strategies with specific mechanisms are uncovered and elucidated at length, which will certainly deepen and advance the knowledge of LCO structure and further its inherent relationship with electrochemical performance. Based on these understandings, remaining questions and opportunities for future stabilization of the LCO structure are also emphasized.
RESUMO
Single-crystal Ni-rich Li[NixMnyCo1-x-y]O2 (SC-NMC) cathodes represent a promising approach to mitigate the cracking issue of conventional polycrystalline cathodes. However, many reported SC-NMC cathodes still suffer from unsatisfactory cycling stability, particularly under high charge cutoff voltage and/or elevated temperature. Herein, we report an ultraconformal and durable poly(3,4-ethylenedioxythiophene) (PEDOT) coating for SC-NMC cathodes using an oxidative chemical vapor deposition (oCVD) technique, which significantly improves their high-voltage (4.6 V) and high-temperature operation resiliency. The PEDOT coated SC LiNi0.83Mn0.1Co0.07O2 (SC-NMC83) delivers an impressive capacity retention rate of 96.7% and 89.5% after 100 and 200 cycles, respectively. Significantly, even after calendar aging at 45 °C and 4.6 V, the coated cathode can still retain 85.3% (in comparison with 59.6% for the bare one) of the initial capacity after 100 cycles at a 0.5 C rate. Synchrotron X-ray experiments and interface characterization collectively reveal that the conformal PEDOT coating not only effectively stabilizes the crystallographic structure and maintains the integrity of the particles but also significantly suppresses the electrolyte's corrosion, resulting in improved electrochemical/thermal stability. Our findings highlight the promise of an oCVD PEDOT coating for single-crystal Ni-rich cathodes to meet the grand challenge of high-energy batteries under extreme conditions.