It is expected that composites made of carbon nanotubes (CNT) and copper (Cu) display both mechanical and electrical properties, but the low damage dispersion and high-quality composite of high-content CNTs have always been research difficulties. In this paper, high-content CNTs/Cu composites were prepared. The effects of the sintering method, sintering temperature, directional rolling and the CNTs' content on the relative density, hardness and electrical conductivity of the composites were studied. The uniform dispersion of high-content CNTs in Cu matrix was achieved by ball milling, sintering and rolling, and the processes did not cause more damage to the CNTs. The properties of composites prepared by spark plasma sintering (SPS) and vacuum hot pressing sintering (HPS) were compared, and the optimum process parameters of SPS were determined. When the CNTs' content is 2 wt.%, the hardness is 134.9 HBW, which is still 2.3 times that of pure Cu, and the conductivity is the highest, reaching 78.4%IACS. This study provides an important reference for the high-quality preparation and performance evaluation of high-content CNTs/Cu composites.
RESUMO
In this paper, the effects of carbon nanotube defects and a copper surface oxide layer on a carbon nanotube-copper interface were studied via first-principles. A defect-free CNT-Cu interface, Stone-Wales defect CNT-Cu interface, single-hole and double-hole defect CNT-Cu interface, and Cu2O-Cu interface were simulated and calculated. By simulating the differential charge density, atomic population, bond population and density of states of the interface model, the effects of various defects on the interface bonding and electrical conductivity of the composites during the preparation of the CNT-reinforced copper matrix composites were analyzed, which provided theoretical guidance for the preparation of CNT/Cu composites. After that, copper matrix composites with different CNT defect contents were prepared via different rolling deformation processes. Their hardness and electrical conductivity were tested, and the results were consistent with the results obtained via the first-principles calculations.
RESUMO
Composite structure design is an important way to improve reinforcement strengthening efficiency. The dispersion of the external reinforcement is often not uniform enough, however, and it is agglomerated in the matrix, which cannot uniformly and effectively bear the load. The interconnected reinforcement network prepared by the in-situ self-growth method is expected to obtain higher material properties. In this paper, the TiN shell was formed on the surface of Ti powder by the in-situ nitriding method, and then the network TiN/Ti composites were prepared by sintering. In the control group, TiN was dispersed by mechanical ball milling, and it was found that TiN powder was coated on the surface of Ti particles, and the sintered TiN/Ti composites formed a discontinuous structure with a great deal of TiN agglomeration. A uniform TiN nitride layer of 5~7 µm was formed on the surface of Ti powder by the in-situ nitriding method, and a connected TiN network was formed in the sintered Ti-N/Ti composites. The composites prepared by nitriding have higher compressive strength, hardness, and plasticity. The hardness of the Ti-N/Ti composite is 685.7 HV and the compressive strength is 1468.5 MPa. On this basis, the influence of the connected TiN structure on the material properties was analyzed, which provided theoretical guidance for the structural design of the network structure-reinforced titanium matrix composites.
RESUMO
The current cross-sectional study aimed to investigate eHealth literacy among adult workers in China and explore the relationship between eHealth literacy and mental health in this population. Convenience sampling was used to conduct a survey among adult workers aged 18 to 60 years. Potential participants were chosen from those who completed physical examinations at the Health Management Center of one hospital in China. Participants' eHealth literacy and mental health were assessed using the eHealth Literacy Scale, Patient Health Questionnaire, Generalized Anxiety Disorder Scale, and Perceived Stress Scale. Mean scores for eHealth literacy and perceived stress were 28.39 (SD = 5.78) and 5.49 (SD = 2.61), respectively. Depression and anxiety were found in 8.2% and 10.1% of participants, respectively. Multivariate logistic regression analysis showed that a 1-point increase in eHealth literacy score was associated with a 7% decrease in depressive symptoms (odds ratio [OR] = 0.93, 95% confidence interval [CI] [0.88, 0.99]) and a 6% decrease in anxiety symptoms (OR = 0.94, 95% CI [0.89, 0.99]). Furthermore, multiple linear regression analysis showed that perceived stress decreased 0.08 points (B = -0.08, 95% CI [-0.13, -0.04]) with every 1-point increase in eHealth literacy score. Thus, eHealth literacy has the potential to reduce risk of depression, anxiety, and perceived stress, and to promote the mental health of adult workers. [Journal of Psychosocial Nursing and Mental Health Services, 61(9), 40-46.].
