Sphere-shaped ZnO photocatalyst synthesis for enhanced degradation of the Quinolone antibiotic, Ofloxacin, under UV irradiation.

The sphere-shaped zinc oxide (ZnO) photocatalyst was synthesized by the homogeneous precipitation method, using Zn(CH3COO)2·2H2O as a zinc precursor and NH4OH as a precipitating agent. The morphology and crystal structure of the prepared ZnO sample were studied by XRD, SEM, FT-IR, XPS, zeta potential measurements, and a low-temperature nitrogen adsorption-desorption technique. The optical characteristics of ZnO were determined by UV - Vis diffuse reflectance spectroscopy. ZnO photocatalyst performance of up to 100% within 210 min was observed in the photodegradation of the ofloxacin antibiotic under ultraviolet (UV) irradiation. The effect of antibiotic concentration, heavy metal ions, and water sources on the photocatalytic activity of ZnO demonstrated both the potential of its application under different conditions, and a good adaptability of this photocatalyst. The photodegradation reaction correlated well with the first-order kinetics model, with a rate constant of 0.0173 min-1. The reusability of the photocatalyst was verified after three cycles of use. Admittedly, photogenerated electrons and holes played a key role in removal of the antibiotic. This work showed the suitability of prepared ZnO for antibiotic removal, and its potential use for environmental protection.

Advanced Removal of Dyes with Tuning Carbon/TiO2 Composite Properties.

This study evaluates the removal of several dyes with different charge properties, i.e., anionic (Acid Red 88), cationic (Basic Red 13), and neutral (Basic Red 5) using transition metal-doped TiO2 supported on a high-surface-area activated carbon. Experimental results confirm the successful deposition of TiO2 and the derivatives (Zr-, Cu-, and Ce-doped samples) on the surface of the activated carbon material and the development of extended heterojunctions with improved electronic properties. Incorporating a small percentage of dopants significantly improves the adsorption properties of the composites towards the three dyes evaluated, preferentially for sample AC/TiO2_Zr. Similarly, the photodegradation efficiency highly depends on the nature of the composite evaluated and the characteristics of the dye. Sample AC/TiO2_Zr demonstrates the best overall removal efficiency for Acid Red 88 and Basic Red 5-83% and 63%, respectively. This promising performance must simultaneously be attributed to a dual mechanism, i.e., adsorption and photodegradation. Notably, the AC/TiO2_Ce outperformed the other catalysts in eliminating Basic Red 13 (74%/6 h). A possible Acid Red 88 degradation mechanism using AC/TiO2_Zr was proposed. This study shows that the removal efficiency of AC/TiO2 composites strongly depends on both the material and pollutant.