The main challenge in treating aged soils highly contaminated with total petroleum hydrocarbons (TPH) is to enhance their bioavailability for microbial degradation. Hydrocarbons in soils undergo chemical changes that make them more resistant to biodegradation. This study investigates toluene's efficacy in enhancing the biodegradation of aged hydrocarbon-contaminated soil containing 292,000 mg TPH kg-1 dry soil. Toluene's effect was compared between solid phase (SOP) and slurry phase (SLP) treatments using a microbial consortium isolated from Cyperus laxus rhizosphere. TPH biodegradation and microbial respiration were measured, the latter to estimate the respiratory quotient (RQ, the ratio between moles of carbon dioxide released and moles of oxygen absorbed during respiration). Toluene significantly accelerated TPH biodegradation in both treatments, achieving ~ 30% higher removal than in a non-solvent control, possibly through improved bioavailability of aromatic compounds and other low molecular weight compounds. According to the RQ analysis, toluene enhanced microbial respiratory processes and hydrocarbon catabolism with higher hydrocarbon mineralization (RQ = ~ 0.5) in both SOP and SLP assays. Our results reveal toluene's potential to increase hydrocarbon availability and microbial degradation efficiency in aged contaminated soils; its use in various bioremediation techniques could be of broad applicability across diverse soil types and pollutants.

Role of dislocation elastic field on impurity segregation in Fe-based alloys.

Dislocation engineering in crystalline materials is essential when designing materials for a large range of applications. Segregation of additional elements at dislocations is frequently used to modify the influence of dislocations on material properties. Thus, the influence of the dislocation elastic field on impurity segregation is of major interest, as its understanding should lead to engineering solutions that improve the material properties. We report the experimental study of the elastic field influence on atomic segregation in the core and in the area surrounding edge dislocations in Fe-based alloys. Each element is found either to segregate in the edge dislocation core or to form atmospheres. The elastic field has a strong effect on the segregation atmosphere, but no effect on the dislocation core segregation. The theory is in good agreement with experiments, and should support dislocation engineering.