Assuntos
Letramento em Saúde , Telemedicina , Humanos , Adulto , Estudos Transversais , Saúde Mental , Inquéritos e QuestionáriosRESUMO
Composite material uses ceramic reinforcement to add to the metal matrix to obtain higher material properties. Structural design is an important direction of composite research. The reinforcement distribution of the core-shell structure has the unique advantages of strong continuity and uniform stress distribution. In this paper, a method of preparing boron carbide (B4C)-coated titanium (Ti) powder particles by ball milling and preparing core-shell B4C-reinforced Ti matrix composites by Spark Plasma Sintering was proposed. It can be seen that B4C coated on the surface of the spherical Ti powder to form a shell structure, and B4C had a certain continuity. Through X-ray diffraction characterization, it was found that B4C reacted with Ti to form layered phases of titanium boride (TiB) and titanium carbide (TiC). The compressive strength of the composite reached 1529.1 MPa, while maintaining a compressive strain rate of 5%. At the same time, conductivity and thermal conductivity were also characterized. The preparation process of the core-shell structure composites proposed in this paper has high feasibility and universality, and it is expected to be applied to other ceramic reinforcements. This result provides a reference for the design, preparation and performance research of core-shell composite materials.
RESUMO
In the present study, the effects of SiC nanowires (SiCnws) with diameters of 100 nm, 250 nm and 450 nm on the microstructure and mechanical behavior of 20 vol.% SiCnws/6061Al composites prepared by pressure infiltration were studied. It was found that the interface between SiCnws and Al matrix was well bonded, and no interface product was found. The thicker SiCnws are beneficial to improve the density. In addition, the bamboo-like and bone-like morphologies of SiCnws produce a strong interlocking effect between SiCnws and Al, which helps to improve the strength and plasticity of the material. The tensile strength of the composite prepared by SiCnws with a diameter of 450 nm reached 544 MPa. With a decrease in the diameter of SiCnws, the strengthening effect of SiCnws increases. The yield strength of SiCnws/6061Al composites prepared by 100 nm is 13.4% and 28.5% higher than that of 250 nm and 450 nm, respectively. This shows that, in nano-reinforced composites, the small-size reinforcement has an excellent improvement effect on the properties of the composites. This result has a guiding effect on the subsequent composite structure design.
RESUMO
Background: The wellbeing of college students is an important concern for public health, and may have associations with insufficient physical activity and psychological distress. This study aimed to identify the latent classes of wellbeing based on the PERMA (i.e., positive emotions, engagement, relationships, meaning, and accomplishments) wellbeing framework, and to explore their associations with levels of physical activity and psychological distress. Methods: A cross-sectional online survey was conducted. A latent profile analysis was performed to characterize the different classes of wellbeing of nursing college students. Results: A group of 1741 nursing college students in China completed the study. Three wellbeing classes were identified in the final model (i.e., low-level wellbeing, moderate-level wellbeing, and high-level wellbeing). Significant differences were found between the three classes in terms of gender (p = 0.002) and year of study (p = 0.038). Low levels of physical activity participation were significantly associated with lower odds of being in the high-level wellbeing class compared with the moderate-level wellbeing class (OR = 1.398, 95%CI [1.023, 1.910], p = 0.035). Lower levels of psychological distress were also associated with greater wellbeing among the three wellbeing classes (p < 0.05). Conclusions: Effective strategies are needed to increase college students' physical activity participation and decrease the severity of psychological distress to improve their health and wellbeing in China.
