Electroactive biomimetic collagen-silver nanowire composite scaffolds.

Electroactive biomaterials are widely explored as bioelectrodes and as scaffolds for neural and cardiac regeneration. Most electrodes and conductive scaffolds for tissue regeneration are based on synthetic materials that have limited biocompatibility and often display large discrepancies in mechanical properties with the surrounding tissue causing problems during tissue integration and regeneration. This work shows the development of a biomimetic nanocomposite material prepared from self-assembled collagen fibrils and silver nanowires (AgNW). Despite consisting of mostly type I collagen fibrils, the homogeneously embedded AgNWs provide these materials with a charge storage capacity of about 2.3 mC cm(-2) and a charge injection capacity of 0.3 mC cm(-2), which is on par with bioelectrodes used in the clinic. The mechanical properties of the materials are similar to soft tissues with a dynamic elastic modulus within the lower kPa range. The nanocomposites also support proliferation of embryonic cardiomyocytes while inhibiting the growth of both Gram-negative Escherichia coli and Gram-positive Staphylococcus epidermidis. The developed collagen/AgNW composites thus represent a highly attractive bioelectrode and scaffold material for a wide range of biomedical applications.

Emulsion electrospinning as an approach to fabricate PLGA/chitosan nanofibers for biomedical applications.

Novel nanofibers from blends of polylactic-co-glycolic acid (PLGA) and chitosan have been produced through an emulsion electrospinning process. The spinning solution employed polyvinyl alcohol (PVA) as the emulsifier. PVA was extracted from the electrospun nanofibers, resulting in a final scaffold consisting of a blend of PLGA and chitosan. The fraction of chitosan in the final electrospun mat was adjusted from 0 to 33%. Analyses by scanning and transmission electron microscopy show uniform nanofibers with homogenous distribution of PLGA and chitosan in their cross section. Infrared spectroscopy verifies that electrospun mats contain both PLGA and chitosan. Moreover, contact angle measurements show that the electrospun PLGA/chitosan mats are more hydrophilic than electrospun mats of pure PLGA. Tensile strengths of 4.94 MPa and 4.21 MPa for PLGA/chitosan in dry and wet conditions, respectively, illustrate that the polyblend mats of PLGA/chitosan are strong enough for many biomedical applications. Cell culture studies suggest that PLGA/chitosan nanofibers promote fibroblast attachment and proliferation compared to PLGA membranes. It can be assumed that the nanofibrous composite scaffold of PLGA/chitosan could be potentially used for skin tissue reconstruction.

Polycaprolactone-thiophene-conjugated carbon nanotube meshes as scaffolds for cardiac progenitor cells.

The myocardium is unable to regenerate itself after infarct, resulting in scarring and thinning of the heart wall. Our objective was to develop a patch to buttress and bypass the scarred area, while allowing regeneration by incorporated cardiac stem/progenitor cells (CPCs). Polycaprolactone (PCL) was fabricated as both sheets by solvent casting, and fibrous meshes by electrospinning, as potential patches, to determine the role of topology in proliferation and phenotypic changes to the CPCs. Thiophene-conjugated carbon nanotubes (T-CNTs) were incorporated to enhance the mechanical strength. We showed that freshly isolated CPCs from murine hearts neither attached nor spread on the PCL sheets, both with and without T-CNT. As electrospun meshes, however, both PCL and PCL/T-CNT supported CPC adhesion, proliferation, and differentiation. The incorporation of T-CNT into PCL resulted in a significant increase in mechanical strength but no morphological changes to the meshes. In turn, proliferation, but not differentiation, of CPCs into cardiomyocytes was enhanced in T-CNT containing meshes. We have shown that changing the topology of PCL, a known hydrophobic material, dramatically altered its properties, in this case, allowing CPCs to survive and differentiate. With further development, PCL/T-CNT meshes or similar patches may become a viable strategy to aid restoration of the postmyocardial infarction myocardium.

The biocompatibility and antibacterial properties of collagen-stabilized, photochemically prepared silver nanoparticles.

Spherical 3.5 nm diameter silver nanoparticles (AgNP) stabilized in type I collagen (AgNP@collagen) were prepared in minutes (5-15 min) at room temperature by a photochemical method initiated by UVA irradiation of a water-soluble non-toxic benzoin. This biocomposite was examined to evaluate its biocompatibility and its anti-bacterial properties and showed remarkable properties. Thus, while keratinocytes and fibroblasts were not affected by AgNP@collagen, it was bactericidal against Bacillus megaterium and E. coli but only bacteriostatic against S. epidermidis. In particular, the bactericidal properties displayed by AgNP@collagen were proven to be due to AgNP in AgNP@collagen, rather than to released silver ions, since equimolar concentrations of Ag are about four times less active than AgNP@collagen based on total Ag content. This new biocomposite was stable over a remarkable range of NaCl, phosphate, and 2-(N-morpholino)ethanesulfonic acid concentrations and for over one month at 4 °C. Circular dichroism studies show that the conformation of collagen in AgNP@collagen remains intact. Finally, we have compared the properties of AgNP@collagen with a similar biocomposite prepared using α-poly-L-Lysine and also with citrate stabilized AgNP; neither of these materials showed comparable biocompatibility, stability, or anti-bacterial activity.