Assuntos
Angústia Psicológica , Estudantes de Enfermagem , Humanos , Estudos Transversais , População do Leste Asiático , Exercício FísicoRESUMO
The mechanical properties of (Ti, Nb)B/Ti2AlNb composites were expected to improve further by utilizing spark plasma sintering (SPS) and inducing the novel three-dimensional network architecture. In this study, (Ti, Nb)B/Ti2AlNb composites with the novel architecture were successfully fabricated by ball milling the LaB6 and Ti2AlNb mixed powders and subsequent SPS consolidation. The influence of the (Ti, Nb)B content on the microstructure and mechanical properties of the composites was revealed by using the scanning electron microscope (SEM), transmission electron microscopy (TEM) and electronic universal testing machine. The microstructural characterization demonstrated that the boride crystallized into a B27 structure and the α2-precipitated amount increased with the (Ti, Nb)B increasing. When the (Ti, Nb)B content reached 4.9 vol%, both the α2 and reinforcement exhibited a continuous distribution along the prior particle boundaries (PPBs). The tensile test displayed that the tensile strength of the composites presented an increasing trend with the increasing (Ti, Nb)B content followed by a decreasing trend. The composite with a 3.2 vol% reinforcement had the optimal mechanical properties; the yield strengths of the composite at 25 and 650 °C were 998.3 and 774.9 MPa, showing an 11.8% and 9.2% improvement when compared with the Ti2AlNb-based alloy. Overall, (Ti, Nb)B possessed an excellent strengthening effect and inhibited the strength weakening of the PPBs area at high temperatures; the reinforcement content mainly affected the mechanical properties of the (Ti, Nb)B/Ti2AlNb composites by altering the α2-precipitated amount and the morphology of (Ti, Nb)B in the PPBs area. Both the continuous precipitation of the brittle α2 phase and the agglomeration of the (Ti, Nb)B reinforcement dramatically deteriorated the mechanical properties.
RESUMO
Rolling enables the directional alignment of the reinforcements in graphene/Cu composites while achieving uniform graphene dispersion and matrix grain refinement. This is expected to achieve a breakthrough in composite performance. In this paper, the process parameters of rolling are investigated, and the defects, thickness variations of graphene and property changes of the composite under different parameters are analyzed. High-temperature rolling is beneficial to avoid the damage of graphene during rolling, and the prepared composites have higher electrical conductivity. The properties of graphene were investigated. Low-temperature rolling is more favorable to the thinning and dispersion of graphene; meanwhile, the relative density of the composites is higher in the low-temperature rolling process. With the increase of rolling deformation, the graphene defects slightly increased and the number of layers decreased. In this paper, the defect states of graphene and the electrical conductivity with different rolling parameters is comprehensively investigated to provide a reference for the rolling process of graphene/copper composites with different demands.
RESUMO
High-performance extruded aluminum alloys with complex textures suffer significant dimension variation under environmental temperature fluctuations, dramatically decreasing the precision of navigation systems. This research mainly focuses on the effect of the texture of extruded pure aluminum on its dimensional stability after various annealing processes. The result reveals that a significant increment in the area fraction of recrystallized grains with <100> orientation and a decrement in the area fraction of grains with <111> orientation were found with increasing annealing temperature. Moreover, with the annealing temperature increasing from 150 °C to 400 °C, the residual plastic strain after twelve thermal cycles with a temperature range of 120 °C was changed from -1.6 × 10-5 to -4.5 × 10-5. The large amount of equiaxed grains with <100> orientation was formed in the microstructure of the extruded pure aluminum and the average grain size was decreased during thermal cycling. The area fraction of grain with <100> crystallographic orientation of the sample annealed at 400 °C after thermal cycling was 30.9% higher than annealed at 350 °C (23.7%) or at 150 °C (18.7%). It is attributed to the increase in the proportion of recrystallization grains with <100> direction as the annealing temperature increases, provided more nucleation sites for the formation of fine equiaxed grains with <100> orientation. The main orientation of the texture was rotated from parallel to <111> to parallel to <100> after thermal cycling. The change in the orientation of grains contributed to a change in interplanar spacing, which explains the change in the dimension along the extrusion direction during thermal cycling.
RESUMO
In this paper, six-layer AlN/Al gradient composites were prepared by a spark plasma sintering process to study the influences of sintering temperature and holding time on the microstructure and mechanical properties. The well-bonded interface enables the composite to exhibit excellent thermal and mechanical properties. The hardness and thermal expansion properties of the composite exhibit a gradient property. The hardness increased with the volume fraction of AlN while the CTE decreased as the volume fraction of AlN. The thermal expansion reaches the lowest value of 13-14 ppm/K, and the hardness reaches the maximum value of 1.25 GPa, when the target volume fraction of AlN is 45%. The simulation results show that this gradient material can effectively reduce the thermal stress caused by the mismatch of the thermal expansion coefficient as a transmitter and receiver (T/R) module. This paper attempts to provide experimental support for the preparation of gradient Al matrix composites.
RESUMO
Graphene has extremely high theoretical strength and electrothermal properties, and its application to Cu-based composites is expected to achieve a breakthrough in the performance of existing composites. As a nano-reinforced body, graphene often needs a long time of ball milling to make it uniformly dispersed, but the ball milling process inevitably brings damage to the graphene, causing the performance of the composite to deviate from expectations. Therefore, this paper uses CH4 as a carbon source to repair graphene through a CVD process to prepare low-damage graphene/Cu composites. The process of graphene defect generation was studied through the ball milling process. The effects of defect content and temperature on the graphene repair process were studied separately. The study found that the graphene defect repair process, the decomposition process of oxygen-containing functional groups, and the deposition process of active C atoms existed simultaneously in the CVD process. When the repair temperature was low, the C atom deposition process and the oxygen-containing functional group decomposition process dominated. In addition, when the repair temperature is high, the graphene defect repair process dominated. 3 wt% graphene/Cu composites were prepared by pressure infiltration, and it was found that the bending strength was increased by 48%, the plasticity was also slightly increased, and the thermal conductivity was increased by 10-40%. This research will help reduce graphene defects, improve the intrinsic properties of graphene, and provide theoretical guidance for the regulation of C defects in composites.
RESUMO
With the aim of overcoming the limitations of traditional soldering ceramic methods for power device packaging, a simple but ultrafast bonding technology is reported. The effect and mechanism of ultrasonic action on the interfacial bonding and microstructure is investigated and thoroughly discussed. An ultrafast interfacial bond between SiC ceramics and SnAgTi active solder has been successfully achieved through a reaction at the interface at a low temperature of 250 °C in the extremely short time. High-resolution transmission electron microscopy (HRTEM) revealed that a silica layer on the surface of SiC reacted with Ti from the SnAgTi active solder to form a nanometer-thickness amorphous titania layer at the interface under the ultrasonic action, which creates an exceptional interfacial structure and facilitates bonding between the two dissimilar crystals. A discontinuous titania layer at the interface was identified within 0.1 s. With further increasing ultrasonic action time to 1 s, a continuous titania layer with a thickness of 7.6 ± 0.5 nm formed at the interface. A new interfacial reaction mechanism was revealed and it was found that ultrasound accelerated the reaction of liquid active solder/ceramic. Our finding demonstrated that ultrasound could be an effective approach for joining ceramics which is difficult to wet by a liquid metal at low temperature. The combined impact of ultrasonic cavitation and streaming dominated the mechanism and kinetics of the rapid interfacial reaction.
RESUMO
SiC ceramics were successfully soldered with the assistance of ultrasound. Two kinds of filler metals, namely non-eutectic Zn-5Al-3Cu and eutectic Zn-5Al alloys, were used. The effects of ultrasonic action on the microstructure and mechanical properties of the soldered joints were investigated. The results showed that ultrasound could promote the wetting and bonding between the SiC ceramic and filler metals within tens of seconds. For the Zn-5Al-3Cu solder, a fully grain-refined structure in the bond layer was obtained as the ultrasonic action time increased. This may lead to a substantial enhancement in the strength of the soldered joints. For the Zn-5Al solder, the shear strength of the soldered joints was only â¼102â¯MPa when the ultrasonic action time was shorter, and fractures occurred in the brittle lamellar eutectic phases in the center of the bond layer. With increasing ultrasonic action time, the lamellar eutectic phase in the bond layer of SiC joints could be completely transformed to a fine non-lamellar eutectic structure. Meanwhile, the grains in the bond layer were obviously refined. Those results led to the remarkable enhancement of the shear strength of the joints (â¼138â¯MPa) using the Zn-5Al solder, which had approached that enhancement using the Zn-5Al-3Cu solder. The enhanced mechanical properties of the joints were attributed to the significant refinement of the grains and the change in the eutectic structure in the bond layer. Prolonged enhanced heterogeneous nucleation triggered by ultrasonic cavitation is the predominant refinement mechanism of the bond metals of the SiC joints.